Grafen katkılı aramid esaslı kompozit malzemelerin mekanik ve balistik özelliklerinin değerlendirilmesi
Evaluation of the mechanical and ballistic properties of aramid-based composite materials with graphene reinforcement
- Tez No: 742557
- Danışmanlar: PROF. DR. ATİLLA EVCİN
- Tez Türü: Yüksek Lisans
- Konular: Mühendislik Bilimleri, Savunma ve Savunma Teknolojileri, Tekstil ve Tekstil Mühendisliği, Engineering Sciences, Defense and Defense Technologies, Textile and Textile Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Afyon Kocatepe Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Nanobilim ve Nanoteknoloji Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 86
Özet
Bu araştırmada, aramid esaslı kompozit plakalara farklı miktarlarda grafen ve epoksi reçine karışımı takviye ederek nanokompozit yapıda numuneler elde edilmiştir. Deneysel çalışmada kullanılan grafen nano tabakalara; FTIR, Raman analizleri yapılarak karakteristik pikler elde edilmiştir. Balistik kompozitler için referans olabilecek bir balistik plakanın üretim prosesi ayrıntılarıyla açıklanmıştır. Grafen nano tabaka takviyeli ve takviyesiz balistik plakalara, balistik test laboratuvarında NIJ-STD-0101.04 standardında atış testleri uygulanmış ve test sonuçlarının kıyaslaması yapılmıştır. Atış testleri sonucunda bir plaka haricinde grafen ve epoksi reçine takviyeli balistik plakalarda başarılı sonuçlar elde edilememiş ve bunun epoksi reçinenin aramid katmanların esneklik ve enerji sönümleme özelliklerine olumsuz tesir etmesinden kaynaklandığı değerlendirilmiştir. Söz konusu balistik nanokompozit numunelerin dijital fotoğrafları çekilerek balistik etki altında oluşan delinme, fiber kopması, delaminasyon gibi enerji yayılım mekanizmaları incelenmiştir. Çekme testleri sonucunda ağırlıkça % 0,5 ve 1 grafen katkılı numunelerin nihai gerilme kuvvetlerinin artarak mekanik özelliklerinde iyileşme olduğu görülmüştür.
Özet (Çeviri)
In this research, nanocomposite samples were obtained by reinforcing different amounts of graphene and epoxy resin mixture to aramid-based composite plates. Characteristic peaks were obtained by performing FTIR and Raman analyzes on graphene nanoplatelets used in the experimental study. The production process of a ballistic plate, which can be a reference for ballistic composites, is explained in detail. Graphene nanoplatelet reinforced and non-reinforced ballistic plates were exposed shooting test in the ballistic test laboratory in accordance with the NIJ-STD-0101.04 standard and the test results were compared. As a result of the shooting tests, successful results were not obtained in ballistic plates reinforced with graphene and epoxy resin, except for one plate and it was evaluated that this was due to the negative effect of epoxy resin on the flexibility and energy absorption properties of aramid layers. Energy dissipation mechanisms such as perforation, fiber breakage and delamination, which occur under ballistic effect, were investigated in digital photographs of the aforementioned ballistic nanocomposite samples. As a result of the tensile tests, it was observed that the ultimate tensile strength of the 0.5% and 1% by weight graphene added samples increased and their mechanical properties improved.
Benzer Tezler
- Kumaş düzleminde ve düzlem dışında kat arası açılma (ıntra-lamınar) dayanımı
In-plane and out-of-plane interlaminar strength of woven fabric
ELİF ALTUNTAŞ
Yüksek Lisans
Türkçe
2020
Tekstil ve Tekstil MühendisliğiErciyes ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
PROF. DR. ABDULKADİR BİLİŞİK
- Grafen katkılı hibrit kompozit malzemelerden üretilmiş silindirik kutuların ezilme davranışları, hasar analizleri ve yaşlanma etkisinin incelenmesi
Investigation of the crushing behavior, damage analyses and aging effect of cylindrical boxes manufactured from graphene added hybrid composite materials
BARAN ERKEK
Doktora
Türkçe
2024
Makine MühendisliğiBatman ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. HAMİT ADİN
DOÇ. DR. ERTAN KÖSEDAĞ
- Investigation of impact behavior of the nano-scaled particle filled hybrid composite plates
Nano katkılı hibrit kompozit plakaların darbe davranışlarının incelenmesi
NURETTİN FURKAN DOĞAN
Doktora
İngilizce
2019
Makine MühendisliğiGaziantep ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. AHMET ERKLİĞ
- Vakum infüzyon yöntemiyle yama yapılmış hibrid kompozit plaklarda lineer olmayan burkulma analizi
Nonlinear buckling analysis in patched hybrid composite plates by vacuum infusion method
SERKAN ERDEM
Doktora
Türkçe
2020
Makine MühendisliğiFırat ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. MUSTAFA GÜR
- Tabakalı kompozit levhaların balistik performanslarının incelenmesi
Investigation on ballistic performance of layered composite plates
FERHAT ATEŞ
Yüksek Lisans
Türkçe
2024
Makine MühendisliğiDicle ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ GURBET ÖRÇEN