Yeni nesil CAD/CAM materyallerin yüzeylerinde farklı yüzey bitirme işlemleri sonrasında gastrik sıvı etkisi ile oluşabilecek bakteriyel adherensin araştırılması
Investigation of bacterial adherence on the surface of new generation CAD/CAM materials that may occur with the effect of gastric juice after different surface finishing processes
- Tez No: 755841
- Danışmanlar: PROF. DR. SEDANUR TURGUT
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: CAD/CAM, Dental materyaller, Dental restorasyon, Gastrik asit, Streptococcus mutans, Yüzey parlatma, CAD/CAM, Dental materials, Dental restoration, Gastric acid, Streptococcus mutans, Surface polishing
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Çalışmanın amacı; diş hekimliğinde yaygın olarak kullanılan estetik CAD/CAM restoratif materyallerin yüzeyinde oluşabilecek bakteriyel adherense, farklı yüzey bitim işlemlerinin ve gastrik sıvının etkisinin değerlendirilmesidir. Bu çalışmada, Vita Enamic (EN), Vita Suprinity (SP), Cerasmart (CS), Lava Ultimate (LU) ve IPS e.max ZirCAD (ZC) materyalleri kullanıldı. 5x5x1 mm boyutlarında toplam 160 adet örnek elde edildi (n=8). Örneklere polisaj (P) veya glaze (G) yüzey işlemleri uygulandı. Sonrasında örnekler in-vitro şartlarda 24 saat gastrik sıvıya maruz bırakıldı ve otoklavda steril edildi. Örnekler sentetik tükürükte 1 saat bekletildi. Örneklerin S. mutans suşu ile inkübasyonu ardından yüzeyde oluşan S. mutans kolonileri sayıldı. Üç yönlü Anova ve Bonferroni testi ile istatistiksel analizleri yapıldı (p<0.05). Materyal*yüzey bitirme faktörlerinin ikili etkileşiminin bakteriyel adherens miktarını anlamlı derecede etkilemediği bulundu (p>0.05). Materyal*gastrik sıvı ve yüzey işlemi*gastrik sıvı faktörlerinin ikili etkileşiminin bakteriyel adherens miktarını anlamlı derecede etkilediği bulundu (p<0.001). Materyal*yüzey işlemi*gastrik sıvı* her üç parametrenin de S. mutans adherens miktarına etkisi istatiksel olarak anlamlı bulundu (p=0.01). Kontrol gruplarında (gastrik sıvı uygulanmayan), yüzey bitirme işlemlerinin S. mutans adherens miktarını farklı etkilemediği görüldü (p>0.05). Gastrik sıvı uygulanan örneklerde ise, farklı yüzey bitirme işlemlerinin gruplar arasında anlamlı farklılıklar oluşturduğu gözlendi (p<0.05). Gastrik sıvı uygulanan glazeli SP ve CS gruplarında istatiksel olarak anlamlı farklılıklar oluştu (p<0.05). Yüzey işlemlerinden bağımsız olarak gastrik sıvı; EN, SP, CS, LU, ZC yüzeylerinde S.mutans adherens miktarını arttırıcı etki göstermektedir. Gastroözofajial reflü ya da bulimia hikayesi olan hastalarda glaze uygulanmış SP ya da CS materyallerini tercih etmek bakteriyel tutulumun daha az olması için uygun olacaktır.
Özet (Çeviri)
Investigation of Bacterial Adherence on The Surface of New Generation CAD/CAM Materials That May Occur With The Effect of Gastric Juice After Different Surface Finishing Processes The aim of the study is to evaluate the effect of different surface finishing processes and gastric juice on the bacterial adherence that may occur on the surface of aesthetic CAD/CAM restorative materials which are commonly used in dentistry. In this study, Vita Enamic (EN), Vita Suprinity (SP), Cerasmart (CS), Lava Ultimate (LU) and IPS e.max ZirCAD (ZC) materials were used. Total of 160 samples with the dimensions of 5x5x1 mm were obtained (n=8). Polishing (P) or glaze (G) surface treatments were applied to the samples. Afterwards, the samples were exposed to gastric juice for 24 hours under in-vitro conditions and sterilized in an autoclave. Samples were kept in synthetic saliva for 1 hour. After incubation of samples with S. mutans strain, S. mutans colonies formed on the surfaces were counted. Statistical analyzes were performed using Three-Way Anova and Bonferroni tests (p<0.05). It was found that the interaction of material*surface finishing factors did not significantly affect the amount of bacterial adherence (p>0.05). It was found that the interaction of material*gastric juice and surface treatment*gastric juice significantly affected the amount of bacterial adherence (p<0.001). Material*surface treatment*gastric juice* the effect of the three parameters on the amount of S. mutans adherence was found to be statistically significant (p=0.01). In the control groups (no gastric juice applied), it was observed that the surface finishing treatments did not affect the amount of S. mutans adherence differently (p>0.05). The specimens that were treated with gastric juice, it was observed that different surface finishing treatments caused significant differences between the groups (p<0.05). Statistically significant differences were performed in the glazed applied SP and CS groups which were treated with gastric juice (p<0.05). Regardless of the surface treatment, gastric juice increases the amount of S.mutans adherence on EN, SP, CS, LU, ZC surfaces. In patients with a history of gastroesophageal reflux or bulimia, it would be more convenient to prefer glazed SP or CS materials to reduce the bacterial adherence.
Benzer Tezler
- Kısa fiber ile güçlendirilen posterior overlay restorasyonların, kırılma dirençlerinin, farklı kalınlıktaki CAD/CAM restoratif materyalleri ile karşılaştırılması
Comparison of fracture resistance of short fiber reinforced posterior overlay restorations with different thicknesses CAD/CAM restorative materials
ALPTEKİN YUSUF KÖK
Doktora
Türkçe
2025
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. SADULLAH ÜÇTAŞLI
- Bilgisayar destekli üretilen yeni nesil kaide materyallerinin farklı PH değerlerindeki mikrobiyolojik özelliklerinin değerlendirilmesi
Evaluation of microbiological properties of computer-aided new generation denture base materials at different PH values
EZGİ ARSLAN
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiEskişehir Osmangazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. CANAN AKAY
- Farklı nikel-titanyum aletlerin CAD/CAM kullanılarak seramik blok üzerinde simüle edilmiş farklı kök kanal eğriliklerinde döngüsel yorulma dirençlerinin karşılaştırılması
Comparison of cyclic fatigue resistance of different nickel-titanium instruments various root canal curvatures simulated on ceramic block using cad/cam
TUĞÇENUR YILDIZ
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiSivas Cumhuriyet ÜniversitesiEndodonti Ana Bilim Dalı
DOÇ. DR. RECAİ ZAN
- Yeni nesil farklı ışık geçirgenliğine sahip tam kristalize CAD/CAM seramik materyallerin farklı yüzey bitirme işlemi ve yaşlandırma sonrası yüzey pürüzlülüğü, ışık geçirgenliği ve renk değişiminin in vitro değerlendirilmesi
In vitro evaluation of surface roughness, light transmission and color change after different surface finishing and aging of new generation fully crystallized CAD/CAM ceramic materials with di̇fferent light transmi̇ttance
BAŞAK TIMARCIOĞLU
Doktora
Türkçe
2024
Diş HekimliğiSağlık Bilimleri ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ CUMHUR KORKMAZ
- Farklı CAD/CAM materyallerin renk stabiliteleri ve yüzey özelliklerinin değerlendirilmesi
Evaluation of color stability and surface properties of different CAD/CAM materials
AYÇA TOPALOĞLU
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiSüleyman Demirel ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. HAKKI CENKER KÜÇÜKEŞMEN