Pota cürufu ve silika bazlı sentetik cüruf kullanılarak oluşturulan cürufların MgO-C tuğlaları üzerindeki korozyon profillerinin incelenmesi

Examination of penetration behavior of MgO-C refractory bricks used in steel ladles slag zone against different quality steel slags

  1. Tez No: 761806
  2. Yazar: BERKAY YILMAZ
  3. Danışmanlar: DR. ÖĞR. ÜYESİ SERDAR ASLAN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2022
  8. Dil: Türkçe
  9. Üniversite: Sakarya Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 95

Özet

Bu çalışmada, Kardemiş AŞ. Pota fırınlarında üretilen on farklı çelik kalitesine ait cürufun, çelik potası cüruf bölgesinde kullanılan MgO-C refrakter tuğlalara olan etkilerinin incelenmesi hedeflenmiştir. Bu doğrultuda, refrakter tuğlalardan kroze oluşturulmuş ve cüruf numuneleri içerilerine doldurularak“Cüruf – Refrakter Penetrasyon Testi”uygulanmıştır. Penetrasyon testi sonuçları; makro, taramalı elektron mikroskobu ve görüntü işleme yöntemleri ile irdelenmiştir. Çalışma kapsamında hazırlanan refrakter krozelerin içerisine cüruf doldurulmuş ve fırına şarj edilmiştir. Krozeler, 3 saatte 1600 °C sıcaklığa ulaşılmış ve pota fırınlarında yaklaşık işlem sıcaklığı olan 1600 °C'de 2 saat bekletilerek etkileşim sağlanmıştır. Cüruf – Refrakter korozyon testinin tamamlanmasının ardından, etkileşim alanında korozyon alanının hesaplanması amaçlanmıştır. Bu doğrultuda, cüruf-refrakter etkileşim bölgelerinde penetrasyon görülen bölgelerden alınmış SEM görüntüsü üzerinden“ImageJ”programı yardımı ile analizler gerçekleştirilmiştir. MgO-C refrakter krozeler ile cüruf numuneleri arasındaki etkileşimin anlaşılması amacıyla ergitme sonrasında taramalı elektron mikroskobu kullanılarak, cüruf – refrakter etkileşim alanlarında noktasal, alansal ve çizgisel mikro-kimyasal analizler yapılmıştır. EDS nokta analizlerinden, refrakterin MgO ve C esaslı olduğu, kullanılan cürufların ise Mg, Si, Al, Ca elementlerini içerdiği belirlenmiştir. Cüruf penetrasyonunun etkin bir şekilde gerçekleştiği 6,7 ve 8 numaralı numuneler haricinde cürufun refrakter malzemeye nüfuz edemediği görülmüştür. Korozyonun gerçekleştiği bölgelerde, cüruftan refraktere Ca difüzyonu, refrakterden cürufa ise Mg ve C difüzyonlarının olduğu tespit edilmiştir. Bu doğrultuda, SEM görüntülerinde etkin bir korozyonun görülmediği numunelerde dahi etkileşimin gerçekleştiği sonucuna varılmıştır.

Özet (Çeviri)

In this study, It is aimed to investigate the effects of slag belonging to ten different steel grades produced in Kardemiş A.Ş. ladle furnaces on MgO-C refractory bricks used in the steel ladle slag region. In this direction, a cross-section was formed from refractory bricks and slag samples were filled in and the“Slag - Refractory Penetration Test”was applied. The penetration test results were examined by macro, scanning electron microscopy and image processing methods. The slag was filled into the refractory crucibles prepared within the scope of the study and charged into the oven. The crucibles reached a temperature of 1600 °C in 3 hours and the interaction was achieved by holding them for 2 hours at 1600 °C, which is the approximate process temperature in ladle furnaces. After the completion of the slag – Refractory corrosion test, it is aimed to calculate the corrosion area in the interaction area. In this direction, analyzes were carried out with the help of the“ImageJ”program using the SEM image taken from the areas where penetration was observed in the slag-refractory interaction zones. In order to Decipher the interaction between MgO-C refractory crozes and slag samples, point, spatial and linear microchemical analyses were performed in the slag–refractory interaction areas using scanning electron microscopy after melting. From the EDS point analysis, it was determined that the refractory is based on MgO and C, and the slags used to contain the elements Mg, Si, Al, and Ca. It has been observed that slag cannot penetrate the refractory material, except for samples 6,7 and 8, where slag penetration occurs effectively. In the regions where corrosion occurs, Ca diffusion from the slag to the refractory, and Mg and C diffusion from the refractory to the slag have been found. Accordingly, it was concluded that the interaction occurred even in samples where no effective corrosion was observed in SEM images

Benzer Tezler

  1. Laboratuvar tipi elektrik ark fırını tasarımı ve e-atıktan öğütülebilir alaşım üretimi

    Design of laboratory scale electrical arc furnace and production of grindable alloy from e-waste

    RIDVAN ORMAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. SERVET İBRAHİM TİMUR

  2. Preliminary studies in the production of FeV from fuel oil slag formed in power plants

    Fuel oil termik santral cürufundan FeV üretimi ön çalışmaları

    GÜNEŞ YAKUPOĞLU

    Yüksek Lisans

    İngilizce

    İngilizce

    2009

    Metalurji MühendisliğiMarmara Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. ERSAN KALAFATOĞLU

    YRD. DOÇ. DR. SEVAL GENÇ

  3. Sürekli döküm tandişlerindeki cüruf ile refrakter etkileşimleri

    Slag and refractory interactions in continuous casting tundishes

    İSMAİL ŞİŞLİ

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Metalurji MühendisliğiKarabük Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. ALİ GÜNGÖR

  4. Na2O - B2O3 ikili curuf sisteminin kükürt kapasitesinin incelenmesi

    Examining sulphide capacity of Na2O - B2O3 binary slag system

    BURAK TARHAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2013

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. CEVAT BORA DERİN

  5. Geri dönüştürülebilir atık malzemelerin yol dolgusunda kullanılabilirliğinin karşılaştırılmalı olarak incelenmesi

    Comparative analysis of the usability of recyclable waste materials in road embankment

    ŞÜHEDA TAŞTAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    İnşaat Mühendisliğiİstanbul Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ ASLI YALÇIN DAYIOĞLU