X120MN12 çeliğinin döküm ve ısıl işlem şartlarının; mikroyapı, mekanik ve aşınma özelliklerine etkisinin incelenmesi

Casting and heat treatment conditions of X120MN12 steel; investigation of the effect on microstructure, mechanical and wear properties

PDF İndir

  1. Tez No: 762929
  2. Yazar: BERKAN SARDOĞAN
  3. Danışmanlar: DOÇ. DR. MEHMET ÜNAL
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2022
  8. Dil: Türkçe
  9. Üniversite: Karabük Üniversitesi
  10. Enstitü: Lisansüstü Eğitim Enstitüsü
  11. Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 92

Özet

Östenitik manganlı çeliklerin arasında yer alan X120Mn12 (HADFIELD) çeliğinin döküm yönteminin ve ısıl işlem şartlarının: mukavemet özellikleri ile aşınma özelliklerine olan etkisinin incelenmesi ve arttırılması tezimin konusunu oluşturmaktadır. Belirlenen alaşımın kimyasal özellikler değiştirilmeden kum kalıba ve kokil kalıba olmak üzere altı döküm yapılmıştır. Elde edilen numunelerden kum kalıba ve kokil kalıba dökümden birer numuneye ısıl işlem uygulanmamış, kum kalıba ve kokil kalıba dökümden birer numuneye 1100 °C'de ısıl işlem uygulanıp suda soğutulmuş, kum kalıba ve kokil kalıba dökümden birer numuneye 1100 °C'de ısıl işlem uygulanıp yağda soğutulmuştur. Bu numunelerin çekme, çentik, sertlik, aşınma, mikroyapı, SEM, EDX testleri yapılmış ve karşılaştırılmıştır. Yapılan dökümler doğrultusunda; mikroyapı incelemelerinde tane boyutlarındaki farklılıklar, tane sınırlarındaki ve östenit tane sınırı içerisindeki karbür oluşumları gözlenmiştir. Tane sınırlarındaki karbür yapılarının yapılan ısıl işlemlerle inceldiği ve koptuğu, östenit fazı içerisine bu karbürlerin homojen olarak yayıldığı görülmüştür. Mikroyapı ve SEM incelemeleri doğrultusunda bu karbür yapılarının tane içerisine dağılması akma ve çekme değerlerinin artmasını sağlamıştır. Akma ve çekme değeri en yüksek olan kokil kalıba döküm yağda soğuma ısıl işlemi uygulanan numune olmuştur. Bu mekanik özelliklerin etkisiyle aşınmaya karşı dayanımı en yüksek olan kokil kalıba döküm yağda soğuma ısıl işlemi uygulanan numune olmuştur.

Özet (Çeviri)

The subject of my thesis is to examine and increase the effect of casting method and heat treatment conditions of X120Mn12 (HADFIELD) steel, which is among the austenitic manganese steels, on the strength properties and wear properties. Six castings were made in sand mold and permanent mold without changing the chemical properties of the determined alloy. From the samples obtained, one sample from the sand mold and one sample from the permanent mold casting was not applied heat treatment, one sample from the sand mold and one sample from the permanent mold was heat treated at 1100 °C and cooled in water, one sample from the sand mold and one sample from the permanent mold was heat treated at 1100 °C. cooled in oil. Tensile, notch, hardness, abrasion, microstructure, SEM, EDX tests of these samples were performed and compared. In line with the castings; In microstructural examinations, differences in grain sizes, carbide formations at grain boundaries and within austenite grain boundaries were observed. It was observed that the carbide structures at the grain boundaries were thinned and ruptured with the heat treatments, and these carbides were spread homogeneously into the austenite phase. In accordance with the microstructure and SEM investigations, the dispersion of these carbide structures into the grain increased the yield and tensile values. The sample with the highest yield and shrinkage value was the sample, which was treated with oil cooling heat treatment in permanent mold casting. With the effect of these mechanical properties, it was the sample that had the highest resistance to abrasion, and the oil cooling heat treatment was applied to the permanent mold casting.

Benzer Tezler

  1. Tez No

    810895

    X120Mn12 çeliğinin çamurlu erozif aşınma davranışının incelenmesi

    Investigation of slurry erosive wear behavior of X120Mn12 steel

    GAYENUR TEKER ÇELİK

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Makine MühendisliğiKarabük Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. RECEP DEMİRSÖZ

  2. Tez No

    726993

    Yük vagonu imalatında x120mn12 çeliği yerine Hardox 550 çeliğinin kullanılmasının aşınma davranışı ve kaynak edilebilirlik üzerine etkisinin araştırılması

    Investigation of the effect of using Hardox 550 steel in place of x120mn12 steel on wear behavior and weldability in manufacturing of freight wagon

    OĞUZHAN ATLI

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Makine MühendisliğiOndokuz Mayıs Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. KEMAL YILDIZLI

  3. Tez No

    887978

    Maden sanayisinde kullanılan Hadfield çeliğinin aşınma özelliklerinin geliştirilmesi

    Improvement of wear properties of Hadfield steel used in the mining industry

    MEHMET ALTAN SERTKAYA

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    Makine MühendisliğiGazi Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. YUSUF USTA

  4. Tez No

    57330

    Kazı makinası (1900 Al ekskavatör) kepçe dişi üzerinde uygulanan ısıl işlemlere bağlı olarak Ç 1060, Ç 4140 ve G-x 120 Mn 12 çeliklerinin aşınma davranışların incelenmesi

    Başlık çevirisi yok

    RECEP BOZKURT

    Yüksek Lisans

    Türkçe

    Türkçe

    1996

    Makine MühendisliğiUludağ Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. A. HALİM DEMİRCİ

Geri Dön