Cam-seramik ve katıhal reaksiyon yöntemleri ile LiFePO4 üretimi ve elektrokimyasal performanslarının araştırılması

Production of LiFePO4 by glass-ceramic and solid state reaction methods and investigation of it's electrochemical performance

PDF İndir

  1. Tez No: 766640
  2. Yazar: EZGİ GÜLTEK
  3. Danışmanlar: PROF. DR. SERDAR ALTIN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Enerji, Energy
  6. Anahtar Kelimeler: lityum, batarya, enerji, LFP, cam-seramik, katıhal. Li-ion, lithium, battery, energy, LFP, glass-ceramics, solid state, Li-ion
  7. Yıl: 2022
  8. Dil: Türkçe
  9. Üniversite: İnönü Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Enerji Bilim ve Teknoloji Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 154

Özet

Bu yüksek lisans tez çalışmasında elektriksel cihazlarda ve platformlarda kullanılmak üzere lityum bazlı kurşun katkılamalı katotlar üretilmiştir. Bu üretim için cam-seramik yöntemi kullanılmıştır. Öncelikli olarak saf LiFePO4 üretilmiş ve daha sonra kurşun (Pb) katkılı katot üretimleri yapılmıştır. Li1,4Fe1-xPbxPO4 formülü kullanılarak yapılan bu çalışmada, x değişkeni 0-0.03-0.06-0.09 ve 0.12 olarak belirlenmiştir. Sentezlenen katot malzemelerinde %99.9 saflık oranındaki Li₂O, Fe₂O₃, PbO ve P₂O₅ kimyasalları kullanılarak, asetonla bilyalı öğütücüde 450 rpm hızında 18 saat karışım yapılmıştır. Öğütülen tozlar alumina potalara koyularak 1200˚C 'de 2 saat, erime işlemi için elektrikli fırına koyulmuştur. Ani soğutma yapmak üzere fırından çıkarılan cam malzeme, sıvı nitrojen kullanılarak dondurulmuştur. Havanda asetonla beraber homojenize olarak toz haline getirilen malzeme %10 oranındaki glikoz ile öğütülmüştür. Hazırlanan numune, 5 dakikada 850˚C sıcaklığa çıkıp, 12 saat bekleyecek şekilde ısıl işleme tabi tutulmuştur. Bu ısıl işlem kuvars tüplü, %7 Ar/H₂ gazının bulunduğu bir fırında yapılmıştır. Yapılan çalışmanın güvenilirliği ve kıyaslanması açısından az uygulanmış bir cam-seramik yöntemine karşılık; sık kullanılan katı hal yöntemi ile farklı bir prosedür izlenerek aynı formül ve katkılama oranlarında üretim gerçekleştirilmiştir. Bu yöntemde yine %99.9 saflık oranındaki Li2CO3, FeC2O4.2H2O, NH4H2PO4, PbO ve C6H12O6 kullanılmıştır. Tüm malzemeler sitokiyometrik oranlarda 350 rpm hızında 5 saat asetonla bilyalı öğütücüde karıştırılıp etüvde kurutulmuştur. Ardından 10 saat 350˚ ısıl işleme tabi tutulup elde edilen malzeme, 500 rpm hızında 5 saat asetonla tekrar bilyalı öğütücüde öğütülmüştür. Elde edilen karışım son olarak 650˚, 12 saat ısıl işleme bırakılmıştır. İki prosedür için de ayrı ayrı; fiziksel karakterizasyon ve elektrokimyasal analizler yapılmıştır. Bu veriler sonucunda şarj edilebilen lityum pil üretilebilmiştir. Morfolojik yapıları incelendiğinde safsızlığın gözlemlenmediği ve kristalizasyonun gerçekleşip olivin yapının elde edildiği, Pb-Fe yer değişiminin gerçekleştiği gözlemlenmiştir. Elde edilen kapasiteler, akım ve voltaj değerleri grafiklerle değerlendirilmiştir. Katkılama ile kapasite değerinde artış gözlemlenip cam-seramik yönteminde en yüksek kapasite 80 mAh/g, katı hal yönteminde en yüksek kapasite 140 mAh/g olmuştur.

Özet (Çeviri)

In this master thesis, lithium-based lead doped cathodes were produced for use in electrical devices and platforms. Glass ceramic method was used for this production. First of all, pure LiFePO4 was produced and then lead (Pb) doped cathodes were produced. This is done using the formula Li1,4Fe1-xPbxPO4 in the study, the variable x was determined as 0-0.03-0.06-0.09 and 0.12. By using Li₂O, Fe₂O₃, PbO and P₂O₅ chemicals with 99.9% purity in the synthesized cathode materials, acetone was mixed in a ball mill at 450 rpm for 18 hours. Grinding powders were put into crucibles and placed in an electric furnace for 2 hours at 1200˚C for melting. The glass material removed from the furnace was frozen using liquid nitrogen for instant cooling. The material, wich was homogenized and pulverized with acetone in a mortar, was ground with 10% glucose. The prepared humune was subjected to heat treatment by rising to 850˚C in 5 minutes and waiting for 12 hours. This heat treatment was carried out in a quartz tube furnace with 7% Ar/H₂ gas. In contrast to a less applied glass ceramic method in terms of reliability and comparison of the study; by following a different procedure with the frequently used solid state method, production was carried out with the same formula and doping ratios. In this method, Li2CO3, FeC2O4.2H2O, NH4H2PO4, PbO and C6H12O6 with 99.9% purity were used. All materials were mixed in a ball mill with acetone at 350 rpm at stoichiometric ratios for 5 hours and dried in an oven. Then, it was subjected to heat treatment at 350˚C for 10 hours and the obtained material was ground in a ball mill again with acetone at 500 rpm for 5 hours. The resulting mixture was finally heat treated at 650˚C for 12 hours. Separately for both procedures; physical characterization and electrochemical analyzes were carried out. As a result of these datas, a rechargeable lithium battery was produced. When their morphological structures were examined, it were observed that no impurities were observed, crystallization took place and olivine structure was obtained, and Pb-Fe substitution took place. Obtained capacites, current and voltage values were evaluated with graphics. An increase was observed in the capacity value with doping, and the highest capacity was 80 mAh/g in the glass-ceramic method, and the highest capacity was 140 mAh/g in the solid state method.

Benzer Tezler

  1. Tez No

    352481

    Synthesis of Ce(III) and Eu(III) doped YAG (Y3Al5O12) and ZnO ceramics

    Ce(III) ve Eu(III) katkılı YAG (Y3Al5O12) ve Zno seramiklerinin sentezi

    REFİK ERGÜN

    Yüksek Lisans

    İngilizce

    İngilizce

    2014

    Seramik MühendisliğiKoç Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. UĞUR ÜNAL

  2. Tez No

    536802

    Kristalografik yönlenmenin Li(1+x)AlxTi(2-x)(PO4)3 katı elektrolitlerinin iyonik iletkenliğine etkisi

    Effect of crystallographic orientation on ionic conductivity of Li(1+x)AlxTi(2-x)(PO4)3 solid electrolytes

    CEM EREN ÖZBİLGİN

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    EnerjiEskişehir Teknik Üniversitesi

    PROF. DR. SERVET TURAN

    DR. ÖĞR. ÜYESİ EMRAH DÖLEKÇEKİÇ

  3. Tez No

    202541

    BiPbSrCaCuO seramik süperiletkenlerde onset sıcaklığının katkı oranlarına göre değişimi

    The variation of onset temperature with substitutional ratio in BiPbSrCaCuO ceramic superconductors

    EBRU KIŞ ÇAM

    Yüksek Lisans

    Türkçe

    Türkçe

    2005

    Fizik ve Fizik MühendisliğiDokuz Eylül Üniversitesi

    Fizik Ana Bilim Dalı

    PROF. DR. KEMAL KOCABAŞ

  4. Tez No

    893505

    Development of high near-infrared (NIR) reflective black pigments

    Yüksek yakın kızılötesi (NIR) yansıtıcı siyah pigmentlerin geliştirilmesi

    EMRE TOY

    Yüksek Lisans

    İngilizce

    İngilizce

    2024

    Metalurji MühendisliğiYıldız Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    DOÇ. DR. BUĞRA ÇİÇEK

  5. Tez No

    300146

    Katkılandırılmış lityum silikat camsı seramiklerin sentezi ve lüminesans özelliklerinin incelenmesi

    Synthesis and investigation of luminescence properties of doped lithium silicate glass ceramics

    İSRAFİL ŞABİKOĞLU

    Doktora

    Türkçe

    Türkçe

    2011

    Fizik ve Fizik MühendisliğiCelal Bayar Üniversitesi

    Fizik Ana Bilim Dalı

    PROF. DR. NURDOĞAN CAN

Geri Dön