Klinker öğütme silpeps'lerinin alaşım katkı oranlarına bağlı abrasiv aşınma davranışlarının araştırılması

A Research, resistance of grinding silpeps relatively alloying elements

  1. Tez No: 77625
  2. Yazar: ŞİNASİ ELÇİ
  3. Danışmanlar: DOÇ. DR. HALİS ÇELİK
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 1998
  8. Dil: Türkçe
  9. Üniversite: Fırat Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji Eğitimi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 85

Özet

ÖZET Yüksek Lisans Tezi KLİNKER ÖĞÜTME SİLPEPS'LERİNİN, ALAŞIM KATKİ ORANLARINA BAĞLI ABRASİV AŞINMA DAVRANIŞLARININ ARAŞTIRILMASI Şinasi ELÇİ Fırat Üniversitesi Fen Bilimleri Enstitüsü Metalürji Eğitimi Anabilim Dalı 1998, Sayfa: 71 Bu araştırmada, yüksek krom alaşımlı dökme demir malzemelerin oda sıcaklığındaki aşınma davranışları incelenmiştir. Aşınma testlerinde alüminyum oksit ve silisyum karbür taneli abrası v aşındırma kağıtları kullanılmıştır. Kırşehir Çelik Döküm Fabrikasında halen üretilmekte olan orjinal malzemelere değişik alaşım elementleri ve değişik ısıl işlemler uygulanarak dökme demir numuneler elde edilmiştir. İki adet orjinal malzeme ve otomat çeliği mukayese malzemeleri olarak kullanılmışlardır. Aşınma deneyleri pirn-disk (pin-on disk) test cihazında yapılmıştır.II Pim-disk aşınma cihazında iki farklı yük ( 55.6 N ve 100 N ) kullanılmıştır. Bu deneylerde kullanılan numune boyutları 16 mm çap ve yaklaşık 16 mm boyutlarındadır. Abrası' v aşındırıcı olarak 60 numaralı alüminyum oksit ve 80 numaralı silisyum karbür kağıtlar kullanılmıştır. Her bir deney numunesi için en az üç deney yapılmıştır. Deneyden sonra numuneler aseton ile temizlenerek 10~4 g hassesi yeti i terazi ile ağırlık kayıpları tesbit edilmiştir. Pim disk aşınma cihazında, aşınma için kayma yolu 4.43 m dir. Numunelerin mikroskobik incelemeleri optik metal mikroskobunda yapılmıştır. Fazların ve karbürlerin belirlenmesi için değişik dağlayıcılar kullanılmış ve fotoğrafları çekilmiştir. Sonuç olarak, numunelere ilave edilen bazı alaşım elementleri ve yapılan ısıl işlemler ile numunelere aşınma direnci kazandırılmıştır.

Özet (Çeviri)

II! SUMMARY Masters Thesis THE INVESTIGATION OF ABRASIVE WEAR BEHAVIOUR OF 6RINDIN6 SUPERS WITH RESPECT TO ALLOVING CONTENTS Şi nasi ELÇİ Fırat University Institute of Science and Technology Metallurgical Education Department 1 998, Page : 7 1 In this study, abrasive wear behaviour of high chromium cast irons were examined at the room temperature. A1“0, and SIC abrasives, 80 qrit were used for this study. The reference specimens and research specimens were produced at Kırşehir Steel Casting Factory (ÇEMAŞ). Research specimens were produced adding some alloying elements to ÇEMAŞ* original product. In addition research specimens were heat treated. Two original steels were used as comparison materials. Abrasion tests were carried out on a pin-on disc tester. Two different loads were applied to the specimens on this tester (55,6 N and 100 N).IV Pin specimens were manufactured 16 mm in diameter and 16 mm in length. Every specimen were abraded at least three times and average values were taken for calculations. Mass losses of specimens were measured using 10”4 g balance. For abrasion, sliding distance was 4.43 m. Carbides and matrix were identified by etching. The microstructures of specimens were examined using optical microscope. As a result, this research was done to produce better wear resistant materials.

Benzer Tezler

  1. Tez No

    97774

    Klinker öğütme prosesinin matematiksel modellemesi

    Mathematical modelling of clinker grinding process

    HAKAN BENZER

    Doktora

    Türkçe

    Türkçe

    2000

    Maden Mühendisliği ve MadencilikHacettepe Üniversitesi

    Maden Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MUAMMER ÖNER

    DOÇ. DR. Ş. LEVENT ERGÜN

  2. Tez No

    708533

    Farklı tip klinker öğütme kolaylaştırıcı katkı kullanımının çimentolu sistemlerin özelliklerine etkisi

    The effect of utilization of different types of clinker grinding aids on the properties of cement systems

    YAHYA KAYA

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    İnşaat MühendisliğiBursa Uludağ Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. ALİ MARDANİ AGHABAGLOU

  3. Tez No

    75729

    Effects of clinker composition on the properties of pozzolonic cements

    Klinker kompozisyonunun, puzolanik çimentoların özelliklerine etkileri

    ARIN YILMAZ

    Yüksek Lisans

    İngilizce

    İngilizce

    1998

    İnşaat MühendisliğiOrta Doğu Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MUSTAFA TOKYAY

  4. Tez No

    222211

    Bilyalı değirmenlerde bazı öğütme parametrelerinin modellenmesi ve optimizasyonu

    Modeling and optimization of some grinding parameters for ball mill

    NUH AKÇİÇEK

    Yüksek Lisans

    Türkçe

    Türkçe

    2007

    Maden Mühendisliği ve MadencilikCumhuriyet Üniversitesi

    Maden Mühendisliği Bölümü

    YRD. DOÇ. DR. NEVZAT ASLAN

  5. Tez No

    202534

    Çimento klinker fazlarının mikro yapısı ve öğütme parametreleri arasındaki ilişkilerin araştırılması

    Investigations the relationship between the microstructures of cement clinker pahses and their grindabilities

    DİYAL GÜLLÜ

    Yüksek Lisans

    Türkçe

    Türkçe

    2006

    DemografiDokuz Eylül Üniversitesi

    Maden Mühendisliği Bölümü

    YRD. DOÇ. DR. UFUK MALAYOĞLU

Geri Dön