Fabrication of drug-loaded janus nanoparticles with microfluidic system
Mikroakışkan sistem ile ilaç yüklü janus nanopartiküllerin üretimi
- Tez No: 787632
- Danışmanlar: DOÇ. DR. CEM BÜLENT ÜSTÜNDAĞ
- Tez Türü: Yüksek Lisans
- Konular: Biyomühendislik, Biyoteknoloji, Polimer Bilim ve Teknolojisi, Bioengineering, Biotechnology, Polymer Science and Technology
- Anahtar Kelimeler: Janus parçacıkları, Kontrollü ilaç salımı, Mikro akışkanlar, Polimerik partiküller, Taramalı elektron mikroskobu, Janus particles, Controlled drug release, Microfluidics, Polymeric particles, Scanning electron microscope
- Yıl: 2023
- Dil: İngilizce
- Üniversite: Yıldız Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Biyomühendislik Ana Bilim Dalı
- Bilim Dalı: Biyomühendislik Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Polimerik ilerlemenin çok işlevli polimorfik yapısının ilerlemesi son yıllarda öncelik kazanmıştır. Bu tez çalışmasında polimerik janus tipi baloncuklardan partikül oluşumları değerlendirilmiştir. %3 PLA ve ağırlıkça %3 PEG, 1000 μm VJM aparatı ile 275 μl/dk, 180 μl/dk 0,012 MPa basınçta sisteme beslenerek janus mikrobaloncuklar elde edilip karakterizasyon sonuçları incelenmiştir. Fonksiyonel grupların analizi, Fourier dönüşümü kızılötesi spektroskopisi (FTIR) ile gerçekleştirilirken, farklı özel çözücülerin etkisi altındaki Janus tipi mikrobaloncuklardaki morfolojik farklılıklar, Taramalı Elektron Mikroskobu (SEM), ışık mokroskobu ve konfokal mikroskobu ile incelenmiştir. Boyutlar 5 μm-189 nm arasında değişenkenlik göstermiştir. Partikül yapısı seçilerek janus taşıyıcıların içerisine model olarak seçilen amfoterisin-B, gentamisin enkapsüllerenerek ilaç salım profilleri incelenmiştir.
Özet (Çeviri)
The advance of the multifunctional polymorphic nature of polymeric progression has gained priority in recent years. In this thesis, particle formations from polymeric janus-type bubbles were evaluated. For this purpose, 3% wt% PLA and 3% wt% PEG were integrated into the system with a 1000 μm VJM junction at 275 μl/min, 180 μl/min at 0.012 MPa pressure to obtain janus-type microbubbles and the characterization results were examined. While the analysis of functional groups was performed by Fourier transform infrared spectroscopy (FTIR), the morphological differences were examined by Scanning Electron Microscopy (SEM), light microscope, and confocal microscopy. According to the results obtained, honeycomb and particle formation was observed at different scales ranging 5 μm -189nm. For drug implementation, hydrophobic and hydrophilic drugs were chosen; amphotericin-B, gentamicin and encapsulation and drug release profile were examined with the quantities of the particle obtained group.
Benzer Tezler
- Kam yapma aparatı
Cam milling attachment
ORHAN UZUN
Yüksek Lisans
Türkçe
1986
Makine MühendisliğiGazi ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. FEVZİ ERCAN
- Orisini özellikleri, oranları farklı L. bulgaricus ve s.thermophilus bakterileri içeren sıvı, dondurulmuş ve liyotilize kültürler ile yapılan yoğurtların nitelikleri üzerinde araştırmalar
Başlık çevirisi yok
SEVDA KILIÇ
Doktora
Türkçe
1986
Gıda MühendisliğiEge ÜniversitesiSüt Teknolojisi Ana Bilim Dalı
PROF. DR. HASAN YAYGIN
- Halı ipliği yapımında kullanılan yünlerin teknolojik özellikleri üzerinde araştırmalar
Investigations on the technological properties of wools which are used in woollen carpet yarn production
BEKİR YILMAZ
Doktora
Türkçe
1985
Tekstil ve Tekstil MühendisliğiEge ÜniversitesiTarım Ürünleri Teknolojisi Ana Bilim Dalı
PROF. DR. MUSTAFA HARMANCIOĞLU
- Düşük tenörlü pirolüzit cevherlerinden yeni bir MnSO4-H2O üretim metodu
Başlık çevirisi yok
MAHMUT BAYRAMOĞLU
Doktora
Türkçe
1983
Kimya Mühendisliğiİstanbul ÜniversitesiKimya Mühendisliği Bilim Dalı
DOÇ. DR. ÜNAL SANIGÖK