Structural, physical, and mechanical properties of the (Cu-nano MgO) system by powder metallurgy method
Toz metalürjisi yöntemiyle (Cu-nano MgO) sisteminin yapısal, fiziksel ve mekanik özellikleri
- Tez No: 788154
- Danışmanlar: PROF. DR. SEBAHADDİN ALPTEKİN, DR. ÖĞR. ÜYESİ SALİH YOUNİS DARWEESH
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Altın metalurjisi, Fiziksel özellikler, Mekanik özellikler, Taramalı elektron mikroskobu, Toz metalurjisi, X ışını kırınımı, Gold metallurgy, Physical properties, Mechanical properties, Scanning electron microscope, Powder metallurgy, X ray diffraction
- Yıl: 2023
- Dil: İngilizce
- Üniversite: Çankırı Karatekin Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada, toz metalurjisi tekniği kullanılarak bakır ve MgO kompozitlerinin hazırlanması ve nano MgO içeriğinin kompozitlerin yapısal, fiziksel ve mekanik özellikleri üzerindeki etkisinin test edilmesi amaçlanmıştır. MgO farklı yüzdelerde % (2, 4, 6, 8, 10) bakır yüzdeleri % (98, 96, 94, 92, 90) ile tavlanmıştır. Kullanılan tozlar bir saat boyunca 200 °C sıcaklıkta kurutulmuş ve 2 saat boyunca öğütülüp karıştırıldıktan sonra numuneler preslenmiş ve ardından iki saat boyunca 900 °C sıcaklıktaki bir fırında termal olarak sinterlenmiştir. Mevcut çalışmanın sonuçları magnezyum nanopartikülleri kullanılarak bakırın güçlendirilebileceğini göstermiştir. Cu yüksek sıcaklıklarda yumuşayan bir malzeme özelliği taşımaktadır. Bakıra MgO ekleyerek malzemenin farklı bir özellik gösterdiği ve sertliğinin arttığı gözlenmiştir. Görünür yoğunluk, hacimsel yoğunluk, mikroyapı, Vickers sertliği, mutlak gözeneklilik, EDS, su emme, termal iletkenlik, basınç dayanımı ve aşınma oranı gibi gerekli testler yapılmıştır. Ayrıca, kullanılan maddenin yapısını bulmak için SEM (Taramalı Elektron Mikroskobu) ve XRD (X-Işını Kırınımı) analizleri yapılmıştır.
Özet (Çeviri)
The aim of this study was to prepare copper and MgO composites using powder metallurgy technique and to test the effect of nano MgO content on the structural, physical and mechanical properties of the composites. MgO was annealed in different percentages (2, 4, 6, 8, 10)% with copper percentages (98, 96, 94, 92, 90)%. The powders used were dried at 200 °C for one hour and after grinding and mixing for 2 hours, the samples were pressed and then thermally sintered in an oven at 900 °C for two hours. The results of the present study showed that copper can be strengthened using magnesium nanoparticles. Cu is a material that softens at high temperatures. By adding MgO to copper, it was observed that the material showed a different property and its hardness increased. Necessary tests such as apparent density, apparent density, microstructure, Vickers hardness, absolute porosity, EDS, water absorption, thermal conductivity, compressive strength and wear rate were performed. In addition, SEM (Scanning Electron Microscope) and XRD (X-Ray Diffraction) analyses were performed to find the structure of the material used.
Benzer Tezler
- Doğuştan kalça çıkıklı hastalarda kalça patolojilerinin bilgisayarlı tomografi ile değerlendirilmesi
Başlık çevirisi yok
NECDET ŞÜKRÜ ALTUN
Tıpta Uzmanlık
Türkçe
1987
Ortopedi ve TravmatolojiGazi ÜniversitesiOrtopedi ve Travmatoloji Ana Bilim Dalı
PROF.DR. ORHAN ASLANOĞLU
- Dokuma kumaşlarda örgü tipinin ham kumaşın boyutları ve geometrik özellikleri üzerindeki etkilerinin araştırılması
Başlık çevirisi yok
EMEL ÖNDER
Yüksek Lisans
Türkçe
1985
Tekstil ve Tekstil MühendisliğiEge ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
DOÇ. DR. GÜNGÖR BAŞER
- Vecihi Bey'in hikayelerinde fiktif yapı
Başlık çevirisi yok
MEHMET ÖNAL
Yüksek Lisans
Türkçe
1985
Türk Dili ve EdebiyatıGazi ÜniversitesiTürk Dili ve Edebiyatı Ana Bilim Dalı
DOÇ. DR. SADIK TURAL
- Plazma arkı eldesi ve yüzey bölgesi modifikasyonunda kullanılabilirliği
Başlık çevirisi yok
ÖZKAN ÖZİPEKLİLER
Yüksek Lisans
Türkçe
1986
Makine MühendisliğiUludağ ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. HALİM DEMİRCİ
- Enez kili ve asitle etkileşmesinin kristal yapı bakımından x-ışını kırınım yöntemi ile incelenmesi
Başlık çevirisi yok
NEZİHE ÇALIŞKAN
Doktora
Türkçe
1986
Fizik ve Fizik Mühendisliğiİnönü ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. NİZAMETTİN ARMAĞAN
- 1,3-difenil-4,5-bis(hidroksiimino)-imidazolidin ve Ni(II), Cu(II), Pd(II), UO2(VI) komplekslerinin sentezi
Başlık çevirisi yok
VEFA AHSEN
Doktora
Türkçe
1984
Kimya MühendisliğiUludağ ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. ÖZER BEKAROĞLU