Alümina ile Ti6Al4V ve AISI 316L paslanmaz çeliğin aktif sert lehimleme yöntemi ile birleştirme parametrelerinin araştırılması
Investigation of joining parameters of alumina to Ti6Al4V ve AISI 316L stainless steel by active brazing method
- Tez No: 788793
- Danışmanlar: DOÇ. DR. BİLGE YAMAN ISLAK
- Tez Türü: Doktora
- Konular: Metalurji Mühendisliği, Mühendislik Bilimleri, Metallurgical Engineering, Engineering Sciences
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Eskişehir Osmangazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Malzeme Bilim Dalı
- Sayfa Sayısı: 153
Özet
Seramikler, metal malzemeler ile birleştirilerek muadili malzemelere kıyasla mekanik, termal, kimyasal dayanım gibi özellikler açısından çeşitli avantajlar sunmakta ve bu doğrultuda akademik ve endüstriyel alanda ilgi görmektedir. Son yıllarda birçok alanda kullanımı söz konusu olması ve geleneksel birleştirme yöntemlerine göre daha kolay ve kısa bir üretim prosesine sahip olması nedenleriyle aktif sert lehimleme yöntemine olan ilgi artmıştır. Ancak araştırmaların devam ederek literatürün bu konuda genişletilmesi gerekmektedir. Bu kapsamda yeterli mukavemete sahip alümina – metal yapıların elde edilmesi ihtiyacı bulunmaktadır. Bu tez çalışmasında medikal, havacılık ve savunma sanayinde tercih edilen seramik ve metal malzemelerin aktif sert lehimleme tekniği kullanılarak birleştirilmesi ve birleştirme işlemine yönelik parametrelerin tespit edilmesi amaçlanmıştır. Bu kapsamda alümina ile AISI 316L paslanmaz çelik ve Ti6Al4V titanyum alaşımı, gümüş bazlı aktif sert lehim dolgu alaşımı (63,0Ag, 35,25Cu, 1,75Ti) kullanılarak birleştirilmiştir. Farklı parametreler ile üretilen numunelerin; yüzey pürüzlülük etkisi, mikroyapısal karakterizasyon, mekanik ve ısıl şok testleri açısından değerlendirilerek proses optimizasyonu gerçekleştirilmiştir. İki ana metal için de 0,45 µm ortalama pürüzlülük değerine sahip seramik birleşme yüzeyi kullanılarak ve 10-5 mbar sert lehim vakum değerinde, 830°C'de 10 dakika aktif sert lehimleme prosesinin uygulanması durumunda en yüksek kesme mukavemet değerleri (66,62 - 61,58 MPa) elde edilmiştir.
Özet (Çeviri)
Joining ceramics to metal materials offers various advantages in terms of properties such as mechanical, thermal and chemical resistance compared to equivalent materials, and they attract attention in the academic and industrial fields. In recent years, the interest in active brazing method has increased due to its use in many areas and its easier and shorter production process compared to traditional joining methods. However, it is necessary to improve the literature data on this subject by continuing the researches. In this context, there is a need to obtain alumina-metal structures with sufficient strength. In this thesis, it is aimed to join ceramic and metal materials, which are preferred in the medical, aerospace and defense industries, by active brazing technique and to determine the parameters for the joining process. In this context, alumina and AISI 316L stainless steel and Ti6Al4V titanium alloy were joined using silver-based active brazing filler alloy (63,0Ag, 35,25Cu, 1,75Ti). Samples produced with different parameters; the process optimization was carried out by investigation the surface roughness effect, microstructural characterization, mechanical and thermal shock tests. For both base metals; ceramic mating surface with an average roughness value of 0.45 µm should be used and when the active brazing process was applied at 830°C for 10 minutes at brazing vacuum value of 10-5 mbar.
Benzer Tezler
- AlN ve Al2O3 katkılı Ti6Al4V alaşımının spark plazma sinterleme yöntemi ile üretimi ve karakterizasyonu
Production and characterization of AlN and Al2O3 reinforced Ti6Al4V alloy via spark plasma sintering method
İLAYDA ÖZBAĞ
Yüksek Lisans
Türkçe
2021
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. FİLİZ ŞAHİN
- Mikro ark oksidasyon işlemi uygulanmış Ti6Al4V alaşımının yapısal ve tribolojik özelliklerinin incelenmesi
Investigation of structural and tribological characteristics of Ti6Al4V alloy applied micro arc oxidation process
EDA YELKENCİ
Yüksek Lisans
Türkçe
2020
Metalurji MühendisliğiKaradeniz Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. BÜLENT ÖZTÜRK
- Titanyumun plazma pasta borlanması
Ti̇tani̇um plasma paste bori̇di̇ng
VOLKAN ATAİBİŞ
Yüksek Lisans
Türkçe
2015
Metalurji MühendisliğiAfyon Kocatepe ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ŞÜKRÜ TAKTAK
- İmplant malzemelerinin mekanik özelliklerinin geliştirilmesi
Improvement of mechanical properties of implant materials
FATMA ZEHRA KÖSE
Yüksek Lisans
Türkçe
2024
BiyomühendislikSakarya ÜniversitesiBiyomedikal Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ MEHMET İSKENDER ÖZSOY
- Wear behaviour analysis of different metals by the finite element method
Farklı metallerin aşınma davranışının sonlu elemanlar yöntemi ile analizi
CANAY DEMİR
Yüksek Lisans
İngilizce
2020
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MURAT BAYDOĞAN