Production and development of photocurable resin used in 3D printing for dental applications
Dental uygulamalar için 3 boyutlu yazıcıda kullanılan fotokürlenebilir reçinenin üretimi ve geliştirilmesi
- Tez No: 789722
- Danışmanlar: DOÇ. DR. SERDAR YILDIRIM
- Tez Türü: Yüksek Lisans
- Konular: Polimer Bilim ve Teknolojisi, Polymer Science and Technology
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2023
- Dil: İngilizce
- Üniversite: Dokuz Eylül Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 103
Özet
Eklemeli imalat yöntemlerinden biri olan fotokimyasal üç boyutlu yazıcılar, UV-ışık ile foto-çapraz bağlanabilir reçineleri polimerize ederek kalıp kullanmadan ince ayrıntılı dental modeller üretir. Bu reçineler monomerler, oligomerler, fotobaşlatıcılar, tercihen nanoparçacıklar ve renk pigmentleri içerir. Titanya ve silika nanopartiküllerinin eklenmesiyle nanokompozit polimerler yüksek dönüşüm derecesine ve mekanik özelliklere sahip olabilir. Ancak nanopartiküllerin topaklanma eğilimi yüksektir. Fakat silanizasyon işlemi ile bu davranış önlenebilmektedir. Bu tez kapsamında, UDMA ve bis-GMA bazlı reçinede takviye malzemesi olarak kullanılan farklı oranlardaki titanya ve silika nanopartiküllerinin mekanik özellikler ve dönüşüm derecesi üzerindeki etkileri araştırılmıştır. 40 nm ile 150 nm arasında partikül boyutuna sahip küresel şekilli nanopartiküller sol-jel yöntemi kullanılarak sentezlenmiş ve silanize edilmiştir. Daha sonra akrilat bazlı hazır reçine ile karıştırılarak optimum partikül miktarı belirlenmiştir. Buna paralel olarak uygun monomer ve oligomer oranı belirlenmiş ve belirlenen miktarda partiküller UDMA ve bis-GMA bazlı reçine içerisine katılarak nanokompozit reçineler elde edilmiştir. Her üretim aşamasının sonunda malzemelere FT-IR, XRD, SEM, çekme, üç noktalı eğme gibi ilgili karakterizasyon yöntemleri uygulanmıştır. U1S ve B1S numuneleri eğme mukavemeti değerlerinde sırasıyla yüzde 38,3 ve 6,4, elastisite modülünde ise sırasıyla yüzde 17,9 ve 8,3 artış göstermiştir. Dönüşüm derecesinde ise sırasıyla yüzde 14,3 ve 12,4 düşüş göstermiştir. Dental uygulamalarda dönüşüm derecesinin yanında eğme mukavemeti ve elastisite modülü de önem taşıdığından, elde edilen sonuçlar hazırlanan nanokompozit reçinelerin dental uygulamalarda kullanılabilmesi için umut vaat etmektedir.
Özet (Çeviri)
Photochemical 3D printers, one of the additive manufacturing methods, polymerize photo-crosslinkable resin with UV-light to fabricate well-detailed dental models without using molds. These resin contain monomers, oligomers, photoinitiators, preferably nanoparticles and color pigments. With the addition of titania nanoparticles, nanocomposite polymers may have high conversion degree and mechanical properties. However, nanoparticles tend to agglomerate. But this behavior can be prevented by the silanization process. In this thesis, the effects of different ratios of titania and silica nanoparticles used as reinforcement materials in UDMA and bis-GMA based resins on the mechanical properties and conversion degree were investigated. Spherical shaped nanoparticles with particle sizes between 40 nm and 150 nm were synthesized and silanized using the sol-gel method. Then, the optimum particle amount was determined by mixing it with the acrylate-based commercial resin. In parallel, the appropriate monomer and oligomer ratio was determined and nanocomposite resins were obtained by adding the determined amount of particles into UDMA and bis-GMA based resin. At the end of each production stage, relevant characterization methods such as FT-IR, XRD, SEM, tensile, three-point bending were applied to the materials. U1S and B1S samples showed an increase of 38.3 percent and 6.4 percent in flexural strength values, 17.9 percent and 8.3 percent in modulus of elasticity, and decrease of 14.3 percent and 12.4 percent in conversion degree, respectively. Besides the conversion degree, flexural strength and modulus of elasticity are also important in dental applications. The results are promising for the use of prepared nanocomposite resins in dental applications.
Benzer Tezler
- Development and characterization of 3d printed frequency selective surface structures in aerospace applications
Havacılık uygulamalarında 3b yazılmış frekans seçici yüzey yapılarının geliştirilmesi ve karakterizasyonu
ÖMER ZİYAEDDİN ALABOYUN
Yüksek Lisans
İngilizce
2022
Elektrik ve Elektronik MühendisliğiAnkara Yıldırım Beyazıt ÜniversitesiHavacılık ve Uzay Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ METE BAKIR
- Development of polymer nanocomposites with improved mechanical and functional properties via stereolithography technique
Stereolitografi tekniği ile geliştirilmiş mekanik ve fonksiyonel özelliklere sahip polimer nanokompozitlerin geliştirilmesi
AYBERK BAYKAL
Yüksek Lisans
İngilizce
2024
Polimer Bilim ve TeknolojisiGebze Teknik ÜniversitesiNanobilim ve Nanomühendislik Ana Bilim Dalı
DOÇ. DR. NURAY KIZILDAĞ
- Çapraz bağlı etoksile akrilat reçinesine enzim immobilizasyonu
Enzyme immobilization on cross-linked ethoxylate achrylate resin
GAREN KARABURUN
Yüksek Lisans
Türkçe
2024
BiyokimyaMarmara ÜniversitesiKimya Ana Bilim Dalı
DR. ÖĞR. ÜYESİ EFE BATURHAN ORMAN
PROF. DR. AYŞE OGAN
- Polimer matrisli sürekli fiber takviyeli kompozit parça üretimi için bir eklemeli imalat yönteminin geliştirilmesi
Development of an additive manufacturing method for manufacturing continuous fiber reinforced polymer matrix composite parts
MUHAMMED ENES GEBEL
Yüksek Lisans
Türkçe
2018
Makine MühendisliğiKahramanmaraş Sütçü İmam ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ MEHMET ERMURAT
- Production and development of light metal containing high entropy alloys by a self-propagating high-temperature synthesis method
Kendiliğinden ilerleyen yüksek sıcaklık sentezi yöntemi ile hafif metal içerikli yüksek entropili alaşımların üretilmesi ve geliştirilmesi
ASLIHAN KARAKANAT
Yüksek Lisans
İngilizce
2022
Metalurji MühendisliğiDokuz Eylül ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. ESRA DOKUMACI ALKAN