Mn, Al ve Zn katkılı MgB2 süperiletkenlerinin manyetik ve mekanik özelliklerinin incelenmesi
The investigation of the magnetic and mechanical properties of Mn, Al and Zn doped MgB2 superconductors
- Tez No: 792235
- Danışmanlar: PROF. DR. KEMAL KOCABAŞ
- Tez Türü: Doktora
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Akı tutma, Kritik akım, Magnezyum borür, Nano parçacık, Üstün iletkenlik, Flux pinning, Critical current, Magnesium boride, Nano particles
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Dokuz Eylül Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada nano boyutta alüminyum, çinko ve mangan katkı elementleri magnezyum borür bileşiğine katkılanarak yapısal, süperiletkenlik ve mekanik özellikleri üzerine etkileri incelendi. Katkı işlemi in-situ ve ex-situ yöntemleri kullanılarak 850 °C de 2 saatlik ısıl işlem sonucunda yapıldı. Alüminyum katkısının magnezyum borür bileşiğinin geçiş sıcaklığını baskıladığı ancak %1 oranındaki katkının kritik akım yoğunluğu değerini yükselttiği bulundu. Aynı zamanda bu katkı oranına ait örneklerin mekanik sertlik değerlerinde de iyileştirme görüldü. Çinko katkısı, magnezyum borürün geçiş sıcaklığı üzerinde bir değişim yaratmadığı ancak kritik akım yoğunluğunun artan çinko katkısıyla geliştirildiği bulundu. Aynı zamanda çinko katkısının malzemenin mekanik sertliğini de sistematik olarak değiştirdiği bulundu. Mangan katkısı ise diğer katkılara oranla yapısal bozulmalara neden olurken manyetik doğası nedeniyle elektron çiftlerinin kırılmasına yol açarak hem geçiş sıcaklığını hem de kritik akım yoğunluğu değerini önemli ölçüde baskıladığı bulundu. Mangan elementinin yarattığı yapısal bozulma mekanik sertlik değerlerinin de azalmasına yol açar. Sentezlenen tüm örneklerin mekanik özelliklerinin incelenmesinde Hays-Kendall modelinin daha uyumlu olduğu bulundu. Katkısız magnezyum borürün nokta tipi çivileme merkezi ile yönetildiği bulundu. Kritik akım yoğunluğunda artış gösteren örneklerin hem nokta hem de üç boyutlu Δκ tipi çivileme merkezinin etkisi altında olduğu bulundu.
Özet (Çeviri)
In this work, nanoscale aluminum, zinc and manganese elements were added to magnesium boride compound and their effects on structural, superconductivity and mechanical properties were investigated. The additive process was carried out after 2 hours of heat treatment at 850 °C using in-situ and ex-situ methods. It was found that the aluminum additive suppressed the transition temperature of the magnesium diboride, but the 1% additive increased the critical current density. At the same time, the mechanical hardness values of the samples belonging to this additive ratio were also improved. It was found that the zinc additive did not cause a change on the transition temperature of magnesium diboride, but the critical current density was improved with increasing zinc doping. It was also found that the zinc additive systematically changed the mechanical hardness of the material. It was found that while manganese additive causes structural deterioration compared to other additives, it significantly suppresses both the transition temperature and the critical current density value by causing electron pair breaking effect due to its magnetic nature. The structural deterioration caused by the manganese element also leads to a decrease in mechanical hardness values. The Hays-Kendall model was found to be more suitable model for the samples. It was found that pure magnesium diboride was managed with a point-type pinning center. It was found that the samples showing increased critical current density were under the influence of both point and three-dimensional Δκ-type pinning centers.
Benzer Tezler
- Sol-jel tekniği ile hazırlanan katkılı (Li,Mn,Cu,Al) ZnO ince filmlerin mikroyapısal ve optik özelliklerinin incelenmesi
İnvestigation of micro structural and optical properties of doped (Li,Mn,Cu,Al) ZnO thin films by sol-gel technique
ZEHRA BANU BAHŞİ
Yüksek Lisans
Türkçe
2004
Metalurji MühendisliğiGebze Yüksek Teknoloji EnstitüsüMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. HASAN ASLAN
- Bazı spineller ve YBiPt kristallerinde paramanyetik rezonans incelemeleri
Paramagnetic resonance studies on some spinels and YBiPt crystals
SADIK GÜNER
Doktora
Türkçe
2003
Fizik ve Fizik MühendisliğiGebze Yüksek Teknoloji EnstitüsüFizik Ana Bilim Dalı
PROF. DR. BEKİR AKTAŞ
- Kangal termik santrali uçucu küllerinin analitik ve çevresel olarak incelenmesi ve değerlendirilmesi
Investigation and utilization of fly ash from Kangal power plant in terms of analytical and environmental points of view
ÜMİT ŞENGÜL
- Taban malzeme ile emaye kaplama arasındaki difüzyon mekanizmasının araştırılması ve düşük metal migrasyonuna sahip emaye geliştirilmesi
Investigation of diffusion mechanisms at substrate enamel interface and development of new enamel surface with low metal migration
ÖZGE IŞIKSAÇAN
Doktora
Türkçe
2020
Besin Hijyeni ve Teknolojisiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ONURALP YÜCEL
- Farklı tahıl unlarından geliştirilen ekstrüde ürünlerin teknolojik ve bazı besinsel özelliklerinin belirlenmesi
Determination of technological and some nutritional characteristics of extruded products formulated from various cereal flours
ARZU ÖZER
Doktora
Türkçe
2025
Gıda MühendisliğiAnkara ÜniversitesiGıda Mühendisliği Ana Bilim Dalı
PROF. DR. BERRİN ÖZKAYA