Yüksek manyetik özellikli demir nanoparçacıklarının nanoküre litografisi kullanarak üretilmesi
Fabrication of highly magnetic iron nanoparticles using nanosphere lithography
- Tez No: 810051
- Danışmanlar: DR. ÖĞR. ÜYESİ YAVUZ NURİ ERTAŞ
- Tez Türü: Yüksek Lisans
- Konular: Bilim ve Teknoloji, Science and Technology
- Anahtar Kelimeler: Demir oksit, Nanoküre litografisi, MRG, Kontrast ajan, Iron oxide, Nanosphere lithography, MRI, Contrast agent
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Erciyes Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Nanobilim ve Nanoteknoloji Ana Bilim Dalı
- Bilim Dalı: Nanoteknoloji Bilim Dalı
- Sayfa Sayısı: 78
Özet
Manyetik rezonans görüntüleme (MRG), iyonize radyasyon içermeyen ve klinik olarak nispeten kolay erişilebilir bir yöntemdir. Sağlıklı ve hasta dokular arasındaki kontrast farkının geliştirilmesiyle hastalıklı dokulara teşhis konulması daha doğru olmaktadır. Bu sebeple bu kontrast farkını arttıracak kontrast malzemelerine olan ihtiyaç gün geçtikçe artmaktadır. MRG' de elde edilen görüntüler T1-T2 veya proton ağırlıklı olarak karşımıza çıkmaktadır. T2 ağırlıklı görüntülerin elde edilebilmesi için sıklıkla demir bazlı kontrast ajanları araştırılmaktadır. Klinikte kullanılan demir bazlı kontrast ajanlarının yetersiz kısımlarını teşhis edip çözmeye yönelik uygulamalar eşliğinde bu tez çalışmasında biyouyumlu, ıslak-kimyasal üretim süreçlerinden arındırılmış, sentezi ve tekrarlanabilirliği yüksek silisyum dioksit kaplı demir oksit nanopartiküllerinin (Fe@SiO2) nanoküre litografisi kullanılarak üretilmesi önerilmiştir. Üretilen nanopartiküllerin karakterizasyonu ve manyetik davranışları incelenmiştir. T2 kontrast ajanı olarak kullanılabilirliğinin kanıtlanması için gevşeme çalışmaları yapılmıştır. Sonuç olarak üretilen Fe@SiO2 nanopartiküllerinin 5K sıcaklık değerinde 82 emu/g satürasyon manyetizasyonu sergilediği gösterilmiştir. Gevşeme çalışmaları sonucunda artan Fe@SiO2 konsantrasyonlarında elde edilen negatif kontrastın arttığı ve r2= 30 mM-1s-1 olarak bulunmuştur. Bu sonuçlar, üretilen nanopartiküllerin geliştirilebilir bir kontrast ajanı adayı olduğunu göstermektedir.
Özet (Çeviri)
Magnetic resonance imaging (MRI) is a non-ionizing radiation imaging technique that can be used in healthcare situations with relative ease. By increasing the contrast difference between healthy and sick tissues, it is possible to diagnose diseased tissues with greater accuracy. As a result, the demand for contrast materials that will increase this contrast difference is growing by the day. T1-T2 or proton-weighted images are produced by MRI. T2-weighted images are frequently obtained using iron-based contrast agents. In this thesis, it is proposed to use nanosphere lithography to produce biocompatible, free-of-wet-chemical production processes, high synthesis, and reproducibility silicon dioxide-coated iron oxide nanoparticles (Fe@SiO2), along with applications for diagnosing and solving insufficient parts of iron-based contrast agents used in the clinic. The magnetic behavior and characterization of the produced nanoparticles were investigated. Its suitability as a T2 contrast agent has been demonstrated through relaxation studies. As a result, the produced Fe@SiO2 nanoparticles have a saturation magnetization of 82 emu/g at 5K temperature. Relaxation studies revealed that the contrast increased with increasing Fe@SiO2 concentrations, with r2= 30 mM-1s-1. These results suggest that the nanoparticles produced are a viable candidate for developable contrast agents.
Benzer Tezler
- Demir oksit nanoparçacıklarının ağır metal adsorpsiyonunda kullanımı
Using of iron oxide nanoparticles on adsorption of heavy metals
İLKYAZ ÇETİN ERCAN
- The modification of divergent magnetite nanoparticles with cyclodextrin and applications in magnetic hyperthermia
Farklı magnetit nanoparçacıkların siklodekstrin ile modifikasyonu ve manyetik hipertermi uygulamaları
MİRAY ŞENKAL
Yüksek Lisans
İngilizce
2025
Kimya MühendisliğiYeditepe ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ CEM LEVENT ALTAN
- Tümör hedefli mangan-demir oksit manyetik nanoparçacık hibrit görüntüleme ajanının potansiyelinin değerlendirilmesi
Evaluation of the potential of tumor-targeted manganese-iron oxidemagnetic nanoparticle hybrid imaging agent
DERYA ÖZEL
- Development of polymer coated nanoparticles and polymer bridged magnetic luminescent hybrids
Polimer kaplı nanoparçacıkların ve polimer köprülü manyetik lüminesan hibritlerin geliştirilmesi
HANDE ÖZTÜRK
Yüksek Lisans
İngilizce
2010
Polimer Bilim ve TeknolojisiKoç ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
DOÇ. DR. H. FUNDA YAĞCI ACAR
- Mühendislik nanoparçacıklarının canlı sistemler ve/veya çevre ile etkileşim türlerinin ve mekanizmalarının sistematik olarak incelenmesi
Systematic investigations of the mechanisms and effects of engineered nanomaterial interactions with living systems and/or the environment
FATMA GÖZDE YÜCE
Yüksek Lisans
Türkçe
2020
Mühendislik BilimleriTOBB Ekonomi ve Teknoloji ÜniversitesiMikro ve Nanoteknoloji Ana Bilim Dalı
DOÇ. DR. HATİCE DURAN DURMUŞ