Sodyum bazlı 3 boyutlu doku iskelelerinin üretimi, karakterizasyonu, antibakteriyel ve antibiyofilm etkilerinin araştırılması
Synthesis and characterization of sodium-based 3d scaffolds, and i̇nvestigation of their antibacterial and antibiofilm effects
- Tez No: 815813
- Danışmanlar: PROF. DR. GÜLGÜN TINAZ
- Tez Türü: Yüksek Lisans
- Konular: Biyomühendislik, Mikrobiyoloji, Bioengineering, Microbiology
- Anahtar Kelimeler: Pseudomonas aeruginosa, biyofilm, çevreyi algılama sistemi, bakteriyel iletişim, virülans faktörleri
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Marmara Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Eczacılık Temel Bilimleri Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 76
Özet
Amaç: Bu çalışma 3 boyutlu doku iskelesi yapısına, feniletil alkol (PEA) ve sinnamaldehit (CA) gibi bakteriyel iletişim inhibitörlerinin sodyum bazlı polimerler ile kombine edilerek üretilmesi ve üretilen doku iskelelerinin 4 farklı bakteri suşu üzerinde antibakteriyel ve biyofilm potansiyellerinin değerlendirilmesi amacıyla yapılmıştır. Gereç ve Yöntem 3 boyutlu biyoyazıcı ile SA, SA/PEG, SA/PEG/PEA,ve SA/PEG/CA yüklü doku iskeleleri başarıyla üretilmiştir. Üretilen iskelelerin yüzey morfolojisi ve porozitesi SEM cihazı; kimyasal ve moleküler etkileşimleri FTIR cihazı, mekanik özellikleri çekme test cihazı, termal davranışı DSC cihazı kullanılarak analiz edilmiştir. Ayrıca in vitro PEA salımı analizi UV-VIS spektrofotometresi kullanılarak inelenmiştir. Çalışmada P. aeruginosa (PA01), E. coli ATCC 25922, S. aureus ATCC 25923, ve E. faecalis ATCC 29212 suşları kullanılmıştır. Kullanılan bakteri suşları için disk difüzyon testi ve kristal boyama metodu ile biyofilm tayini yapılmıştır. Bulgular : Antimikrobiyal test sonuçları doku iskelelerinde bulunan CA ve PEA inhibitör miktarlarının öldürücü dozda olmadığı görüldü. Fakat 3000 µl PEA yüklü doku iskelesinin PA01 suşu üzerinde %71'lik biyofilm inhibisyonu gerçekleştirirken, elektrosprey ile 450 µl CA nanopartikül ile kaplanmış doku iskelesi PA01 suşu üzerinde %64 biyofilm inhibisyonu gerçekleştirdiği görülmüştür. Sonuç : Doku iskelelerinin morfolojik, termal, kimyasal ve antimikrobiyal testler sonucunda SA/PEG/3000PEA yüklü doku iskelelerinin yapısının yara örtüsü kullanımı için ideal şartlarda olduğu yapılan analizler sonucunda görülmüştür.
Özet (Çeviri)
Aim : This study aims to produce a 3D tissue scaffold structure by combining bacterial communication inhibitors such as phenylethyl alcohol (PEA) and cinnamaldehyde (CA) with sodium-based polymers, and to evaluate the antibacterial and biofilm potentials of the produced tissue scaffolds on four different bacterial strains. Material and Methods : 3D tissue scaffolds loaded with SA, SA/PEG, SA/PEG/PEA, and SA/PEG/CA were successfully produced using a 3D bioprinter. The surface morphology and porosity of the produced scaffolds were analyzed using scanning electron microscopy (SEM); their chemical and molecular interactions were analyzed using Fourier-transform infrared spectroscopy (FTIR), their mechanical properties were analyzed using a tensile testing machine, and their thermal behavior was analyzed using differential scanning calorimetry (DSC). In vitro PEA release analysis was also examined using a UV-VIS spectrophotometer. P. aeruginosa (PA01), E. coli ATCC 25922, S. aureus ATCC 25923, and E. faecalis ATCC 29212 strains were used in this study. Disk diffusion tests and crystal violet staining were used to determine biofilm formation for the bacterial strains used. Results: Antimicrobial test results showed that the amounts of CA and PEA inhibitor in tissue scaffolds were not lethal. However, a tissue scaffold loaded with 3000 µl PEA achieved 71% biofilm inhibition on the PA01 strain, while a tissue scaffold coated with 450 µl CA nanoparticles via electrospray achieved 64% biofilm inhibition on the PA01 strain. Conclusion : As a result of morphological, chemical, and antimicrobial tests of the tissue scaffolds, it was seen that SA/PEG/3000PEA loaded tissue scaffolds had ideal structures for wound coverage use. Keywords : Biofilm, phenylethyl alcohol, cinnamaldehyde, sodium alginate, quorum sensing.
Benzer Tezler
- Osteosarkoma tedavisinde kullanılmak üzere kemik doku oluşumunu destekleyici ilaç yüklü üç boyutlu doku iskelelerinin geliştirilmesi
Development of drug loaded 3-dimensional bone tissue scaffolds for treatment of osteosarcoma and regeneration of defected bone tissue
ELİF SARIGÖL ÇALAMAK
Doktora
Türkçe
2022
Eczacılık ve FarmakolojiAnkara ÜniversitesiFarmasötik Teknoloji Ana Bilim Dalı
PROF. DR. CANAN HASÇİÇEK
- Üstün mekanik özelliklere sahip ipek fibroin iskeletlerinin yüksek fibroin konsantrasyonlarında üretimi
Production of silk fibroin scaffolds with remarkable mechanical properties at high fibroin concentrations
CANER AKINCI
- Yara örtüsü uygulamaları için nanopartikül ve antibiyotik yüklüdoku iskelelerinin 3D basımı
3D printing of nanoparticle and antibiotic-loaded scaffolds forwound dressing applications
SEMA TUĞÇE AYDIN
Yüksek Lisans
Türkçe
2021
BiyoteknolojiYıldız Teknik ÜniversitesiMoleküler Biyoloji ve Genetik Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ESRA YÜCA
DOÇ. DR. OĞUZHAN GÜNDÜZ
- 3-D printed recombinant collagen type 2 and calcium phosphate cement cartilage tissue scaffolds for joint cartilage defects
Eklem kikirdak defektleri için 3-boyutlu baskilanan rekombinant kolajen ve kalsiyum fosfat çimentosu kikirdak doku iskeleleri
HÜMEYRA HANDE YAVUZ
Yüksek Lisans
İngilizce
2023
BiyolojiAnkara ÜniversitesiBiyomedikal Mühendisliği Ana Bilim Dalı
DOÇ. DR. AÇELYA YILMAZER AKTUNA
- Sentez sıcaklığı ve çapraz bağlayıcı konsantrasyonunun ipek fibroin kriyojelerinin özelliklerine etkisi
Effects of preparation temperature and cross-linker concentration on the properties of silk fibroin cryogels
ZEYNEP ÖZTOPRAK