Determination of mechanical and microstructural properties of engineered cementitious composite incorporating different types of SCM, filler, and PVA fiber
Farklı türlerde SCM, dolgu ve PVA elyaf içeren tasarlanmış çimento kompozitlerin mekanik ve mikroyapı özelliklerinin belirlenmesi
- Tez No: 821551
- Danışmanlar: PROF. DR. LUTFULLAH TURANLI, PROF. DR. AFŞİN SARITAŞ
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2022
- Dil: İngilizce
- Üniversite: Ankara Yıldırım Beyazıt Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: İnşaat Mühendisliği Bilim Dalı
- Sayfa Sayısı: 89
Özet
Tasarlanmış çimento kompoziti (ECC), gerinim pekleşmesi sergileme ve çoklu mikro çatlak oluşumları yoluyla yüksek eğilme kapasitesi elde etme konusundaki benzersiz yeteneğinden dolayı belirli bir elyaf takviyeli çimentolu kompozit sınıfıdır. Bu deneysel inceleme programında doğal zeolit tozu (NZP) ve doğal perlit tozu (NPP) ek çimento esaslı malzeme (SCM) olarak kullanılmış olup, yağlı ve yağsız olmak üzere iki tip polivinil alkol (PVA) lifi %2 hacimsel oranda kullanılmıştır. ECC üretiminin silis kumuna olan bağımlılığını azaltmak için, silika kumunun kısmi ilavesi olarak doğal perlit kumu (NPS) 0, 25, 50, 75 ve %100 oranlarında kullanılmıştır. 7 ve 28. günlerde ECC numunelerin mekanik ve mikroyapısal özellikleri incelenmiştir. Genel olarak, NZP içeren ECC, daha iyi yük-deplasman performansı ve eğilme mukavemeti elde etmiş, ayrıca NPP içeren ECC'den daha yüksek bir deplasman kapasitesi sergilemiştir. Ancak basınç dayanımı sonuçlarında bunun tersi gözlenmiştir. Özellikle, yağlanmış PVA lifi içeren ECC numuneleri, yağlanmamış PVA lifi içeren ECC numunelerinden daha yüksek deplasman kapasitesi sağlarken, yağlanmış PVA lifinin kullanılması nedeniyle basınç ve eğilme dayanımları kısmen azalmıştır. Ayrıca silikanın kısmen perlit kumu ile yer değiştirmesi de sehim kapasitesini olumsuz etkilemiştir. Ayrıca, taramalı elektron mikroskobu (SEM) görüntülerinden, yüksek miktarda NPS'nin PVA elyafının erken kopmasına neden olduğunu ortaya konmuştur. NZP, yağlanmamış PVA elyafı ve çimentolu kompozitin moleküler bağlanma mukavemetini azaltmada en etkilidir. Bu nedenle, çekilen lifler, bir SCM olarak NZP içeren ECC'de kopmuş uç PVA lifinden daha fazlaydı. ECC'nin mikroyapısal özelliklerini ve NPP, NZP gibi SCM'ler içiren karışımların puzolanik reaktivitesini değerlendirmek için X-ışını kırınım testi de yapılmıştır.
Özet (Çeviri)
Engineered cementitious composite (ECC) is a particular class of fiber-reinforced cementitious composite due to its unique ability to perform stain-hardening and attain high deflection capacity through multiple microcrack formations. In this experimental examination program, natural zeolite powder (NZP) and natural perlite powder (NPP) were used as supplementary cementitious materials (SCMs) in addition to two types of polyvinyl alcohol (PVA) fiber, oiled PVA and non-oiled PVA fibers with 2 percent of volume fraction. In order to reduce the reliance of ECC production on silica sand, natural perlite sand (NPS) was used as a partial replacement for silica sand at (0, 25, 50, 75, and 100 percent). The ECC specimens' mechanical properties and microstructural characteristics were examined at 7- and 28-days' age. In general, ECC containing NZP obtained better load-deflection performance and flexural strength and revealed a higher deflection capacity than ECC containing NPP. However, the opposite was observed in the compressive strength results. In particular, ECC specimens with oiled PVA fiber resulted in higher deflection capacity than ECC specimens containing non-oiled PVA fiber, while compressive and flexural strengths slightly dropped due to the use of oiled PVA fiber. Furthermore, the partial replacement of silica with perlite sand adversely affected the deflection capacity. Moreover, it can be noted from the scanning electron microscope (SEM) images that the high amount of NPS resulted in a premature failure of the PVA fiber. The NZP was most effective in reducing the molecular bonding strength of non-oiled PVA fiber and cementitious composite. Thus, pulled-out fibers were more than the ruptured end PVA fiber in ECC containing NZP as an SCM. An X-ray diffraction test was also conducted to assess ECC's microstructural properties and pozzolanic reactivity containing SCMs like NPP and NZP.
Benzer Tezler
- T4 ve T6 ısıl işlemli 6061 alüminyum levhanın iki eksenli gerilmeler altında şekil değiştirmesinin incelenmesi
Investigation of deformation of T4 & T6 heat treated 6061 aluminum plate under biaxial stress
EGEMEN UZ
Yüksek Lisans
Türkçe
2022
Makine Mühendisliğiİstanbul Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. ŞAFAK YILMAZ
- Otomotiv sektöründe dinamik yüklere maruz bir kaynaklı bağlantı için yorulma dayanımı değerlendirmesi
A fatigue damage assessment of welded joints under dynamic loading in automotive industry
SERKAN ORHAN
Yüksek Lisans
Türkçe
2017
Makine Mühendisliğiİstanbul Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. ATAKAN ALTINKAYNAK
- Ara katmanlı sürtünme karıştırma nokta kaynağı
Interlayer friction stir spot welding
ECEM ORUÇ
Yüksek Lisans
Türkçe
2020
Metalurji MühendisliğiMarmara ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. YAHYA BOZKURT
- Kürün betonun kuruma etkisinde büzülme davranışına etkisi
The effect of curing on the shrinkage behavior of concrete
UBEYDULLAH AYVAZ
Yüksek Lisans
Türkçe
2024
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ÜNAL ANIL DOĞAN
- Determination of microstructural properties of PM Al-SiC composites by ultrasonic techniques
TM Al-SiC kompozitlerin mikroyapı özelliklerinin ultrasonik tekniklerle belirlenmesi
ESRA ATAŞ
Yüksek Lisans
İngilizce
2000
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. C. HAKAN GÜR
DOÇ. DR. BİLGEHAN ÖGEL