Yeşil prosesle üretilmiş gözenekli hidroksiapatit esaslı hibrit kompozitlerin indüksiyonla sinterlenmesi ve karakterizasyonu

Induction sintering and characterization of porous hydroxyapatite based hybrid composites made with the green process

  1. Tez No: 826453
  2. Yazar: ESRA NUR USTA
  3. Danışmanlar: DOÇ. DR. NERMİN DEMİRKOL, DOÇ. DR. MEVLÜT GÜRBÜZ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Biyomühendislik, Bioengineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2023
  8. Dil: Türkçe
  9. Üniversite: Kocaeli Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Biyomedikal Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Biyomedikal Mühendisliği Bilim Dalı
  13. Sayfa Sayısı: 113

Özet

Vücudumuzda yaralanmalar sonucunda hasar gören dokuların onarılması ve yeniden yapılandırılması için kullanılan biyomalzemelerin vücut ile uyum sağlaması herhangi bir toksik etki oluşturmaması çok önemlidir. Bu çalışmada kemik atıklarının değerlendirilmesi amacıyla koyun femur kemiğinden gözenekli yapıda koyun hidroksiapatit (KHA), ülkemizde biyomalzeme üretiminde kullanımı yaygınlaşmaya başlayan indüksiyonla sinterleme yöntemi ile üretildi. Yapılan çalışmada; termal yöntem ile koyun femur kemiğini temizleme, yakma, karbon uzaklaştırma ve öğütme işlemlerinden sonra elde edilen hidroksiapatit toz eldesine biyouyumluluğu bozmayacak şekilde ağ. %1, 5 ve 10 oranlarında MgO takviye edilip bilyalı değirmende karıştırıldı. Bağlayıcı malzeme olarak %2,5 oranında PVA kullanıldı. Tozlar 1200oC 'de 5 dk sürelerde 2 kez indüksiyon fırında sinterlemeye maruz bırakıldı. Elde edilen gözenekli yapıdaki kompozitlerin fiziksel ve mekanik ölçümleri yapıldı ve en yüksek yoğunluğa sahip ağ %1 MgO içeren kompozite ağ. %0,1, 0,5 ve 1 oranlarında grafen takviye edildi. Hazırlanan kompozitler kemik-doku benzerliği için test ve analizlere tabi tutuldu. Yoğunluk, porozite miktarı ve basma mukavemeti testi yapıldı. Taramalı elektron mikroskobuyla (SEM) tane morfolojisi , X- ışını kırınımı (XRD) ile oluşan fazlar incelendi. Elde edilen gözenekli (KHA) koyun hidroksiapatitin süngerimsi kemiği karşılar nitelikte mekanik özelliklere sahip olduğu tespit edildi. En iyi yoğunluk ve basma mukavemeti değerlerine sahip olan KHM1 ile KHM1GRF0.1 numunelerin yoğunluk ve basma mukavemeti değerleri sırasıyla 2.771 g/cm3 - 28.42 MPa ve 2.636 g/cm3 – 26.25 MPa olarak elde edildi. Yapay vücut sıvısı içerisinde 2,3 ve 4 hafta bekletilme süresince statik in vitro biyoaktivite testine tabi tutulan kompozitlerin biyoaktif özellikte oldukları incelemelerde görülen hidroksi karbona apatit tabakası ile tespit edildi.

Özet (Çeviri)

It is very important that the biomaterials used for the repair and restructuring of the tissues damaged as a result of injuries in our body are compatible with the body and do not cause any toxic effects. In this study, porous sheep hydroxyapatite (CHA) from sheep femur bone was produced by induction sintering method, which has become widespread in biomaterial production in our country, in order to evaluate bone wastes. In the study; A mesh that does not impair biocompatibility to the hydroxyapatite powder obtained after cleaning, burning, carbon removal and grinding processes of sheep femur bone by thermal method. 1, 5 and 10% MgO was supplemented and mixed in a ball mill. 2.5% PVA was used as the binding material. The powders were sintered twice in an induction furnace at 1200oC for 5 minutes. The physical and mechanical measurements of the obtained porous composites were made and the mesh with the highest density was calculated on the composite containing 1% MgO. Graphene was supplemented at 0.1%, 0.5%, and 1% ratios. Prepared composites were subjected to tests and analyzes for bone-tissue similarity. Density, porosity amount and compressive strength tests were performed. Grain morphology was investigated by scanning electron microscopy (SEM) and phases formed by X-ray diffraction (XRD). It was determined that the obtained porous (CHA) sheep hydroxyapatite had mechanical properties that match the spongy bone. The density and compression strength values of KHM1 and KHM1GRF0.1 samples, which had the best density and compression strength values, were obtained as 2.771 g/cm3 - 28.42 MPa and 2.636 g/cm3 - 26.25 MPa, respectively. It was determined that the composites, which were subjected to static in vitro bioactivity test during 2, 3 and 4 weeks of storage in artificial body fluid, were bioactive with the dense hydroxy carbon apatite layer formed.

Benzer Tezler

  1. Katodik hidrojen peroksit üretim veriminin ve sulardan kirletici giderme performansının değerlendirilmesi

    Evaluation of cathodic hydrogen peroxide production efficiency and pollutant removal performance from water

    TUĞBA KAKTİMUR

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Çevre MühendisliğiBursa Teknik Üniversitesi

    Çevre Mühendisliği Ana Bilim Dalı

    PROF. DR. ORHAN TANER CAN

  2. Yarı iletken diyot lazerin çevresel uygulamaları

    Environmental applications of semiconductor diode laser

    BARIŞ POLAT

    Doktora

    Türkçe

    Türkçe

    2021

    Fizik ve Fizik MühendisliğiMersin Üniversitesi

    Nanoteknoloji ve İleri Malzemeler Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ İBRAHİM KÜÇÜKKARA

    PROF. DR. NADİR DİZGE

  3. Akrilik mikroliflerin uzun lif eğirme sisteminde işlenebilirliğinin geliştirilmesi

    Improvement of processing acrylic microfibres in long-staple spinning system

    YEŞİM İRİDAĞ

    Doktora

    Türkçe

    Türkçe

    2000

    Tekstil ve Tekstil Mühendisliğiİstanbul Teknik Üniversitesi

    PROF. DR. BÜLENT ÖZİPEK

  4. Yeşil sentez metodu ile hazırlanan Ag2S temelli nanokompozitlerin fotokatalitik hidrojen üretiminde kullanılması

    The use of Ag2S based nanocomposites prepared by green synthesis method in photocatalytic hydrogen production

    AYDIN BARIŞ ŞİMŞİR

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    EnerjiSakarya Üniversitesi

    Kimya Ana Bilim Dalı

    DOÇ. DR. KEZİBAN ATACAN

  5. Towards heterogeneous biocatalysis of glutathione production by selective conjugation of enzymes

    Glutatyon enzimlerinin seçici konjugasyonu ile heterojen biyokatalize dair çalışmalar

    YAĞMUR ERSOY

    Yüksek Lisans

    İngilizce

    İngilizce

    2021

    BiyokimyaKoç Üniversitesi

    Kimya ve Biyoloji Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ CEM ALBAYRAK