Manyezit cevheri kullanılarak hazırlanan manyezit-al katmanlı çift hidroksit kompozitin sulu çözeltiden azo boyar madde gideriminde kullanılabilirliğinin araştırılması
The investigation of the usability of magnesite-al layered double hydroxide composite prepared using magnesite ore in azo dye removal from aqueous solution
- Tez No: 827682
- Danışmanlar: PROF. DR. İLKER KIPÇAK
- Tez Türü: Yüksek Lisans
- Konular: Kimya Mühendisliği, Chemical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Eskişehir Osmangazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Temel İşlemler ve Termodinamik Bilim Dalı
- Sayfa Sayısı: 113
Özet
Yapılan çalışmada, manyezit cevheri ve alüminyum nitrat kullanılarak katmanlı çift hidroksit adsorbanı (Manyezit-Al KÇH) sentezlenmiş, karakterize edilmiş ve adsorpsiyon yöntemiyle sulu çözeltiden Reactive Black 5 (RB5) azo boyar maddesinin gideriminde kullanılabilirliği araştırılmıştır. Manyezit ve Manyezit-Al KÇH kompozitinin karakterizasyonları XRF, XRD, FTIR ve SEM/EDS analizleri ile gerçekleştirilmiştir. Adsorpsiyon yoluyla RB5 giderimine, adsorban miktarının, pH değerinin, temas süresinin, başlangıç derişiminin ve sıcaklığın etkileri araştırılmıştır. Adsorban miktarı 0,02 g, pH 6, temas süresi 1440 dk, başlangıç derişimi 100 mg/L ve 25°C uygun deney koşulları olarak belirlenmiştir. Ayrıca adsorpsiyon kinetiği, izotermi ve termodinamiği aydınlatılmıştır. Adsorban miktarı arttıkça giderim verimi artmıştır. pH arttıkça giderim veriminde artış gözlenmiştir. Adsorpsiyon işlemi 24 saatte dengeye ulaşmıştır. Ayrıca adsorpsiyon kinetiği araştırılmış yalancı ikinci derece kinetik modele uyum sağladığı tespit edilmiştir. Başlangıç derişimi ve sıcaklığın etkisi birlikte incelenmiş olup, boyar madde derişimi arttıkça giderim verimi azalmıştır. Adsorpsiyon süreci Langmuir ve Freundlich izotermleri ile değerlendirilmiş Langmuir izotermi ile daha uyumlu olduğu tespit edilmiştir. 25°C'deki maksimum adsorpsiyon kapasitesi ise 196,08 mg/g olarak saptanmıştır. Adsorpsiyon termodinamik verilerine göre, 25°C sıcaklıkta ΔG°, ΔH°, ΔS° değerleri sırasıyla -30,25 kJ/mol, -20,57 kJ/mol, 32,54 J/mol K olarak hesaplanmıştır ve bu veriler neticesinde adsorpsiyonun kendiliğinden gerçekleştiği, ekzotermik olduğu ve düzensizliğe eğilimde artış gösterdiği değerlendirilmiştir.
Özet (Çeviri)
In this study, a layered double hydroxide adsorbent (Magnesite-Al KÇH) from was synthesized using magnesite ore and aluminium nitrate, characterized and used for the removal of Reactive Black 5 (RB5) azo dye from aqueous solution by adsorption method. Characterization of magnesite and Magnesite-Al KÇH composite was carried out by XRF, XRD, FTIR and SEM/EDS analyzes. The effects of adsorbent amount, pH value, contact time, initial concentration and temperature on RB5 removal by adsorption were investigated. The amount of adsorbent 0,02 g, pH 6, contact time 1440 min, initial concentration 100 mg/L and 25°C were determined as suitable experimental conditions. In addition, adsorption kinetics, isotherm and thermodynamics were clarified. The removal efficiency increased with increasing adsorbent amount. The removal efficiency increased as the pH increased. The adsorption process reached equilibrium in 24 hours. In addition, the adsorption kinetics were investigated and it was found that it conformed to the pseudo-second order kinetic model. The effect of initial concentration and temperature were also examined, and as the azo dye concentration increased, the removal efficiency decreased. Adsorption process was evaluated with the Langmuir and Freundlich isotherms and it was found to be more compatible with the Langmuir isotherm. The maximum adsorption capacity at 25°C was found to be 196,08 mg/g. According to adsorption thermodynamic data, ΔG°, ΔH°, ΔS° values at 25°C were calculated as -30,25 kJ/mol, -20,57 kJ/mol, 32,54 J/molK, respectively. It was evaluated that the adsorption occurred spontaneously, was exothermic and showed an increased tendency to disorder.
Benzer Tezler
- Manyetit cevheri konsantresinin karbotermik redüksiyonuna karbonize çay tesis atıklarının etkisi
The effect of carbonised tea waste plants on the carbothermic reduction of magnetite ore concentrate
BAYRAM BOSTANCI
Yüksek Lisans
Türkçe
2018
Metalurji MühendisliğiFırat ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
YRD. DOÇ. MUSTAFA BOYRAZLI
- Gedebey (Batı-Azerbaycan) altın-bakır yatağının jeolojik, mineralojik, petrografik ve jeokimyasal özelliklerinin incelenmesi
Investigation of the geological, mineralogical, petrographical and geochemical properties of the gadabay (West Azerbaijan) gold- copper deposit
COŞQUN ISMAYIL
Yüksek Lisans
Türkçe
2019
Jeoloji MühendisliğiSelçuk ÜniversitesiJeoloji Mühendisliği Ana Bilim Dalı
PROF. DR. FETULLAH ARIK
- Development of a new centrifugal separator
Yeni bir santrifüj ayırıcı geliştirilmesi
MOHAMMED SAMI ALI AL-SULTAN
Yüksek Lisans
İngilizce
2021
Maden Mühendisliği ve Madencilikİstanbul Teknik ÜniversitesiCevher Hazırlama Mühendisliği Ana Bilim Dalı
PROF. DR. AYHAN ALİ SİRKECİ
- Türkiye manyezit yataklarından çeşitli magnezyum bileşiklerinin hazırlanması
The Preparation of some magnesium compounds from natural magnesite beds in Türkiye
A.HAKAN AKTAŞ
- Bir ilaç taşıyıcı sistemi olarak montmorillonit/manyetit nano-kompozit sentezi ve karakterizasyonu
Synthesis and characterization of montmorillonite/mannetite nano-composite as a drug carrier system
HAKAN ÇİFTÇİ
Doktora
Türkçe
2019
Eczacılık ve FarmakolojiAfyon Kocatepe ÜniversitesiMaden Mühendisliği Ana Bilim Dalı
PROF. DR. BAHRİ ERSOY