Çelik yüzeylerin emaye kaplanması yüzey hazırlama solüsyonuna farklı oranlarda ilave edilen dipotasyumheksaflorotitanatın etkisi

Effect of dipotassium hexafluorotitanate added to the surface preparation solution in different proportions for enamelling of steel surfaces

  1. Tez No: 829627
  2. Yazar: EROL SALAR
  3. Danışmanlar: PROF. DR. MEHMET TARAKÇI
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2023
  8. Dil: Türkçe
  9. Üniversite: Gebze Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 134

Özet

Bu çalışmada, evsel fırın üretiminde kullanılan çelik sac üzerine yapılan emaye kaplamadaki yüzey kabarcık kusurunun (sineklenme) giderilmesi için son durulama banyosuna farklı oranlarda dipotasyumheksaflorotitanat (K2TiF6) ilavesinin etkisi araştırılmıştır. Emaye kaplama sonrasında, yüzey kabarcık kusuru görülen ve görülmeyen iki farklı çelik sac tedarikçisinin malzemeleri kullanılmıştır. Öncelikle, bu altlık çelik sacların karakterizasyonu spektrometre, optik mikroskop, SEM, SEM-EDS, profilometre, XRD ile yapılmıştır. Son durulama banyosu iki şekilde hazırlanmıştır. Birinci banyoya sadece K2TiF6 ilavesi yapılmış, ikinci banyoya içeriğinde K2TiF6 da bulunan ticari bir karışım ilavesi yapılmıştır. Bu durulama banyoları sonrası, çelik saclar açık atmosferde 820 oC'de 80-125 µm kalınlığında emaye kaplanmıştır. Emaye kaplamaların karakterizasyonu altlık saclara uygulanan test ve analiz cihazları ile benzer şekilde gerçekleştirilmiştir. Çelik sacların kimyasal bileşimlerinde küçük farklılıklar olduğu ancak benzer fazları ve karbonca zengin inklüzyonlar içerdikleri görülmüştür. Her iki çeliğin tane boyutunda ve yüzey pürüzlülük değerlerinde dikkate değer farklılık olduğu görülmüştür. Saclar emaye kaplandıktan sonra, yüzey kabarcık kusuru görülen emayelerde yüzey pürüzlülük değerinin bir miktar yüksek olduğu tespit edilmiştir. Emaye kaplamaların genelinde, benzer kristal yapılarla birlikte bir miktar amorf fazların bulunduğu belirlenmiştir. Emaye kaplamaların yüzeyinde mikroskobik boyutta gözenekliliğin tüm numunelerde bulunduğu ancak bazı kaplamalarda gözle görülür boyutta kusurlar (sineklenme) olduğu belirlenmiştir. Ticari karışım kimyasalın emaye bünyesindeki toplam gözenek miktar ve boyutlarını bariz şekilde düşürdüğü görülmüştür. Sadece K2TiF6 ilavesinin, yüzeyde gözle görülen kabarcık kusurunu azalttığı, ancak emaye iç bölgesinde oluşan gözenek boyut ve sayısını arttırdığı tespit edilmiştir. Kaplamalardaki Ti miktarının durulama banyosunun içeriğine bağlı olarak değişmediği görülmüştür.

Özet (Çeviri)

In this study, the effect of adding different ratios of dipotassium hexafluorotitanate (K2TiF6) to the final rinse bath on eliminating the blister defect in the enamel coating on steel sheets used in cooker production was investigated. Two different steel sheet suppliers' materials were used, one with surface blister defects and the other without. Firstly, the characterization of these substrate steel sheets was performed using a spectrometer, optical microscope, SEM, SEM-EDS, profilometer, and XRD. Two different final rinse bath was prepared. In the first bath, only K2TiF6 was added, while in the second bath, a commercial mixture containing K2TiF6 was added. After these rinse baths, enamel coatings with a thickness of 80-125 µm were fired at 820 °C in an open atmosphere. The characterization of the enamel coatings was carried out using the aforementioned testing and analysis devices in a similar manner. Minor differences in the chemical compositions of the steel sheets were found, but they were found to have similar phases, and both steels contained carbon-rich inclusions. While there were minor differences in the chemical compositions of the steel sheets, they had similar phases and included carbon-rich inclusions. Significant differences were observed in the grain size and surface roughness values of both steels. After the samples were coated, it was determined that the surface roughness value was slightly higher in the enamels with surface blister defects. In all enamel coatings, similar crystal phases were found along with some amorphous phase. Microscopic blistering/pores was observed on the enamel surfaces of all samples, but it was visible to the naked eye in some coatings. It was observed that the commercial mixture significantly reduced the total pore quantity and size within the enamel structure. The addition of only K2TiF6 reduced the visibly observable blister defect on the surface but increased the pore size and quantity within the enamel bulk. It was observed that the amount of Ti in the coatings did not vary depending on the content of the rinse bath.

Benzer Tezler

  1. Taban malzeme ile emaye kaplama arasındaki difüzyon mekanizmasının araştırılması ve düşük metal migrasyonuna sahip emaye geliştirilmesi

    Investigation of diffusion mechanisms at substrate enamel interface and development of new enamel surface with low metal migration

    ÖZGE IŞIKSAÇAN

    Doktora

    Türkçe

    Türkçe

    2020

    Besin Hijyeni ve Teknolojisiİstanbul Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. ONURALP YÜCEL

  2. Yeni yönetmeliklere göre gıdalarla temasa uygun emaye yüzeylerin geliştirilmesiyeni

    Development of food contact safe enamel surfaces according to the new regulations

    GİZEM KADAKAL

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. ONURALP YÜCEL

  3. Termik santrallerin döner tip hava ısıtıcılarında kullanılan ısı değiştirici plakalar için emaye kaplama optimizasyonu

    Optimization of enamel coatings on heat exchanger plates used in rotary air preheaters of thermal power plants

    ERDEM GÜNGÖR

    Yüksek Lisans

    Türkçe

    Türkçe

    2015

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı

    PROF. DR. HÜSEYİN ÇİMENOĞLU

    DOÇ. DR. ERDEM ATAR

  4. Emaye kaplamaya uygun saclarda üretim proses parametrelerinin şekillendirme performansı ve hidrojen geçirgenlik direnci üzerine etkilerinin incelenmesi

    Investigation of effective process parameters on forming performance and hydrogen permeability resistance of enameling steel

    RAMAZAN UZUN

    Doktora

    Türkçe

    Türkçe

    2022

    Metalurji MühendisliğiYıldız Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. ADEM BAKKALOĞLU

  5. Çelik yüzeylerin işlenmesinin kaynak kalitesine etkisinin araştırılması

    Investigation of the effect of welding quality on the processing of steel surfaces

    GÜLÇİN BARBAROS AK

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    İnşaat MühendisliğiAkdeniz Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. RAMAZAN ÖZÇELİK

    YRD. DOÇ. DR. BARIŞ ERDİL