Basınç kaynağı ile birleştirilmiş AA6061, AA5052 alüminyum alaşımları ile AISI 304L paslanmaz çelik malzemenin mekanik özelliklerinin incelenmesi
Investigation of the mechanical properties of AA6061, AA5052 aluminum alloys joined with AISI 304L stainless steel using pressure welding
- Tez No: 835043
- Danışmanlar: DR. ÖĞR. ÜYESİ RECEP YURTSEVEN
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Farklı metallerin kaynağı, 304L paslanmaz çelik, 5052 alüminyum alaşımı, 6061 alüminyum alaşımı, nokta direnç kaynağı, çekme dayanımı, mikrosertlik, Welding of dissimilar metals, 304L stainless steel, 5052 aluminum alloy, 6061 aluminum alloy, resistance spot welding, tensile strength, microhardness
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Pamukkale Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Konstrüksiyon ve İmalat Bilim Dalı
- Sayfa Sayısı: 93
Özet
Günümüzde, mühendislik ve endüstriyel uygulamalarda, farklı malzemelerin üstün özelliklerinden yararlanmak ve aynı zamanda maliyet açısından avantaj sağlamak amacıyla farklı malzemelerin birleştirilmesi giderek daha fazla önem kazanmaktadır. Farklı metallerin birleştirilmesinde yaygın olarak kullanılan kaynak yöntemi basınçlı kaynak yöntemlerinden elektrik direnç nokta kaynağıdır. Kaynak bağlantısından istenilen mekanik özellikleri elde edebilmek için, kaynak kalitesinin ve kaynak mikro yapısının iyileştirilmesi gerekmektedir. Bu iyileştirmeler, özellikle kaynak parametrelerinin doğru bir şekilde belirlenmesi ile sağlanabilir. Bu çalışma kapsamında, farklı kalınlıklarda 304L östenitik paslanmaz çelik ile 5052 ve 6061 alüminyum alaşımları, farklı kaynak akımı parametrelerinde nokta direnç kaynağı yöntemiyle birleştirilmiştir. Kaynak işlemi sırasında, 5 kA, 5,5 kA ve 6 kA kaynak akım değerleri uygulanmıştır. Diğer önemli kaynak parametreleri olan elektrot basıncı ve kaynak süresi sabit tutulmuştur. Kaynak işlemi sonrası malzemelerin mekanik özelliklerini değerlendirmek için, çekme deneyleri ve mikrosertlik ölçümleri yapılmıştır. Ayrıca kaynak bölgesi, taramalı elektron mikroskobu (SEM) görüntüleri ile incelenmiştir. Kaynak bağlantılarının mekanik ve metalografik özellikleri, kaynak akımının bu bağlantılar üzerindeki etkilerini anlamak amacıyla ayrıntılı bir şekilde değerlendirilmiştir. Deney sonuçlarına dayalı olarak, kaynak akımının artmasıyla birlikte çekme dayanımının arttığı tespit edilmiştir. Bu tez kapsamındaki bulgular ile farklı malzemelerin kaynağına yönelik daha etkili ve optimize edilmiş süreçlerin geliştirilmesine katkı sağlanabilir. Böylece, mekanik özelliklerin arttırılası ile endüstriyel kaynak uygulamaları daha verimli ve güvenilir hale getirilebilir.
Özet (Çeviri)
In today's engineering and industrial applications, the joining of dissimilar materials to harness their superior properties while also achieving cost advantages is becoming increasingly important. One of the commonly used welding methods for joining dissimilar metals is resistance spot welding in metalworking and industrial applications. To obtain the desired mechanical properties from the weld joint, it is essential to improve the quality and microstructure of the welding. These improvements can be achieved, especially by accurately determining welding parameters. In this study, different thicknesses of 304L austenitic stainless steel were joined with 5052 and 6061 aluminum alloys using the resistance spot welding method at different welding current parameters. During the welding process, welding current values 5 kA, 5.5 kA, and 6 kA were applied. Other important welding parameters such as electrode pressure and welding time were kept constant. To evaluate the mechanical properties of the materials after the welding process, tensile tests and microhardness measurements were conducted. Additionally, the welding zone was examined with scanning electron microscopy (SEM) images. The mechanical and metallographic properties of the weld joints were thoroughly evaluated to understand the effects of welding current on these connections. Based on the experimental results, it was observed that the tensile strength increased as the welding current increased. The findings in this thesis can contribute to the development of more effective and optimized processes for welding different materials. Consequently, by enhancing mechanical properties, industrial welding applications can be made more efficient and reliable.
Benzer Tezler
- Resistance spot welding of aluminum alloy to carbon steelusing copper as filler metal
Bakır folyo dolgu metali kullanılarak alüminyum alaşımının karbon çeliğine direnç punta kaynağı
HAMZAH HASAN YOUNUS YOUNUS
Yüksek Lisans
İngilizce
2023
Makine MühendisliğiKarabük ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ CEVAT ÖZARPA
- Benzer ve farklı türden alüminyum alaşımlarının sürtünme karıştırma kaynağının deneysel ve sayısal olarak incelenmesi
Investigation of similar and dissimilar friction stir welding of aluminum alloys experimentally and numerically
ZEKİ ALPER KADAYİFÇİ
Yüksek Lisans
Türkçe
2013
Makine MühendisliğiDokuz Eylül ÜniversitesiMakine Mühendisliği Bölümü
DOÇ. DR. BİNNUR GÖREN KIRAL
- Difüzyon kaynağı ile birleştirilmiş TM bakır esaslı kompozit malzemelerin mikroyapı ve mekanik özelliklerinin incelenmesi
Investigation of microstructure and mechanical properties of powder metallurgy (PM) copper-based composites welded by diffusion technique
MARWAN ABDUSSALAM MOHAMMED ELHEMSHERI
Doktora
Türkçe
2022
Mühendislik BilimleriKastamonu ÜniversitesiMalzeme Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ÖZKAN ESKİ
- Ti-6Al-4V/304L malzeme çiftinin bakır aratabaka kullanılarak difüzyon kaynağı ile birleştirilmesi
Diffusion bonding of Ti-6Al-4V/304L steels couple using copper interlayer
BARIŞ BİLGİN
Yüksek Lisans
Türkçe
2007
Metalurji MühendisliğiFırat ÜniversitesiMetalurji Eğitimi Ana Bilim Dalı
DOÇ.DR. NİYAZİ ÖZDEMİR
- Yüksek krom nikel alaşımlı paslanmaz çeliğin alaşımsız düşük karbonlu çelikle difüzyon kaynağının araştırılması
Investigation of the diffusion bonding of a stainless steel with a high chromium and nickel content to a plain law carbon
SERMİN KOÇER
Yüksek Lisans
Türkçe
1998
Metalurji MühendisliğiFırat ÜniversitesiMetalurji Eğitimi Ana Bilim Dalı
YRD. DOÇ. DR. NURİ ORHAN