Geri Dön

Bor ve karbon nanotüpün yonga levha özellikleri üzerindeki etkisinin araştırılması

Investigation of the effect of boron and carbon nanotube on particleboard properties

PDF İndir

  1. Tez No: 859665
  2. Yazar: MUHAMMED ZAKİR TUFAN
  3. Danışmanlar: PROF. DR. CENGİZ ÖZEL, PROF. DR. BİROL ÜNER
  4. Tez Türü: Doktora
  5. Konular: Ağaç İşleri, Ormancılık ve Orman Mühendisliği, Wood Products, Forestry and Forest Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2024
  8. Dil: Türkçe
  9. Üniversite: Isparta Uygulamalı Bilimler Üniversitesi
  10. Enstitü: Lisansüstü Eğitim Enstitüsü
  11. Ana Bilim Dalı: Orman Endüstri Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 237

Özet

Bu çalışmada, iki farklı tutkal türü (Üreformaldehit (UF) ve Melamin üreformaldehit (MUF)), dört farklı bor türü (Çinkoborat (ÇB), Boraks Dekahidrat (BD), Etidot (ED), Eticol (EC)), üç farklı oranda (%3, %7, %11), ve üç farklı karbon nanotüp (KNT) oranı (%0.5, %1, %1.5) kullanılarak üretilen yonga levhaların fiziksel, mekanik ve kimyasal özellikleri araştırılmıştır. Kimyasal özellikleri belirlemek için TGA, SEM-EDS ve FTIR analizleri kullanılmış, ayrıca yüzey temas açısı ölçümleri yapılmıştır. KNT oranı arttıkça, su alma oranı ve kalınlık artım oranlarında iyileşme gözlemlenmiştir: Su alma oranı (%4-22 (UF), %5-37 (MUF)), kalınlık artım oranları ise (%4.19-6.63 (UF), %3.65-5.84 (MUF)) arasında değişmiştir. Genel olarak, UF tutkallı levhaların fiziksel özellikleri MUF tutkallı levhalardan daha iyi olduğu belirlenmiştir. KNT kullanım oranı arttıkça, mekanik özelliklerdeki iyileşme %1'e kadar devam ederken, %1.5 KNT kullanımında düşüş eğilimi olduğu belirlenmiştir. Ayrıca, UF tutkallı levhalardan elde edilen mekanik değerlerin MUF tutkallı levhalardan daha iyi olduğu tespit edilmiştir. TGA analizi, bor ve KNT kullanımıyla yonga levhalarının ilk bozunma sıcaklıklarında artış olduğunu göstermiştir. Yüzey temas açısı ölçümleri, KNT kullanımının artmasıyla yonga levhalarının hidrofobik özellik kazandığı belirlenmiştir. FTIR analizi, OH-CH2-CH3 ve ester gruplarında belirgin değişikliklerin meydana geldiği tespit edilmiştir. EDS analizi ile yonga levhalarda C, Na, Ca ve Zn elementlerinin yüksek oranda bulunduğu tespit edilmiştir.

Özet (Çeviri)

In this study, the physical, mechanical and chemical properties of particleboards produced using two different types of glue (Ureaformaldehyde (UF) and Melamine ureaformaldehyde (MUF)), four different types of boron (Zincborate (ÇB), Borax decahydrate (BD), Etidot (ED), Eticol (EC)), three different proportions (%3, %7, %11), and three different carbon nanotube (CNT) ratios (%0.5, %1, %1.5) were investigated. TGA, SEM-EDS and FTIR analyses were used to determine the chemical properties and surface contact angle measurements were also performed. As the CNT ratio increased, water uptake rate and thickness increase rates improved: Water absorption rate (%4-22 (UF), %5-37 (MUF)) and thickness increase rates (%4.19-6.63 (UF), %3.65-5.84 (MUF)). In general, the physical properties of UF glued boards were better than MUF glued boards. It was determined that as the CNT usage rate increases, the improvement in mechanical properties continues up to %1, while there is a decreasing trend at %1.5 CNT usage. In addition, it was determined that the mechanical values obtained from UF glued boards were better than MUF glued boards. TGA analysis showed that the initial decomposition temperatures of the particleboards increased with the use of boron and CNT. Surface contact angle measurements showed that the particleboards gained hydrophobic properties with the increase in the use of CNT. FTIR analysis showed that significant changes occurred in OH-CH2-CH3 and ester groups. EDS analysis revealed that C, Na, Ca and Zn elements were highly present in the particleboards.

Benzer Tezler

  1. Tez No

    299434

    Karbon nanotüplerin fiziksel özellikleri üzerine katkılamanın etkilerinin incelenmesi

    Investigation of doping effects on physical properties of carbon nanotubes

    ERKAN TETİK

    Doktora

    İngilizce

    İngilizce

    2012

    Fizik ve Fizik MühendisliğiÇukurova Üniversitesi

    Fizik Ana Bilim Dalı

    DOÇ. DR. FARUK KARADAĞ

  2. Tez No

    698539

    Mechanical properties of boron nanotubes

    Bor nanotüplerin mekanik özellikleri

    ERDEM ÇALIŞKAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2021

    Makine Mühendisliğiİstanbul Teknik Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MESUT KIRCA

  3. Tez No

    766655

    PBMA/h-BN ve PBMA/fonksiyonelize bn nanokompozitlerinin termal ve kinetik özellikleri

    Thermal and kinetic properties of PBMA/h-BN and PBMA/functionalized bn nanocomposites

    MEHMET DOĞAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    KimyaBingöl Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. ZAFER ŞERBETÇİ

  4. Tez No

    247010

    Bor karbür nanopartiküllerin ve karbon nanotüplerin sentezlenmesi ve karakterizasyonu

    Synthesis and characterization of boron carbide nanoparticles and carbon nanotubes

    SALİM EĞEMEN KARABULUT

    Yüksek Lisans

    Türkçe

    Türkçe

    2009

    Makine MühendisliğiSelçuk Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. AHMET AVCI

  5. Tez No

    676125

    AISI 316L paslanmaz çelik matrisli, bor karbür ve karbon nanotüp takviyeli nanokompozitlerin toz metalurjisi ile üretimi ve karakterizasyonu

    Production and characterization of AISI 316L stainless steel matrix, boron carbide and carbon nanotube reinforced nanocomposites by powder metallurgy

    ESRA ZENGİN

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Metalurji MühendisliğiKarabük Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. HAYRETTİN AHLATCI

Geri Dön