ZnO ve MgO nanopartikülü katkılanmış dental PMMA'ların antibakteriyel, antifungal, mekanikve fiziksel özelliklerinin incelenmesi ve sitotoksisite açısından değerlendirilmesi
Investigation of the antibacterial, antifungal, mechanical and physical properties of zinc oxide and magnesium oxide nanoparticle added dental PMMAs and evaluation in terms of
- Tez No: 862062
- Danışmanlar: PROF. DR. ENDER AKAN, DR. ÖĞR. ÜYESİ NUSRET KAYA
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2024
- Dil: Türkçe
- Üniversite: İzmir Katip Çelebi Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Dental polimetil metakrilatlar sahip olduğu avantajlar sayesinde günümüzde yaygın olarak kullanılmaktadır. Ancak mekanik özelliklerindeki yetersizlik hastaların protez kırıkları gibi çeşitli zorluluklarla karşılaşmasına neden olmaktadır. Çalışmamızdaki amaç magnezyum oksit ve çinko oksit katkılanmış dental PMMA'larile protezlerde meydana gelen kırılmaları önlemek, mekanik olarak güçlendirilmesini sağlamak ve bu mekanik kazanımlarla birlikte antifungal, antibakteriyel etkisi ve biyolojik uyumu ile sitotoksisitesini takip etmektir. %0,5 - %1 - %3 - %5 oranlarında ayrı ayrı magnezyum oksit ve çinko oksit katkılanmış PMMA'larla hazırlanmış 50mm-15mm-2mm boyutlarındaki yüzey işlemleri uygulanmış örneklere öncelikle mekanik testler uygulanmıştır. Daha sonradisk şeklinde hazırlanan örneklere antifungal ve antibakteriyel testler uygulanmış ve MTT tekniği ile sitotoksisite açısından değerlendirilmiştir. Eğilme dayanımı değerleri açısından ZnO ve MgO nanopartikülü ilave edilen gruplarda kontrol grubuna gör daha düşük değerler bulunmuştur (p<0,05). Sitotoksisite yönünden değerlendirildiğinde kontrol gruplarına göre nanopartikül katkılanan gruplarda sitotoksik etki gözlemlenmiştir. Bu sitotoksik etkinin şiddeti nanopartikül ilavesinin yüzdece oranı arttıkça şiddetlenmektedir. Ayrıca MgO nanopartikülü içeren örneklerin ZnO nanopartikülü içeren örneklere göre daha fazla sitotoksik etkisinin olduğu bulunmuştur (p<0,05). Farklı oranlarda nanopartikül ilave edilmiş örneklerin candidaalbicans'a karşı etkisinin karşılaştırılması amacıyla yapılan mikrobiyolojik testler sonucunda her iki nanopartikül sisteminde de candidaalbicans'a karşı etki izlenmemiştir. ZnO ve MgO nanopartikülü katkılanmış örnekler antibakteriyel etkisi açısından incelenmiş ve tüm oranlarda üretilen örneklerin kontrol grubuna karşı anlamlı bir etkisi izlenmemiştir. Bu çalışmanın limitasyonları dahilinde nanopartikülünün aglomerasyon eğiliminin fazla olmasının mekanik güçlendirme üzerinde olumsuz etki yarattığı söylenebilir. Ayrıca çinko oksit ve magnezyum oksit nanopartiküllerinin biyolojik etkileri için daha fazla çalışmaya ihtiyaç vardır.
Özet (Çeviri)
Dental polymethyl methacrylates are widely used today due to their advantages. However, the mechanical shortcomings of these materials lead to various challenges for patients, such as prosthetic fractures. The aim of our study is to prevent fractures in prosthetics made with magnesium oxide and zinc oxide-modified dental PMMAs, to enhance their mechanical strength, and to evaluate their antifungal, antibacterial effects, and cytotoxicity along with biological compatibility. Surface applications were applied to samples prepared with 0.5%, 1%, 3%, and 5% magnesium oxide and zinc oxide separately in dental PMMAs, with dimensions of 50mm-15mm-2mm. Mechanical tests were initially applied to these samples. Subsequently, disc-shaped samples were subjected to antifungal and antibacterial tests, and cytotoxicity was evaluated using the MTT technique. In terms of flexural strength values, lower values were found in the groups with added ZnO and MgO nanoparticles compared to the control group (p<0.05). Regarding cytotoxicity, a cytotoxic effect was observed in groups with nanoparticle additives compared to the control groups. The intensity of this cytotoxic effect increases as the percentage of nanoparticle addition increases. Additionally, samples containing MgO nanoparticles were found to have a greater cytotoxic effect than those containing ZnO nanoparticles (p<0.05). Microbiological tests comparing the effects of samples with different nanoparticle additions against Candida albicans revealed no effect in both nanoparticle systems. Samples modified with ZnO and MgO nanoparticles were examined for their antibacterial effects, and no significant effect was observed against the control group in all ratios. Within the limitations of this study, it can be stated that the high agglomeration tendency of nanoparticles negatively affects mechanical reinforcement. Furthermore, more research is needed to understand the biological effects of zinc oxide and magnesium oxide nanoparticles.
Benzer Tezler
- Investigation of nanoparticle additives to the biodiesel and diesel fuels for improvement of the performance and exhaust emissions in a compression ignition engine
Dizel motorlarda performans ve egzoz emisyonlarinin iyileştirilmesi için biyodizel ve dizel yakitlarina ilave edilen nanopartikül katkilarinin incelenmesi
TAYFUN ÖZGÜR
Yüksek Lisans
İngilizce
2011
Makine MühendisliğiÇukurova ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. KADİR AYDIN
- Nanopartikül katkılı parafinin ısıl performansının deneysel analizi
Experimental analysis of thermal performance of nanoparticle enhanced paraffin
NERGİZ ÜLKER
Yüksek Lisans
Türkçe
2021
EnerjiHarran ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSAMETTİN BULUT
- Tuz stresi koşullarında yetiştirilen marul ve yaprak salatada (lactuca sativa) nanopartiküler demir oksit, çinko oksit, bakır oksit ve magnezyum oksit uygulamalarının agro-morfolojik ve fizyolojik etkilerinin belirlenmesi
Determination of agro-morphological and physiological effects of nanoparticle iron oxide, zinc oxide, copper oxide, and magnesium oxide applications on lettuce and leaf lettuce (lactuca sativa) grown under salt stress conditions
SEVDA DURSUN
- Parabolik oluk tipi güneş kolektörlerinde nanoakışkan kullanımının ısıl performansa etkisinin deneysel ve sayısal incelenmesi
Experimental and numerical investigation of the effect of nanofluid usage on thermal performance in parabolic trough type solar collectors
RECEP EKİCİLER
Doktora
Türkçe
2022
EnerjiKarabük ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. KAMİL ARSLAN
PROF. DR. OĞUZ TURGUT
- Nanoakışkanların termofiziksel ve reolojik özelliklerinin yapay sinir ağları ile tahmin edilmesi
Prediction of the thermophysical and rheological properties of nanofluids with artificial neural network
KASIM ERDEM
Yüksek Lisans
Türkçe
2022
Makine Mühendisliğiİstanbul Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ABDUSSAMET SUBAŞI