304 çeliğin korozyonuna azo boyar maddelerin inhibitör etkisi
Inhibitory effect of azo dyes on corrosion of 304 steel
- Tez No: 897677
- Danışmanlar: PROF. DR. ABDURRAHMAN ASAN
- Tez Türü: Yüksek Lisans
- Konular: Kimya Mühendisliği, Chemical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2024
- Dil: Türkçe
- Üniversite: Hitit Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 73
Özet
Bu çalışmada asidik, bazik ve klorürlü ortamlarda 2,2'- (((1E,1'E) -1,4- fenilenbis (metaniliden)) bis (azaniliden)) bis (5,5,7,7-tetrametil -4,5,6,7- tetrahidrobenzo (b) tiyofen -3- karbonitril) (AZOB1) ve 2,2'- (((1E,1'E) -1,4- fenilenbis (metaniliden)) bis (azaniliden)) bis (4-etil-5-metiltiyofen -3- karbonitril) (AZOB2) bileşiklerinin Ç 304 çeliğin korozyonuna inhibitör etkisi araştırıldı. Deneysel çalışmalar 0.1 M NaOH, 0.1 M HCI ve 0.1 M NaCI çözeltilerinde gerçekleştirildi. Çeliğin inhibitörsüz ve 50, 100, 250 ve 500 ppm derişimlerde AZOB1 ve AZOB2 bileşikleri içeren bu korozif ortamlardaki elektrokimyasal davranışını belirlemek için Dönüşümlü Voltametri tekniği uygulandı. Bileşiklerin inhibitör etkinliğini belirlemek için gerekli olan çeliğin korozyon hızı ölçümleri Tafel Polarizasyon yöntemi ile yapıldı. Deneyler sonucunda tüm ortamlarda ve her derişimde bileşiklerin inhibitör etkisi gösterdiği belirlendi. Bileşiklerin ortamdaki derişimi arttıkça inhibitör etkinliğinin arttığı tespit edildi. En iyi inhibitör etkinliği 0.1 M HCI çözeltisinde 500 ppm'de AZOB1 için %68, AZOB2 için %80 olarak bulundu.
Özet (Çeviri)
In this study, the inhibitory effects of 2,2'-(((1E,1'E)-1,4-phenylenebis(methanylidene)) bis(azanilidene))bis(5,5,7,7-tetramethyl-4,5,6,7-tetrahydrobenzo(b)thiophene-3-carbonitrile) (AZOB1) and 2,2'-(((1E,1'E)-1,4-phenylenebis(methanylidene)) bis(azanilidene)) bis(4-ethyl-5-methylthiophene-3-carbonitrile) (AZOB2) compounds on the corrosion of Ç 304 steel were investigated in acidic, basic and chloride media. Experimental studies were carried out in 0.1 M NaOH, 0.1 M HCl and 0.1 M NaCl solutions. Cyclic Voltammetry technique was applied to determine the electrochemical behavior of steel in these corrosive environments without inhibitor and containing AZOB1 and AZOB2 compounds at concentrations of 50, 100, 250 and 500 ppm. The corrosion rate measurements of steel, which are necessary to determine the inhibitory activity of the compounds, were made by Tafel Polarization method. As a result of the experiments, it was determined that the compounds showed inhibitory effect in all environments and at all concentrations. It was determined that the inhibitory activity increased as the concentration of the compounds in the environment increased. The best inhibitory activity was found to be 68% for AZOB1 and 80% for AZOB2 at 500 ppm in 0.1 M HCl solution.
Benzer Tezler
- Bazı benzoazol türevlerinin sülfürik asit ortamında çeliğin korozyonuna inhibitör etkilerinin kunantum kimyasal incelemesi
Determination of quantum chemical of inhibition of type 304 stainless steel corrosion in 2M sulfuric acid by some benzoazoles
FUNDA BAYER
Yüksek Lisans
Türkçe
2005
KimyaEskişehir Osmangazi ÜniversitesiKimya Ana Bilim Dalı
PROF.DR. GÖZEN BEREKET
- 304 L çeliğinin bazik ortamdaki elektrokimyasal özelliklerine bazı bor bileşiklerinin etkisi
The effects of some bor's compounds on electrochemical properties of 304 L steel in basic media
GÜL SEDA ÖZ
- Dubleks paslanmaz çeliğin Ni3Al ile kaplanabilirliğinin araştırılması.
Investigation with Ni3Al coating of dublex stainless stell
TAYFUN ÇETİN
Yüksek Lisans
Türkçe
2014
Metalurji MühendisliğiFırat ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. SERMİN OZAN
- Östenitik paslanmaz çeliğin bor katkılı Ni3Al ile kaplanabilirliğinin araştırılması
Investigation of boron doped Ni3Al coating of austenitic stainless stell
MEHMET AKKAŞ
Yüksek Lisans
Türkçe
2013
Metalurji MühendisliğiFırat ÜniversitesiMetalurji Eğitimi Ana Bilim Dalı
DOÇ. DR. SERMİN OZAN
- Elektrolit parlatma yönteminin 430 kalite paslanmaz çelik malzemenin korozyon direncine etkisi
The effect of electroplishing on the corrosion behaviour of 430 type stainless steel
ŞEBNEM AYDOĞAN
Yüksek Lisans
Türkçe
2003
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ALİ FUAT ÇAKIR