Fabrication of ceramic particle-reinforced polymer matrix composites via DLP-additive manufacturing
DLP-eklemeli imalat yöntemiyle seramik parçacık takviyeli polimer matris kompozitlerinin üretimi
- Tez No: 899144
- Danışmanlar: PROF. DR. ÖMER EYERCİOĞLU, DOÇ. DR. DERYA KAPUSUZ YAVUZ
- Tez Türü: Doktora
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2024
- Dil: İngilizce
- Üniversite: Gaziantep Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Konstrüksiyon ve İmalat Bilim Dalı
- Sayfa Sayısı: 95
Özet
Eklemeli İmalat (AM), karmaşık şekilli malzemelerin üretilmesini sağlar. Son on yılda, polimer matris kompozitlerin (PMC'ler) katmanlı üretiminde çeşitli teknikler geliştirilmiştir. Bu çalışma, dijital ışık işleme (DLP) yoluyla toz takviyeli PMC'lerin AM'sine odaklanmıştır. PMC'ler, alümina ve çinko titanat tozlarıyla takviye edilmiş UV duyarlı foto-reçine kullanılarak üretilmiş. Ağırlıkça %50 alümina takviyeli numuneler için parçacıklarının mikro-yapı boyunca dağılımı SEM-EDS ile karakterize edilmiştir. Basılı numuneler, geleneksel kalıplanmış olanlardan daha iyi dağılım sonuçları göstermiştir. Çinko titanat tozları; sol-jel ve solvotermal yöntemlerle sentezlenmiştir. Elde edilen fazlar incelenmiş ve karakterize edilmiştir. [Zn/Ti] kontrol edilerek fotokatalitik kabiliyetleri araştırılmıştır. Çinko titanat takviyeli reçine örnekleri kalıplanmış ve karakterize edilmiş ve renk kararlılığı testi %3 ağırlıkça çinko titanat örneklerinin üstünlüğünü göstermiştir. Yüksek sıcaklık reçinesi 2 ve 4 % ağırlıkça alümina ile takviye edilmiş ve örnekler DLP-AM ile üretilmiştir. Örneklerin fiziksel ve mekanik özellikleri araştırılmıştır. Yüksek sıcaklık reçinesi, hibrit enjeksiyon kalıplama işleminin bir çalışmasında kullanılmıştır. HDPE'nin düşük basınçlı enjeksiyon kalıplaması gerçekleştirilmiş ve kalıpların performansı analiz edilmiştir. Sonuçlar, %4 ağırlıkça alümina eklenmesiyle kalıbın ısıl iletkenliğinin %12 arttığını göstermiştir. Bu sayede kalıpların soğuma süresi ve enjeksiyon kalıplama işleminin süresi azaltılabilmektedir.
Özet (Çeviri)
Additive manufacturing (AM) enables the production of complex-shaped materials. In the last decade, various techniques have been developed in additive manufacturing of polymer matrix composites (PMCs). This study is focused on the AM of powder-reinforced PMCs via digital light processing (DLP). PMCs were fabricated by UV-sensitive photo-resins reinforced by alumina and zinc titanate powders. The distribution of Alumina particles throughout the microstructure for 50 wt.% Alumina-reinforced samples were characterized. The printed samples showed better distribution than the traditional molded ones. The zinc titanate powders were synthesized by sol-gel and solvothermal methods. The resulting phases were examined and characterized. Then their photocatalytic capability was investigated by controlling [Zn/Ti]. zinc titanate-reinforced resins were molded and characterized and the color stability test showed the superiority of the 3 wt.% zinc titanate reinforced samples. A high-temperature resin was reinforced with Alumina by 2 and 4 wt. % and samples were fabricated by DLP-AM. Physical and mechanical properties of samples were investigated in terms of Alumina addition. The low-pressure injection molding process of High-density polyethylene (HDPE) was performed, and the performance of the 3D-printed molds was analyzed. The results showed a 12% increase in the thermal conductivity of the mold with the addition of 4 wt.% of Alumina. This can reduce the cooling duration of the molds and the cycle time of the injection molding process.
Benzer Tezler
- Bakır ve çinko içeren biyoaktif cam katkılı nanokompozit yapı iskelesi üretimi
Fabrication of nanocomposite scaffold with copper and zinc doped bioactive glasses
ZEYNEP ATASAYAR
Yüksek Lisans
Türkçe
2021
Biyomühendislikİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. SADRİYE OSKAY
- Otomotiv endüstrisinde kullanılan Al2O3/SiC partikül destekli metal matriks kompozit üretimi ve mekanik davranışlarının incelenmesi
The Fabrication of Al2O3/SiC particle reinforced metal matrix composites used in automotive, industry and investigation of their mechanical behaviours
NECAT ALTINKÖK
Doktora
Türkçe
2002
Makine MühendisliğiSakarya ÜniversitesiMakine Eğitimi Ana Bilim Dalı
PROF.DR. İBRAHİM ÖZSERT
- Alümina fiber takviyeli Al-si metal matriksli kompozitlerin üretimi ve mikroyapı-özellik ilişkilerinin incelenmesi
production of alumina fiber reinforced Al-si metal matrix composites and the investigation of their microstructure-propetry relation ships
HATEM AKBULUT
- Metal infiltre edilmiş mikro poroz karbon kompozitlerin aşınma ve sürtünme davranışının karakterizasyonu
Başlık çevirisi yok
GÜLTEKİN GÖLLER
Doktora
Türkçe
1997
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. ADNAN TEKİN
- The production and characterization of high thermal conductive coatings for electronic applications
Elektronik uygulamalar için yüksek ısı iletken kaplamaların üretimi ve karakterizasyonu
SUNA AVCIOĞLU
Doktora
İngilizce
2022
Metalurji MühendisliğiOndokuz Mayıs ÜniversitesiNanobilim ve Nanoteknoloji Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SİNEM ÇEVİK