Geoteknik mühendisliğinde sürdürülebilir yapılar için yenibir stabilizasyon önerisi
A new stabilization proposal for sustainable structures ingeotechnical engineering
- Tez No: 909773
- Danışmanlar: DOÇ. DR. TUĞBA ESKİŞAR TEFÇİ
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Geopolimerizasyon, perlit, atık cam tozu, likit aktivatör, zemin iyileştirmesi, Geopolymerization, perlite, waste glass powder, liquid activator, soil improvement
- Yıl: 2024
- Dil: Türkçe
- Üniversite: Ege Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: İnşaat Mühendisliği Bilim Dalı
- Sayfa Sayısı: 106
Özet
Bu çalışmada perlit içeren zeminlerin, perlit içeren zemin geopolimerlerinin, atık cam tozu içeren zeminlerin ve atık cam tozu zemin geopolimerlerinin mekanik özelliklerinin incelenmesi amaçlanmıştır. Örneklere zeminin kuru ağırlığınca %10- 50'si kadar perlit veya atık cam tozu eklenmiştir. Zemin geopolimer örnekleri 7 günden 180 güne kadar değişen farklı kür sürelerine tabi tutulmuş ve kür sıcaklığı olarak 20 veya 40°C seçilmiştir. Farklı özelliklere sahip zemin gruplarını incelemek üzere Atterberg limitleri, kompaksiyon, serbest basınç mukavemeti, direkt kesme kutusu ve konsolidasyon deneyleri yapılmıştır. Perlit içeren zemin geopolimerlerinde, likit aktivatör olarak sodyum hidroksit ile çalışılmıştır. Atık cam tozu içeren zemin geopolimerlerinde sodyum hidroksit ile sodyum silikat da kullanılmıştır. Sadece perlit içeren zeminlerde perlit içeriği arttıkça likit limit ve plastik limitinde azalma olmuştur. Perlit içeren zemin geopolimerlerinde kür süresi ve kür sıcaklığı artışı mukavemette artışa yol açmıştır. 180 gün boyunca 40°C'de küre bırakılan %60 kaolin+%40 perlit+ 6M sodyum hidroksit içeren zemin geopolimer örneğinin serbest basınç mukavemeti 7920 kPa olarak bulunmuştur. Sadece atık cam tozu içeren zeminlerde, atık cam tozu içeriği arttıkça kuru birim hacim ağırlık artarken, optimum su içeriğinde azalma olmuştur. Atık cam tozu içeren zemin geopolimerlerinde en yüksek mukavemet 90 gün boyunca 40°C'de küre bırakılan %70 zemin+%30 atık cam tozu içeren grupta 8923 kPa olarak bulunmuştur. Perlit içeren zeminlerde, perlit içeriği arttıkça konsolidasyon sürecinde başlangıç boşluk oranı azalmıştır. Perlit içeren zemin geopolimerlerinde kür süresi ve kür sıcaklığı kohezyon ve içsel sürtünme açısını arttırmış, sıkışma indislerini de azaltmıştır. Sonuçta, geopolimerizasyon uygulamasının zeminin geomekanik özelliklerini iyileştirici etkileri olduğu ispat edilmiştir.
Özet (Çeviri)
In this study, it was aimed to examine the mechanical properties of perlitecontaining soils, perlite-containing soil geopolymers, waste glass powdercontaining soils and waste glass powder soil geopolymers. Perlite or waste glass powder was added to the samples at the rate of 10-50% of the dry weight of the soil. Soil geopolymer samples were subjected to different curing times ranging from 7 days to 180 days, and 20 or 40°C was selected as the curing temperature. Atterberg limits, compaction, unconfined compressive strength, direct shear and consolidation tests were carried out to examine soil groups with different properties. In soil geopolymers with perlite, only sodium hydroxide was used as a liquid activator. Sodium silicate has also been used along with sodium hydroxide in soil geopolymers containing waste glass powder. In soils containing only perlite, as the perlite content increased, the liquid limit and plastic limit decreased. In soil geopolymers containing perlite, increasing the curing time and curing temperature led to an increase in strength. The unconfined compressive strength of the soil geopolymer sample containing 60% kaolin + 40% perlite + 6M sodium hydroxide, which was left to curing at 40°C for 180 days, was 7920 kPa. In soils containing only waste glass powder, as the waste glass powder content increased, the dry unit weight increased, while the optimum water content decreased. The highest strength in soil geopolymers containing waste glass powder was 8923 kPa in the group containing 70% soil + 30% waste glass powder, which was left to curing at 40°C for 90 days. In perlite-containing soils, as the perlite content increased, the initial void ratio decreased during the consolidation process. In soil geopolymers containing perlite, the curing time and curing temperature increased the cohesion and internal friction angle and reduced the compression indices. As a result, it is proven that geopolymerization application has improving effects on the geomechanical properties of the soil.
Benzer Tezler
- Equivalent linear and nonlinear site response analysis, study case for banda aceh, indonesia
Yerel zemin koşullarının sismik etkiler altında eşdeğer doğrusal ve doğrusal olmayan analizi, banda aceh, endonezya için bir çalısma
AMELIA FITRI
Yüksek Lisans
İngilizce
2022
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Ana Bilim Dalı
PROF. DR. MUSAFFA AYŞEN LAV
- Biyomalzeme kullanımı ile sürdürülebilir zemin iyileştirme
Sustainable soil improvement with the use of biomaterials
MERT KARAGİL
Yüksek Lisans
Türkçe
2021
İnşaat MühendisliğiEge Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. ALPER SEZER
DOÇ. DR. ALPER AKKAYA
- Determination of the mechanical and dynamic properties of recycled concrete aggregate for pavement design
Yol üstyapısı tasarımı için geri dönüştürülmüş beton agregalarının mekanik ve dinamik özelliklerin belirlenmesi
MERVE AKBAŞ
Doktora
İngilizce
2024
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. RECEP İYİSAN
- Geopolimer katkılı jet grout kolonlar ile iyileştirilen organik zeminlerin davranışının incelenmesi
Investigation of the behavior of organic soils improved with geopolymer added jet grout columns
HAKAN YALÇIN
Doktora
Türkçe
2024
İnşaat MühendisliğiErciyes Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. ZÜLKÜF KAYA
DOÇ. DR. MÜGE AKIN
- Enerji kazıklarında ısıl performansın parametrik incelenmesi ve kazık aralıklarının ısıl performansa etkisi
Parametric investigation on thermal performance of energy piles and effect of pile intervals on their thermal performances
TALHA ÖZKAYA
Yüksek Lisans
Türkçe
2016
Enerjiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. MUSTAFA TUĞRUL ÖZKAN