Cam tozu ve talk dolgulu polipropilen kompozitlerin mekanik ve fiziksel özelliklerinin incelenmesi
Investigation of the mechanical and physical properties of glass powder and talk filled polypropylene composites
- Tez No: 910527
- Danışmanlar: PROF. DR. HAMİT ERDEMİ
- Tez Türü: Yüksek Lisans
- Konular: Polimer Bilim ve Teknolojisi, Polymer Science and Technology
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2024
- Dil: Türkçe
- Üniversite: Yalova Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Polimer Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Polimer Malzeme Mühendisliği Bilim Dalı
- Sayfa Sayısı: 61
Özet
Günümüzde kompozit malzemelerin plastik malzeme üretim alanındaki rolleri oldukça büyüktür. Kompozit malzemeler ana matris olarak kullanılan polimer malzemeye bir veya birden fazla dolgu malzemesi eklenerek polimerin özelliklerinin iyileştirilmesiyle oluşur. Bu çalışmada farklı dolgu maddelerinin polipropilen malzemeye eklenmesiyle polimerin mekanik ve fiziksel özelliklerindeki değişimi incelenmiştir. Dolgu maddesi olarak nano mikron boyutunda talk ve cam tozu kullanılmıştır. Dolgu maddeleriyle oluşturulan 6 farklı kompozit çeşidi ekstrüzyon makinesinde farklı oranlarda karıştırılmışlardır. Orijinal hammadde PP ürününe ilk karışım olarak sadece %3 oranında talk eklenmiştir. Daha sonra ise %3 oranında talk miktarı sabit tutularak %5, %10, %15, %20 oranlarında cam tozu eklenmiştir. Hazırlanan karışımlar enjeksiyon kalıplama yöntemiyle çeşitli testler uygulanmak üzere numune olarak üretilmiştir. Üretilen kompozit numunelerine çekme, Izod darbe testleri yapılmış, ayrıca DSC, FTIR, TGA-DTG cihazlarında özellikleri incelenmiş ve değerlerindeki değişimler gözlemlenmiştir. Enjeksiyon kalıplama yöntemiyle üretilen numunelere uygulanan testler sonucunda cam tozu ve talk dolgu maddelerinin polipropilen malzemenin fiziksel ve mekanik özellikleri üzerinde farklı sonuçlar ortaya çıkardığı gözlemlenmiştir. Çekme testi sonuçlarında %5 cam tozu ilave edilen numunede elastik modül değerinin doyma noktasına ulaşarak 712,82 MPa seviyesine geldiği görülmüştür. Bu değerden sonra elastik modül değerinin azaldığı tespit edilmiştir. TGA/DTG analizlerinde talk ilavesiyle bozunma başlangıç sıcaklığının attığı gözlemlenmiştir. Cam tozu ilavesiyle birlikte sıcaklık değerlerinde dalgalanmalar görülmüştür.
Özet (Çeviri)
Today, the role of composite materials in the field of plastic material production is quite large. Composite materials are formed by improving the properties of the polymer by adding one or more filling materials to the polymer material used as the main matrix. In this study, the change in the mechanical and physical properties of the polymer by adding different fillers to the polypropylene material was examined. Nano micron sized talc and glass powder were used as fillers. 6 different types of composites formed with fillers were mixed in different proportions in the extruder. Only 3% talc was added as the first mixture to the original raw material PP product. Then, 5%, 10%, 15%, 20% glass powder was added by keeping 3% talc amount constant. The prepared mixtures were produced as samples for various tests by injection molding method. Tensile, impact and bending tests were performed on the produced composite samples, and their properties were examined using DSC, FTIR and TGA devices and the changes in their values were observed. As a result of the tests applied to the samples produced by the injection molding method, it was observed that glass powder and talc fillers produced different results on the physical and mechanical properties of the polypropylene material. In the tensile test results, it was observed that the elastic modulus value in the sample to which 5% glass powder was added reached the saturation point and reached the level of 712.82 MPa. It was determined that the elastic modulus value decreased after this value. In TGA/DTG analyses, it was observed that the decomposition onset temperature increased with the addition of talc. Fluctuations in temperature values were observed with the addition of glass powder.
Benzer Tezler
- Çam odunu tozu içeren geri dönüştürülmüş polipropilen ve farklı katkılar ile hazırlanan hibrit kompozitlerin özelliklerinin değerlendirilmesi
Evaluation of the properties of hybrid composites based on recycled polypropylene containing pine wood flour and different additives
ESLEM KAVAS
Yüksek Lisans
Türkçe
2024
Mühendislik BilimleriBursa Teknik ÜniversitesiPolimer Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. PINAR TERZİOĞLU
- PE ve PP polimerlerine ahşap tozu ilavesi ile oluşturulan karışımların mekanik, termal ve morfolojik özelliklerinin incelenmesi
Synthesis and investigation of mechanical, thermal and morfological properties of PE and PP/wood flour composites
HASAN BİLTEKİN
Yüksek Lisans
Türkçe
2005
Polimer Bilim ve TeknolojisiMarmara ÜniversitesiMetal Eğitimi Ana Bilim Dalı
Y.DOÇ.DR. MÜNİR TAŞDEMİR
- Development of new generation, high performance polypropylene composites
Yeni nesil, yüksek performanslı polipropilen kompozitlerin geliştirilmesi
ORKUN KAYMAKÇI
Doktora
İngilizce
2021
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. NURSELİ UYANIK
- Cam tozu ve yüksek fırın cürufu kullanımlarının ultra yüksek performanslı beton karışımlarının basınç dayanımına etkisi
Effect of uses of glass powder and ground granulated blast furnace slag to compressive strenght of ultra high performance concrete mixtures
NİYAZİ BIÇAKÇIOĞLU
Yüksek Lisans
Türkçe
2020
İnşaat MühendisliğiBalıkesir Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ UMUT HASGÜL
- Betonun mekanik özellikleri üzerine cam tozu ve alkalilerle aktive edilmiş yüksek fırın cürufu etkisi
The effect of glass powder and alkali activated blast furnace slag on mechanical properties of concrete
MAHIR ALIYEV
Yüksek Lisans
Türkçe
2019
İnşaat MühendisliğiAtatürk Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ MERAL OLTULU