Evaluation of shear bond strength of universal resin cements to dentin subjected to air-particle abrasion before and after thermocycling: An in- vitro study
Termal siklus öncesi ve sonrası air-abrazyon maruz kalan dentine uygulanan üniversal rezin simanın bağlantı kuvvetlerinin in vitro olarak değerlendirilmesi
- Tez No: 931577
- Danışmanlar: PROF. DR. ENDER KAZAZOĞLU
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Universal rezin siman, air-abrazyon, bağlantı kuvveti, termal siklus, Universal resin cement, Air-particle abrasion, shear bond strength, thermocycling
- Yıl: 2024
- Dil: İngilizce
- Üniversite: Yeditepe Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu in-vitro tez çalışmasında, Termal Siklus Öncesi ve Sonrası air-abrazyon maruz kalan dentine uygulanan iki tip üniversal rezin simanın bağlantı kuvvetlerinin değerlendirilmeyi amaçlamaktadır. Gereç ve Yöntem: Dentin açığa çıkmış insan diş örnekleri (n=72) hazırlandı. Tüm örnekler silikon karbür kağıdıyla cilalandı. Örnekler eşit ve rastgele iki gruba ayrıldı; bunlardan birinde dentin bağlama yüzeyi air-abrazyon (Al2O3, 50 µm) (APA grubu) (n=36) ile ön işlem gördü ve herhangi bir ön işlem görmeyen bir kontrol grubu (APA yok) oluşturuldu. Her grup (APA, APA yok) uygulanacak simana göre rastgele iki gruba (no=18) ayrıldı: RelyX Universal (3M™ ESPE, St. Paul, MN, ABD) ve G-CEM ONE Universal (GC, Tokyo, Japonya). Bağlama işlemleri primersiz, self-etch, self-adeziv modunda gerçekleştirildi. Her grup ayrıca saklama koşullarına göre iki alt gruba (n=9) ayrıldı; 37C°'de suda 24 saat saklama ve termal siklus (10000 döngü). Son olarak, tüm örnekler için bağlantı kuvvetlerinin testleri yapıldı. Başarısızlık tipleri de değerlendirildi. Veriler, p<0,05 anlamlılık düzeyinde tek yönlü ve iki yönlü varyans analizi (ANOVA) ve Tukey HSD testi kullanılarak analiz edildi. Bulgular: APA maruz kalan ve maruz kalmayan örnekler arasında bağlantı kuvvetlerinde istatistiksel olarak anlamlı bir fark vardı (p<0,05). Ayrıca, iki siman ortalama değerleri arasında (p<0,05) ve termal siklus maruz kalan örnekler arasında (p<0,05) istatistiksel olarak anlamlı bir fark vardı. En yüksek bağlantı kuvvetlerin değerleri (RelyX Universal, termal siklus yok, APA,) grubunda (6,26±1,22 MPa) gözlenirken, en düşük bağlantı kuvvetlerin değerleri (G-CEM ONE, termal siklus, APA olmayan,) grubunda (2,75±0,76 MPa) gözlendi. APA varlığında veya yokluğunda ve iki siman grubunda, termosiklus tüm grupların bağlantı kuvvetlerini azaltmıştır (p<0,05). En çok bulunan kırılma türü adeziv kırılma iken (%65,3), karma kırılma oranı ise %25 ve koheziv kırılma oranı %9,7 olarak belirlendi. Sonuç: Air-abrazyon, bağlantı kuvvetlerinin ortalama değerlerini artırılmıştır. Termal siklus, çoğu grupların bağlantı kuvvetlerini azaltmıştır. RelyX Universal siman, G-CEM ONE simanından daha yüksek bir bağlantı kuvvetlerine sahip olduğu bulundu.
Özet (Çeviri)
PURPOSE: This in-vitro study aimed to evaluate the shear bond strength of two types of universal resin cements to dentin when treated with air-particle abrasion before and after thermocycling. MATERIALS AND METHODS: The human teeth with exposed dentin (n=72) were prepared. All of these samples were then polished with silicone carbide paper. The samples were equally and randomly divided into two groups one of which the dentin bonding surface was pretreated with air-borne particle abrasion (Al2O3, 50µm) (APA group) (n=36) and a control group which did not receive any pretreatment (No APA). Each group (APA, No APA) was further randomly divided into two groups (no=18) according to the cement to be applied, namely: RelyX Universal (3M™ ESPE, St. Paul, MN, USA) and G-CEM ONE Universal (GC, Tokyo, Japan). Bonding procedures were performed in a no-primer, self-etch, self-adhesive mode. According to the period of storage, each group was further divided into two subgroups (n=9); short period of 24-hours in a 37C° water and thermocycling (10000 cycles). Ultimately, all samples were subjected to shear bond strength tests. Failure forms were assessed. The data were analyzed using one-way and two-way ANOVA and Tukey HSD test with a p<0.05 significance level. RESULTS: There was a statistically significant difference in bond strength between samples with and without APA (p<0.05). There was also a statistically significant difference between the mean values of the two cements (p<0.05), and between samples exposed to thermocycling (p<0.05) as opposed to the samples that were not. The group with the highest shear bond values was (RelyX Universal, No aging, APA) (6.26±1.22 MPa), the lowest shear bond values were observed in (G-CEM ONE, Aged, No APA) group (2.75±0.76 MPa). Regardless of the type of the pretreatment and the brand of the cement, the shear bond strength values of most groups were negatively affected by thermocycling (p<0.05). The most occurred mode of failure was adhesive failure (65.3%), however mixed failure was 25% and the least occurred failure was cohesive (9.7%). CONCLUSION: Air-particle abrasion improved the mean values of the shear bond strength. Thermocycling decreased the shear bond strength of most groups. RelyX Universal cement had a higher shear bond strength than G-CEM ONE cement.
Benzer Tezler
- In- vitro evaluation of shear bond strength of three primer/resin cement systems to monolithic zirconia
Üç tip primer-rezin siman sisteminin monolitik zirkonya ile bağlanma kuvvetinin in vitro değerlendirilmesi
RANIA SALAMA TAWATI SALEM
- Farklı hassasiyet giderici ajanların rezin esaslı simanın dentine bağlantısına etkisinin incelenmesi
Evaluation of the desensitizing agents effect on shear bond strength adhesive resin cement to dentin
MEHMET UĞUR
Diş Hekimliği Uzmanlık
Türkçe
2016
Karadeniz Teknik ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
Yükleniyor...
- Farklı yüzey işlemlerinin rezin simanların seramik materyaline olan bağlantı dayanımı üzerine etkisinin incelenmesi
Evaluation of the effect of different surface treatments on bond strength of the resin cements to the ceramic material
NURAN NOYAN ÖZYÖNEY
- Farklı yüzey işlemlerinin hibrit seramiğin yüzey pürüzlülüğü ve rezin simanların bağlanma dayanımı üzerine etkilerinin değerlendirilmesi
Evaluation of the effects of different surface treatments on the surface roughness and bond strength of resin cements to hybrid ceramics
BUKET YILDIZ
Diş Hekimliği Uzmanlık
Türkçe
2026
Selçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
Yükleniyor...
- Er,Cr:YSGG ve Er:YAG lazer ile hazırlanan dentin yüzeylerine, farklı rezin simanlarla uygulanan seramiklerin bağlanma kuvvetlerinin in-vitro olarak incelenmesi
Evaluation of bond strength of different resin cements used to lute ceramics on Er,Cr:YSGG and Er:YAG laser etched dentin
FİGEN EREN