Sae 10XX (XX=10, 20, 30, 40, 50, 60) çeliklerinde karbon içeriğinin aşınma ve korozyon davranışı üzerindeki etkilerinin taguchi ile incelenmesi

Investigation of the effects of carbon content on wear and corrosion behavior in sae 10xx (XX=10, 20, 30, 40, 50, 60) steels using the taguchi method

PDF İndir

  1. Tez No: 936808
  2. Yazar: ARİF YİĞİT
  3. Danışmanlar: DR. ÖĞR. ÜYESİ ENGİN KOCAMAN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Metalurji Mühendisliği, Mechanical Engineering, Metallurgical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2024
  8. Dil: Türkçe
  9. Üniversite: Zonguldak Bülent Ecevit Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 101

Özet

SBu çalışmada farklı karbon içeriğine sahip SAE 10XX (XX= 10, 20, 30, 40, 50 ve 60) çeliklerinde çeliğin karbon içeriğinin mikroyapı, sertlik, aşınma ve korozyon özellikleri üzerindeki etkisi incelenmiştir. Ayrıca çalışmada aşınma ve korozyon testleri için Taguchi deney tasarımı kullanılmıştır. Bu amaçla SAE 10XX (XX= 10, 20, 30, 40, 50 ve 60) çeliklerine Taguchi L18 ortagonal dizisi kullanılarak bir tasarım yapılmıştır. Aşınma testleri için üç farklı yük (3, 6 ve 9 N), üç farklı mesafe (150, 300 ve 450m) ve üç farklı hız (20,40 ve 60 m/s), seviye ve faktör olarak belirlenmiştir. Korozyon testleri ise üç farklı çözeltide (NaCl, HCl ve NaOH) ve bu çözeltilerin üç farklı konsantrasyonunda (0.1, 0.5 ve 1M) içerisinde gerçekleştirilmiştir. Çalışmada artan karbon miktarı ile mikroyapıdaki perlit miktarı artmış ve buna bağlı olarak sertlikte artışa neden olmuştur. Aşınma test sonuçlarına göre karbon içeriği sürtünme katsayısı ve aşınma oranı üzerinde etkili olmasına rağmen yapılan testlerde en etkili parametre yük faktörü olduğu tespit edilmiştir. Benzer şekilde çelik bileşimindeki karbon içeriği karozyon direnci üzerinde etkili olmasına rağmen farklı çözeltilerde ve derişimlerde gerçekleştirilen korozyon testlerinde en etkili faktör çözelti türü olarak tespit edilmiştir.

Özet (Çeviri)

In this study, the effect of carbon content in SAE 10XX (XX = 10, 20, 30, 40, 50, and 60) steels on the microstructure, hardness, wear, and corrosion properties was investigated. Additionally, the Taguchi experimental design was used for wear and corrosion tests in the study. For this purpose, a design was carried out by using Taguchi L18 orthogonal array for SAE 10XX (XX= 10, 20, 30, 40, 50 and 60) steels. The wear tests were conducted using three different loads (3, 6, and 9 N), three varying distances (150, 300, and 450 m), and three distinct speeds (20, 40, and 60 m/s) as levels and factors. Corrosion tests were carried out in three different solutions (NaCl, HCl and NaOH) and three different concentrations of these solutions (0.1, 0.5 and 1 M). In the study, the amount of pearlite in the microstructure increased with the increasing amount of carbon and caused an increase in hardness accordingly. According to the wear test results, although the carbon content was effective on the friction coefficient and wear rate, the most effective parameter in the tests was determined to be the load factor. Similarly, although the carbon content in the steel composition was effective on corrosion resistance, the most effective factor in the corrosion tests carried out in different solutions and concentrations was determined to be the solution type.

Benzer Tezler

  1. Tez No

    880465

    Kıbrıs'ın uluslaşma sürecinde kimlik arayışındaki bir grup: Sıla 4

    A group in search of identity in Cyprus' nation-building process: Sıla 4

    EREK KIZILÖRS

    Yüksek Lisans

    Türkçe

    Türkçe

    2024

    MüzikDokuz Eylül Üniversitesi

    Müzik Bilimleri Ana Bilim Dalı

    PROF. DR. MEHMET FIRAT KUTLUK

  2. Tez No

    539993

    SAE 4032 dövme çeliğinin mekanik özelliklerine sertleştirme ve kriyojenik işlemlerin etkisinin incelenmesi

    Effect of quenching and cryogenic treatment on forged SAE 4032 steel's mechanical properties

    ERDİNÇ GÜR

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Metalurji MühendisliğiEskişehir Osmangazi Üniversitesi

    Metalurji Mühendisliği Ana Bilim Dalı

    DOÇ. DR. HAKAN GAŞAN

  3. Tez No

    67029

    SAE 8620 çeliğinde gaz sementayon yüzey sertlik derinliğinin eğmeli yorulma mukavemetine etkisi

    Başlık çevirisi yok

    HACI EMİN SÖNMEZ

    Yüksek Lisans

    Türkçe

    Türkçe

    1996

    Makine MühendisliğiSakarya Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. FEHİM FINDIK

  4. Tez No

    67519

    SAE 8620 (DIN 21 cr Ho2) çeliğinde sıvı semantasyonla elde edilen yüzey sertlik derinliğinin eğmeli yorulma mukavemetine etkisi

    Başlık çevirisi yok

    HÜSEYİN ÖZKAYA

    Yüksek Lisans

    Türkçe

    Türkçe

    1996

    MatematikSakarya Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. FEHİM FINDIK

  5. Tez No

    68453

    Investigation of cracks formation in the injection pump camshafts made of caiburized SAE 8620 steel

    SAE 8620 çeliğinden karbonlanmış enjeksiyon pompalarında oluşan çatlakların incelenmesi

    ATİLA KESKİN

    Yüksek Lisans

    İngilizce

    İngilizce

    1997

    Metalurji MühendisliğiOrta Doğu Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. ERDOĞAN TEKİN

Geri Dön