Bulk fill kompozit rezinlere uygulanan ön ısıtma işleminin rezinlerin polimerizasyon derecesi ve monomer salımı üzerine etkisi
The effect of preheating on the degree of conversion and monomer elution of bulk-fill composite resins
- Tez No: 942197
- Danışmanlar: PROF. DR. PINAR GÜL
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Artık monomer, bulk fill kompozit rezin, ön ısıtma, LC-MS/MS, mikro-raman, mikrosertlik, Preheating, bulk-fill composite resin, residual monomer, LC-MS/MS, micro-Raman, microhardness
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Atatürk Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı, ön ısıtma işleminin bulk fill kompozitlerin polimerizasyon derecesi ve salınan artık monomer miktarına etkisini değerlendirmektir. Materyal ve Metot: Bu çalışmada 6 farklı bulk fill kompozit rezin materyalden her bir grupta 10 örnek (5 mm çap ve 4 mm kalınlık) olacak şekilde toplam 60 örnek hazırlanmıştır. Ardından her bir materyal grubu 2 alt gruba ayrılmış, gruplardan birine ön ısıtma işlemi uygulanmış (550C), diğer grup kontrol grubu olarak oda sıcaklığında hazırlanmıştır. Örnekler hazırlandıktan 24 saat sonra örneklerin mikrosertlik ölçümü Vickers test cihazı kullanılarak; polimerizasyon derecesi ise Mikro Raman cihazı kullanılarak analiz edilmiştir. Daha sonra örnekler %75 etanol-su çözeltisinde bekletilmiş ve solüsyon 24 saat sonra yenilenmiştir. Örneklerden salınan artık monomer analizi 24 saat ve 30 günlük periyotlarda incelenmiş ve salınan monomer miktarı Ultra Performans Sıvı Kromatografi-Triple Quadrapol Kütle Spektrometresi (LC-MS/MS) kullanılarak analiz edilmiştir. Elde edilen veriler Paired Samples T Test, Independent Samples T Test, One-way ANOVA ve Tukey çoklu karşılaştırma testleri kullanılarak analiz edilmiştir. p<0.05 değeri istatistiksel olarak anlamlı kabul edilmiştir. Bulgular: Ön ısıtma işleminin bulk fill kompozit rezinlerde polimerizasyon derecesi, polimerizasyon derinliği ve monomer salımına istatistiksel olarak anlamlı bir etkisi bulunamamıştır (p˃0.05). Restoratif materyallerden salınan monomer miktarları 30 günlük periyodda anlamlı oranda azalma göstermiştir (p<0.05).Salınan monomer miktarları açısından restoratif materyaller arasında anlamlı farklılıklar bulunmuştur (p<0.05). Sonuç: Bu çalışmanın limitleri içerisinde ön ısıtma işleminin monomer salımını anlamlı oranda etkilemediği bulunmuştur. Salınan monomer miktarları ise genel olarak toksik limitlerin altındadır.
Özet (Çeviri)
Objective: The aim of this study was to evaluate the effect of preheating on the degree of conversion and residual monomer elution of bulk-fill composite resins. Materials and Methods: In this study, a total of 60 specimens (5 mm in diameter and 4 mm in thickness) were prepared from six different bulk-fill composite resins, with 10 samples per group. Each material group was divided into two subgroups: One subgroup was preheated at 55°C, the other was prepared at room temperature and served as a control. 24 hours after the samples were prepared, the microhardness of the samples was measured using the Vickers tester, and the degree of polymerization was analyzed using the Micro Raman spectrometer. Then, the samples were kept in 75% ethanol-water solution and the solution was renewed after 24 hours. Residual monomer release was evaluated at 24 hours and 30 days using Ultra-Performance Liquid Chromatography coupled with Triple Quadrupole Mass Spectrometry (LC-MS/MS). Data were statistically analyzed using Paired Samples T-Test, Independent Samples T-Test, One-way ANOVA, and Tukey's post-hoc test. p<0.05 considered statistically significant. Results: Preheating had no statistically significant effect on the degree of conversion, polymerization depth, or residual monomer elution in bulk-fill composites (p>0.05). However, the amount of eluted monomer significantly decreased over the 30-day period (p<0.05). Significant differences were also observed among different restorative materials in terms of monomer release (p<0.05). Conclusion: Within the limitations of this study, preheating did not significantly influence residual monomer release. Overall, the levels of eluted monomers remained below toxic thresholds.
Benzer Tezler
- Tekrarlanan ön ısıtma işleminin bulk fill kompozitlerden salınan artık monomer miktarına etkisi
The effect of repeated preheating on monomer elution from bulk fill resin composites
SAMET ATASOY
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiOrdu ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. SERDAR AKARSU
- Ön ısıtma işleminin bulk fill kompozit restorasyonlarda mikrosızıntı üzerine etkisinin in vitro olarak değerlendirilmesi
In vitro evaluation of the effect of preheating on microleakage of bulk fill composite restorations
SULTAN AKTUĞ KARADEMİR
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiOrdu ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SERDAR AKARSU
- Bulk-fill kompozit rezinlere uygulanan farklı ön ısıtma yöntemlerinin pulpal sıcaklık üzerine etkisi
The effect of different preheating methods on the intrapulpal temperature of bulk-fill composite resins
HİLAL ATEŞ
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiAtatürk ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ MERVE İŞCAN YAPAR
- Süt dişlerinde farklı restoratif materyaller ile yapılan inley/onley restorasyonların stres dağılımı
Stress distribution of inlay and onley restorations made with different restorative materials in primary teeth
GÜLÜZAR AKSU
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiOrdu ÜniversitesiPedodonti Ana Bilim Dalı
PROF. DR. ÇİĞDEM GÜLER
- Kompozit tamir zamanı tamir protokolünü etkiler mi? Hemen veya gecikmiş
Does composite repair time affect repair protocol? Immediate or delayed
MURAT CAN ERŞEN
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiSelçuk ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. NEVİN ÇOBANOĞLU