Biyoseramik pulpa kaplama materyallerinin antimikrobiyal özelliklerinin in vitro olarak incelenmesi
In vitro analysis of the antimicrobial activity of bioceramic pulp capping materials
- Tez No: 943859
- Danışmanlar: PROF. DR. OYA AKTÖREN
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: pulpa kaplama materyali, antimikrobiyal etkinlik, direkt kontakt test, pulp capping material, antimicrobial activity, direct contact test
- Yıl: 2025
- Dil: Türkçe
- Üniversite: İstanbul Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Pedodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışma, biyoseramik pulpa kaplama materyallerinin antimikrobiyal etkinliklerinin farklı periyodlarda incelenmesi amacı ile gerçekleştirildi. Gereç ve Yöntem: NeoPuttyMTA (Nusmile,ABD), TheraCalPT (Bisco,ABD), Biodentine (Septodont,Fransa), Dycal (Dentsply,ABD) pulpa kaplama materyallerinin (n:18) Enterococcus faecalis, Streptococcus mutans, Lactobacillus casei suşlarına karşı antibakteriyel etkileri 0.,1.,3.,7. günlerde 18 saat süresince 1 saat aralıklarla direkt kontakt test ile spektrofotometrede incelendi; optik yoğunluk ölçümleri kaydedildi. Elde edilen bulgular Shapiro-Wilk, Robust ANOVA, Bonferroni testleri ile IBM SPSS v23'de analiz edildi. Bulgular: Enterococcus faecalis'e karşı antibakteriyel etkinlik; tüm günlerde en yüksek Biodentine (p<0,05), 0.,1.7. günlerde en düşük Dycal ile saptandı. Enterococcus faecalis'e karşı 0.,1. günlerde gözlenen antibakteriyel etkinliğin 3.,7. günlerde NeoPutty MTA grubunda azaldığı, TheraCalPT grubunda arttığı belirlendi. Streptococcus mutans'a karşı en yüksek antibakteriyel etkinlik 0.günde Dycal, 1.,3. günlerde TheraCal PT (p<0,05), 7. günde Biodentine (p<0,05) ile elde edildi. Dycal'ın Streptococcus mutans'a karşı etkisinin zamanla azalarak 7.günde en düşük (p<0,05), Biodentine'in etkisinin ise zamanla artarak 7. günde en yüksek (p<0,05) etkiyi oluşturduğu görüldü. Streptococcus mutans'a karşı 1.,3. günlerde gözlenen antibakteriyel etkinliğin; 7. günde TheraCalPT grubunda azaldığı, NeoPuttyMTA grubunda ise arttığı belirlendi. Lactobacillus casei'e karşı en yüksek antibakteriyel etkinlik 0.,1.günde NeoPuttyMTA ve 3.,7.günde Theracal PT ile elde edildi. Lactobacillus casei'e karşı 0.günde NeoPuttyMTA'ın Dycal ve TheraCalPT'e, 3.,7.günlerde TheraCalPT'nin NeoPuttyMTA, Dycal, Biodentine'e göre yüksek (p<0,05) antibakteriyel etki gösterdiği; Lactobacillus casei'e karşı antibakteriyel etkinliğin TheracalPT grubunda zaman ile artarken NeoPuttyMTA grubunda azaldığı gözlendi. Sonuç: Çalışmada değerlendirilen tüm pulpa kaplama materyallerinin Enterococcus faecalis, Streptococcus mutans, Lactobacillus casei'e karşı 0.,1.,3.,7. günlerde antimikrobiyal etkinlik gösterdiği; materyallerin etkinliğinin ise zamana bağlı olarak farklı özellikler sergilediği belirlendi.
Özet (Çeviri)
Purpose: The aim of this study was to evaluate the antimicrobial effects of bioceramic pulp capping materials at different time intervals. Materials and Methods: The pulp capping materials, NeoPutty MTA (Nusmile,USA), TheraCal PT (Bisco,USA), Biodentine (Septodont,France), Dycal (Dentsply,USA), were assessed for antibacterial efficacy against Enterococcus faecalis, Streptococcus mutans, Lactobacillus casei strains at 0,1,3,7 days by direct contact test; optical density values were recorded hourly for 18 hours using spectrophotometry. Data were analyzed by Shapiro-Wilk, Robust ANOVA, Bonferroni tests (IBM SPSS v23). Results: Biodentine exhibited the highest antibacterial effect against Enterococcus faecalis at all days (p<0,05) whereas Dycal showed the least activity at days 0,1,7. NeoPuttyMTA's efficacy against Enterococcus faecalis at days 0,1 decreased at days 3,7 while TheraCalPT's was increased. Highest efficacies against Streptococcus mutans were observed at days 0, 1-3,7, respectively, with Dycal, TheraCal PT(p<0,05), Biodentine (p<0,05). Dycal's effect against Streptococcus mutans decreased by time; at day 7, Dycal showed the least, Biodentine exhibited the highest effect against Streptococcus mutans (p<0,05). TheraCalPT's efficacy against Streptococcus mutans at days 1,3 decreased at day 7 whereas NeoPuttyMTA's increased. Highest activities against Lactobacillus caseiwas recorded with NeoPuttyMTA at days 0,1 and with TheraCalPT at days 3,7. TheraCalPT showed higher activity against Lactobacillus caseiat 3,7 days (p<0,05) than other materials; TheraCalPT's effect against Lactobacillus caseincreased with time whereas NeoPuttyMTA's efficacy decreased. Conclusion: All pulp-capping materials evaluated in this study exhibited antimicrobial activities against Enterococcus faecalis, Streptococcus mutans, Lactobacillus caseistrains at days 0,1,3,7; however, the materials presented time-dependent antimicrobial properties.
Benzer Tezler
- Biyoseramik materyallerin sitotoksisite ve biyoaktivite düzeylerinin insan dental pulpa hücrelerinde incelenmesi
“investigation of the cytotoxicity and bioactivity levels of bioceramic materials in human dental pulp cells”
MÜGE ALI METİNER
- Farklı apikal foramen boyutlarına sahip köklerde, guta perka ve biyoseramik esaslı pat ile yapılan üç dolum tekniğinin apikal sızıntı düzeyleri üzerine etkisi
Effect of three filling techniques using gutta-percha and bioceramic-based sealer on apical leakage levels in roots with different apical foramen sizes
ESMA DİNGER
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiZonguldak Bülent Ecevit ÜniversitesiEndodonti Ana Bilim Dalı
PROF. DR. EMRE BODRUMLU
- Kök kanal duvarlarından kök kanal dolgu materyallerinin uzaklaştırılması sırasında kullanılan farklı aktivasyon sistemlerinin etkinliklerinin karşılaştırılması
Comparison of the efficacy of different activation systems for removal of root canal filling materials from root canal walls
ZEYNEP SENA GÜNGÖRDÜ
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiHatay Mustafa Kemal ÜniversitesiEndodonti Ana Bilim Dalı
DOÇ. DR. PELİN TÜFENKÇİ
- Furkasyon perforasyonlarında kullanılan dört farklı biyoseramik içerikli materyalin porözitelerinin mikro-bt ile değerlendirilmesi
Porosity analysis of four different bioceramic materials used in furcation perforations by micro-ct
HATİCE YALNIZ
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiAnkara ÜniversitesiEndodonti Ana Bilim Dalı
PROF. DR. FATMA GÜL ZIRAMAN
- Biyoseramik esaslı dental materyallerin genotoksisite ve biyoaktivite özellikleri ile alkalen fosfataz aktivitesinin incelenmesi
Evaluation of the genotoxicity, bioactivity and alp activity of bioceramic based dental materials
MERVE ESEN
Doktora
Türkçe
2020
Diş Hekimliğiİstanbul ÜniversitesiPedodonti Ana Bilim Dalı
PROF. DR. ELİF BAHAR TUNA İNCE