Akışkan kompozit rezinlere balık (Gökkuşağı alabalığı, Oncorhynchus mykiss) kemiği tozu katkılanmasının polimerizasyon büzülmesi ve mekanik özelliklere etkisi
The impact of incorporating fish bone powder (Rainbow trout, Oncorhynchus mykiss) into flowable composite resins on polymerisation shrinkage and mechanical properties
- Tez No: 960491
- Danışmanlar: DOÇ. DR. EMİNE ŞİRİN KARAARSLAN, DOÇ. DR. HÜSEYİN HATIRLI
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Atık yönetimi, hidroksiapatit, mikrosertlik, büzülme, bükülme dayanımı, Waste management, hydroxyapatite, microhardness, shrinkage, flexural strength
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Tokat Gaziosmanpaşa Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Restoratif Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı ülkemizde yetiştiriciliği ve ihracatı yapılan gökkuşağı alabalığı iskeletinden elde edilen kemiğin, işlenerek nano boyutlu hidroksiapatit tozuna getirilmesi ve ticari dental akışkan kompozite farklı oranlarda inorganik doldurucu olarak katkılanmasının kompozit rezinin mekanik özellikleri üzerindeki etkilerinin değerlendirilmesidir. Gereç ve Yöntemler: Bu çalışmada atık alabalık kılçığı tozundan elde edilen inorganik nano-doldurucuların farklı oranlarda bir akışkan kompozite (İmicryl, Konya) eklenmesinin kompozit rezinin polimerizasyon büzülmesine, sertlik ve eğilme dayanımı özelliklerine etkisi değerlendirildi. Akerko Su Ürünleri (Trabzon) işleme tesisinde işleme sonrası ortaya çıkan alabalık atıkları toplandı. Bu atıklar Tarsus Üniversitesi Kimya Prog. Laboratuvarı'nda işlendi ve inorganik matriks nano-hidroksiapatit doldurucular elde edildi. Ticari bir akışkan kompozitin organik doldurucu oranı sabit tutularak, inorganik doldurucusuna farklı oranlarda elde ettiğimiz nano-hidroksiapatit eklendi. Kontrol gurubu dahil olmak üzere 5 deneysel grup değerlendirildi. Polimerizasyon büzülmesinin değerlendirilmesi için 50 adet örnek yarım küre şeklinde hazırlandı (n=10) ve Acuvol (Bisco, Schaumburg, IL, ABD) ile hacimsel büzülme oranı ölçüldü. Mikrosertlik ölçümü için 8 mm çap ve 2mm kalınlığında disk şeklinde 50 adet örnek hazırlandı (n=10) ve mikrosertlik test cihazı (HWDM-5,TTS Unlimited Inc., Osaka, Japonya) ile Vickers sertlik değeri (VHN)(kg/mm2) belirlendi. Biaksiyel bükülme testi için 12 mm çapında, 1.2 kalınlıkta disk şeklinde 50 örnek hazırlandı (n=10) ve üniversal test cihazı (Shımadzu, Kyoto, Japonya) ile test tamamlandı. Kompozit rezin örneklerin yüzey özellikleri Taramalı Elektron Mikroskobu (JEOL JSM 7001F, Japonya) ile elde edilen görüntüler üzerinden analiz edildi. Verilerin istatistiksel analizleri SPSS v.19 paket programı (SPSS Inc, IBM Corp, IL,ABD) kullanılarak yapıldı. Analizlerde tek yönlü Varyans Analizi (ANOVA) ve post-hoc Tukey HSD testleri kullanıldı(p˂0,05). Bulgular: Mikrosertlik değerlendirmesinde, en yüksek değer %10 nano-hidroksiapatit katkılı 3.grupta görülmüştür (p<0,05). Polimerizasyon büzülmesi değerlendirilmesinde, en düşük hacimsel büzülme gösteren grup %60 nano-hidroksiapatit katkılı 5. grupta görülmüştür (p<0,05). Bükülme dayanımı değerlendiğimizde, en yüksek dayanım nano-hidroksiapatit eklemediğimiz kontrol grubunda görülmüştür (p<0,05). SEM analizi ile örneklerin yüzeyel analizi sonucunda, %10 ve üzeri nano-hidroksiapatit katkısında malzemede topaklanma görülmüştür. Sonuç: Atık malzemelerden nano-hidroksiapatit elde edilebilir ve ekonomiye kazandırılabilir. Nano-hidroksiapatit eklenmiş kompozit rezinler mekanik özellikleri bakımından farklılık göstermiştir.
Özet (Çeviri)
Objective: The aim of this study is to evaluate the effects of the bone obtained from the skeleton of rainbow trout, which is cultivated and exported in our country and then processed into nano-sized hydroxyapatite powder. The powder is then added to commercial dental fluid composite as an inorganic filler at different ratios. This is done to ascertain the effect on the mechanical properties of the composite resin. Materials and methods: This study evaluated the effect of adding inorganic nano-fillers obtained from waste trout bone powder to a flowable composite (Imicryl, Konya) at different ratios on the polymerisation shrinkage, hardness, and flexural strength of the composite resin. The trout waste generated by the Akerko Su Ürünleri processing plant in Trabzon was collected. These wastes were processed at the laboratory of Tarsus University's Chemistry Programme to obtain inorganic nano-hydroxyapatite fillers. The ratio of the organic filler in a commercial fluid composite was kept constant, with different ratios of nano-hydroxyapatite added to the inorganic filler. Five experimental groups including the control group were evaluated. Five experimental groups, including the control group, were evaluated. To evaluate polymerisation shrinkage, 50 samples were prepared as hemispheres (n = 10), and the volumetric shrinkage rate was measured using an Acuvol (Bisco, Schaumburg, IL, USA). For microhardness measurement, 50 disc-shaped samples (n=10) with a diameter of 8 mm and a thickness of 2 mm were prepared and the Vickers hardness value (VHN) (kg/mm2) was determined with a microhardness tester (HWDM-5, TTS Unlimited Inc., Osaka, Japan). For the biaxial bending test, 50 specimens (n = 10) were prepared as 12 mm diameter, 1.2 mm thick discs, and the test was performed using a universal testing machine (Shimadzu, Kyoto, Japan). The surface properties of the composite resin specimens were analysed using scanning electron microscopy (JEOL JSM 7001F, Japan). Statistical analyses of the data were performed using SPSS v.19 package programme (SPSS Inc, IBM Corp, IL, USA). One-way Analysis of Variance (ANOVA) and post-hoc Tukey HSD tests were used in the analyses (p˂0.05). Results: In the microhardness evaluation, the highest value was observed in the 3rd group with 10% nano-hydroxyapatite additive (p<0.05). In the polymerisation shrinkage evaluation, the lowest volumetric shrinkage was observed in the 5th group with 60% nano-hydroxyapatite additive (p<0.05). When the bending strength was evaluated, the highest strength was observed in the control group in which nano-hydroxyapatite was not added (p<0.05). Superficial analysis of the samples by SEM revealed agglomeration in the material containing 10% or more nano-hydroxyapatite additives. Conclusion: Nano-hydroxyapatite can be obtained from waste materials and is economical to produce. Composite resins containing nano-hydroxyapatite exhibited differences in mechanical properties.
Benzer Tezler
- Katı yakıtların akışkan yatakta yakılması ve katı miktarının yatak yüksekliğine etkisi
Combustion of solid fuels in the fkuidized beds and the effects of solid quantity to the height of bed
KAMİL BEKİR KOÇ
Yüksek Lisans
Türkçe
1987
Makine MühendisliğiGazi ÜniversitesiMakine Eğitimi Ana Bilim Dalı
YRD. DOÇ. DR. ALİ YÜCEL UYAREL
- Isparta iline bağlı Senirkent ilçesi ve köylerinde ilkokul çocuklarının beslenme durumları üzerinde bir araştırma
A Research on nutritional status of primary school children in Isparta-Senirkent town and its villages
AYŞE ÖZFER ÖRMECİ
Yüksek Lisans
Türkçe
1987
Ev EkonomisiAnkara ÜniversitesiEv Ekonomisi Ana Bilim Dalı
DOÇ.DR. SENİHA HASİPEK
- Ekseni salınım eksenine paralel olarak salınım yapan dairesel kesitli borularda ısı transferinin deneysel olarak incelenmesi
Başlık çevirisi yok
HASAN GÜL
Yüksek Lisans
Türkçe
1987
Makine MühendisliğiKaradeniz Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. TEOMAN AYHAN
- Bursa ve İstanbul illerinde derin dondurma yöntemi ile sebze ve meyve muhafaza eden tesislerin uyguladığı yöntemler ve sorunları
Başlık çevirisi yok
ŞENEL USLU
Yüksek Lisans
Türkçe
1987
Gıda MühendisliğiUludağ ÜniversitesiTarım Ürünleri Teknolojisi Ana Bilim Dalı
YRD. DOÇ. DR. FİKRİ BAŞOĞLU