Plasticizing and superplasticizing agents and their effects on strength and workability of concrete

Başlık çevirisi mevcut değil.

  1. Tez No: 9617
  2. Yazar: CUMHUR NALCIOĞLU
  3. Danışmanlar: PROF. DR. TURHAN Y. ERDOĞAN
  4. Tez Türü: Yüksek Lisans
  5. Konular: İnşaat Mühendisliği, Civil Engineering
  6. Anahtar Kelimeler: Akışkanlaştırıcı, Süper akışkanlaştırıcı îşlenebilirlik, Beton, Plasticizer, Superplasticizer, Concrete, Workability
  7. Yıl: 1990
  8. Dil: İngilizce
  9. Üniversite: Orta Doğu Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 87

Özet

AKIŞKANLANTIRICI VE SÜPERAKIŞKANLAŞTIRICI KATKI MALZEMELERİ VE BETONUN ÎŞLENEBILİRLÎK VE MUKAVEMETİ ÜZERİNDEKİ ETKİLERİ Nalcıoğlu, Cumhur Mühendislik Fakültesi inşaat Mühendisliği Bölümü, Yüksek Lisans Tezi Tez Yöneticisi: Prof. Dr- Turhan Y. Erdoğan 76 Sayfa, Ocak 1990 ÖZET Bu çalışma akışkanlaştı rıcı katkıların betonun mekanik özellikleri üzerindeki etkilerini gözlemek için yapılmıştır. Akışkanlaştırıcı katkı maddesinin eklenmesi çimento parçacıklarının ve hidrasyonun ilk ürünleri üzerinde ince bir tabaka oluşturur. Parçacıkların normal temasından kaynaklanan sürtünme kuvveti ve parçacıklar arasındaki çekim azalır, dolayısıyla sistem daha iyi ayrışmış ve daha akışkan bir hal alır. Yukarıda sıralanmış olan nedenlerden dolayı, akışkanlaştırıcı katkının eklenmesi ile beton karışımın işlenebilirliği artar. Beton karışımın işlenebilirliği sabit tutulduğu takdirde karışımın suyunda önemli oranda azalma olur. Su çimento oranındaki bu azalma beton mukavemetinde artışa neden olur. ıııBu laboratuvar çalışmasında biri akışkanlaştırıcı“ diğeri süperakışkanlaştırıcı olmak üzere iki değişik katkı maddesi kullanılmıştır. Bunlar ”Sikament“ ve ”Plastiment BV-40" isimli ticari katkı malzemeleridir. Basınç ve eğilmede çekme deneyleri sonucunda olumlu sonuçlar alabilmek için üretici tarafından önerilen en yüksek oranda kullanılmaları gerektiği gözlemlenmiştir.

Özet (Çeviri)

PLASTICIZING AND SUPERPLASTICIZING AGENTS AND THEIR EFFECTS ON STRENGTH AND WORKABILITY OF CONCRETE Nalcıoğlu Cumhur Faculty of Engineering Department of Civil Engineering M.S. Thesis Supervisor: Prof. Dr. Turhan Y. Erdoğan 76 pages, January 1990 ABSTRACT This study was made to determine the effects of plasticizing admixtures on the mechanical properties of concrete. Addition of plasticizing agent in to the concrete mixture forms a thin layer of admixture molecules on the surface of the cement particles and on the very first products of hydration. The ordinary contacts of friction and adhesion between cement particles and thus blocked, or more or less reduced, and the system of particles becomes better dispersed and more fluid. Because of the above listed reasons addition of superplasticizing agent increases the workability of the mix, also if the workability of the concrete mix is kept constant this results a significant decrease in mixing water. Because the water cement ratio is decreased this causes a relative increase on the strength of the hardened concrete.For this experimental study one plasticizing and one superplasticizing agent were selected. These agents were commercial admixtures with trade names of“ Plastiment BV-40' and ”Sikament". The resulting compressive and flexural strength tests performed, reveals that in order to obtain satisfactory results, manufactures' maximum recommended amounts of admixtures must be used in the concrete mixes.

Benzer Tezler

  1. The Effects of a plasticizing and a superplasticizing agents on water-cement ratio and compressive strength of concretes

    Başlık çevirisi yok

    ALİ DAŞÇI

    Yüksek Lisans

    İngilizce

    İngilizce

    1990

    İnşaat MühendisliğiOrta Doğu Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. MUSTAFA TOKYAY

  2. Farklı dayanımlı bazı özel betonlar ile geleneksel betonun gerilme-şekil değiştirme davranışlarının karşılaştırılması

    Comparison of exercise conventional concrete stress-shape replacement excitations of normal and high strengthen special concrete

    TOKHIRI KAMOLZODA

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    İnşaat MühendisliğiAtatürk Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. REMZİ ŞAHİN

  3. Aljinat filmlerinde dış çapraz bağlama ve gliserin katkısının yapı ve fiziksel özelliklere etkileri

    Effect of calcium crosslinking and glycerol plasticizing in alginate films

    MELİSA BERBEROĞLU

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Kimyaİstanbul Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. HATİCE HÜCESTE GİZ

  4. Yeni bir kitosan esaslı süperplastikleştiricinin sentezi ve çimento hamurundaki etkinliğinin araştırılması

    Synthesis of a new kitosan based superplasticizer and investigation of its efficiency on cement paste

    UĞUR SEMİH AYTAÇ

    Yüksek Lisans

    Türkçe

    Türkçe

    2017

    KimyaBülent Ecevit Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. ŞADİ ŞEN

    PROF. DR. HÜLYA ARSLAN

  5. Kenevir dolgulu polipropilen kompozitlerin hazırlanması ve reolojik özelliklerinin incelenmesi

    Preparation of hemp filled polypropylene (PP) composites andinvestigation of their rheological properties

    ÜMMÜHAN YALMAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Kimya Mühendisliğiİstanbul Üniversitesi-Cerrahpaşa

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. İSMAİL AYDIN