Poli(fenilen oksit)/poli(bütilen adipat tereftalat) karışımlarının hazırlanması ve cam elyaf takviye edilerek termal, mekanik ve morfolojik özelliklerinin incelenmesi
Preparation of poly(phenylene oxide)/poly(butylene adipate terephthalate) mixtures and examination of thermal, mechanical and morphological properties by reinforcement with glass fiber
- Tez No: 976092
- Danışmanlar: DOÇ. DR. HÜSEYİN ESEN
- Tez Türü: Yüksek Lisans
- Konular: Polimer Bilim ve Teknolojisi, Polymer Science and Technology
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Kocaeli Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Polimer Bilim ve Teknolojisi Ana Bilim Dalı
- Bilim Dalı: Polimer Bilim ve Teknolojisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Polimer harmanları, farklı fiziksel ve mekanik özelliklere sahip yeni malzemeler elde etmek için iki veya daha fazla polimerin fiziksel olarak karıştırılmasıyla oluşturulur. Polimer harmanlama, istenen nihai özelliklere ve daha iyi işlenebilirliğe sahip yeni malzemeler geliştirmenin uygun maliyetli bir yoludur. Çeşitli uygulamalarda istenen özellikleri karşılamak için özel bileşimlerde tasarlanabilirken, polimerler tek başına sınırlı sayıda uygulamayla kendilerine has özellik profillerine sahiptir. Polifenilen eter (PPE) olarak da bilinen polifenilen oksit (PPO), yüksek mukavemeti, yüksek ısıl bozulma sıcaklığı ve yüksek kimyasal direnci nedeniyle en önemli mühendislik plastiklerinden biri olan amorf polimerlerden biridir. Yüksek mekanik özellik, düşük nem emme, mükemmel elektrik yalıtım özelliği, mükemmel boyut kararlılığı ve doğal alev direncinin benzersiz birleşimi nedeniyle PPO, geniş bir uygulama yelpazesinde yaygın olarak kullanılmaktadır. Fakat fenolik monomerlerden oluşan poli(fenilen oksit) (PPO) reçineleri çok yüksek bir camsı geçiş sıcaklığına (Tg) sahiptir. 200 °C'nin üzerindeki Tg ile saf PPO'nun işlenmesi çok zordur; 255 °C'nin altında erime başlamaz. 300–350 °C'lik ekstrüzyon veya enjeksiyonlu kalıplama sıcaklığında, eriyik akışı çok serttir. Bundan dolayı, farklı polimerlerle karışım yapılarak kullanılmaktadır. Öte yandan PBAT, fosil kaynaklara dayanan, %100 biyolojik olarak parçalanabilen, kopma uzaması yüksek ve çok esnek olan sentetik bir polimerdir. Bu nedenlerden dolayı PPO'nun proses edilebilirliğini kolaylaştırmak ve biyobozunurluğunu artırmak için PBAT ile çift vidalı ekstrüderde uyumlaştırıcılar kullanarak yeni bir ürün elde edilmesi düşünülmüştür. Bu çalışmada da PBAT ve PPO gibi farklı yapıdaki iki polimer uyumlu hale getirilerek mekanik, termal ve morfolojik özellikleri incelenmiştir.
Özet (Çeviri)
Polymer blends are prepared by physically mixing two individual polymers to obtain new properties. This process is an affordable and suitable way to create a polymer blend that offers decent processability. Polyphenylene ether (PPE), also known as polyphenylene oxide (PPO), is one of the amorphous engineering plastics with unique properties such as high modulus, high decomposition temperature, and high chemical resistance. PPO has found a wide range of applications due to its outstanding mechanical properties, very low moisture absorption, excellent dimensional stability, electrical insulation, and inherent flame resistance. However, due to its phenolic monomeric nature, these polymers have high glass transition temperatures. With a Tg over 200 °C, pure PPO is very difficult to process. It does not melt below 255 °C and exhibits very low melt flow during extrusion or injection molding at 300–350 °C. That's why PPO is often blended with other polymers. On the other hand, PBAT is a 100% biodegradable, fossil-based polymer with very high elongation at break and excellent flexibility. For all the reasons stated above, to improve the processability of PPO and to increase the biodegradability of PPO-based products, it is planned to blend it with PBAT along with auxiliary chemicals using twin-screw extrusion. The mechanical, thermal, and morphological properties of the two different polymers PBAT and PPO are examined.
Benzer Tezler
- Farklı uyumlaştırıcıların indirgenmiş grafen oksit takviyeli poli (Etilen teraftalat)/poli (Bütilen eraftalat) nanokompozitlerinin özelliklerine etkisi
The effect of different compatilizer on the properties ofreduced graphene oxide reinforced poly (Ethyleneteraftalate)/poly (Butylened teraftalate) nanocomposites
CANAN ÖZTÜRK
Yüksek Lisans
Türkçe
2020
Polimer Bilim ve TeknolojisiKocaeli ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
DOÇ. DR. AYŞE AYTAÇ
- Çeşitli polimer-polimer karışımlarının ters gaz kromatografi, viskozite ve iletkenlik metodlarıyla karekterizasyonu
Characterization of various polymer-polymer mixtures by inverse gas chromatography, viscosity and conductivity methods
FATİH ÇAKAR
- Synthesis of some functional conducting polymers, characterization, Mott-Schottky analysis and sensor applications
Bazı fonksiyonel iletken polimerlerin sentezi, karakterizasyonu, Mott-Schottky analizi ve sensor uygulamaları
TOLGA KARAZEHİR
Doktora
İngilizce
2017
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. ABDÜLKADİR SEZAİ SARAÇ
PROF. DR. MURAT ATEŞ
- Poli(fenilen oksit)'in fraksiyonlandırılması ve molekül ağırlığı dağılımının incelenmesi
Fractionation of poly(phenylene oxide) and investigation of molecular weight distribution
YASEMİN KİŞMİR
- Bisfenol A'nın tereftalik ve izoftalik asit kopoliesteri ile poli(2,6-dimetil-1,4-fenilen oksit)'in ve karışımlarının çeşitli yöntemlerle incelenmesi
An investigation of a copolyester of bisphenol-A with terepthalic acids and poly(2,6-dimethyl-1,4-phenylene oxide) and their mixtures by various methods
DOLUNAY ŞAKAR