Monolitik zirkonya materyallerinin farklı sinterleme parametrelerinde optik ve mekanik özelliklerinin değerlendirilmesi
Effect of sintering conditions on the optical and mechanical properties of monolithic zirconia
- Tez No: 1008163
- Danışmanlar: PROF. DR. GÖKHAN AKGÜNGÖR
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: CAD/CAM, Mekanik dayanım, Zirkonya, CAD/CAM, Mechanical strength
- Yıl: 2026
- Dil: Türkçe
- Üniversite: İstanbul Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tez çalışmasında, farklı üreticilere ait üç çok katmanlı monolitik zirkonya materyalin (IPS e.max ZirCAD Prime [3Y/5Y-TZP], Katana Zirconia YML [4Y/5Y-TZP] ve VITA YZ/ST Multicolor [4Y-TZP]) standart ve hızlı sinterleme protokolleri sonrası optik ve mekanik özellikleri karşılaştırmalı olarak değerlendirilmiştir. Amaç sinterleme süresi ve materyal kompozisyonunun translüsentlik parametresi (TP) ve biaksiyel kırılma dayanımı üzerindeki etkisini belirlemektir. CAD/CAM sistemi ile hazırlanan disk şeklindeki örnekler, üretici talimatlarına uygun olarak standart ve hızlı sinterleme protokollerine tabi tutulmuştur. Optik analizde, her örneğin kole ve insizal bölgelerinden siyah ve beyaz arka plan üzerinde VITA EasyShade V spektrofotometre ile CIE L*, a*, b* değerleri ölçülmüş ve TP değerleri hesaplanmıştır. Mekanik değerlendirme üç top üzerinde piston yöntemiyle gerçekleştirilen biaksiyel bükülme testi ile yapılmıştır. Veriler uygun istatistiksel analiz yöntemleri kullanılarak değerlendirilmiş ve anlamlılık düzeyi p<0,05 olarak kabul edilmiştir. Bulgular, sinterleme protokolünün mekanik dayanım üzerinde anlamlı bir etkisi olmadığını, ancak hızlı sinterlemenin tüm materyallerde translüsentlik değerlerini istatistiksel olarak anlamlı düzeyde azalttığını göstermiştir (p<0.05). Markalar arasında hem translüsentlik hem de kırılma dayanımı açısından anlamlı farklılıklar saptanmıştır. ZirCAD Prime ve VITA grupları Katana'ya kıyasla daha yüksek kırılma dayanımı göstermiştir. Tüm materyallerde insizal bölge, kole bölgesine göre daha yüksek translüsentlik değerleri sergilemiştir. Sonuç olarak, hızlı sinterleme klinik açıdan zaman kazandıran bir yöntem olmakla birlikte optik özelliklerde sınırlı bir azalmaya yol açmaktadır. Çok katmanlı zirkonya sistemlerinde kimyasal kompozisyon ve faz dağılımı, optik ve mekanik performans üzerinde belirleyici rol oynamaktadır.
Özet (Çeviri)
In this study, the optical and mechanical properties of three multilayered monolithic zirconia materials from different manufacturers (IPS e.max ZirCAD Prime [3Y/5Y-TZP], Katana Zirconia YML [4Y/5Y-TZP], and VITA YZ/ST Multicolor [4Y-TZP]) were comparatively evaluated after conventional and speed sintering protocols. The aim was to determine the effect of sintering duration and material composition on the translucency parameter (TP) and biaxial flexural strength. Disc-shaped specimens prepared using a CAD/CAM system were sintered according to the manufacturers' recommendations under conventional and speed sintering protocols. For optical analysis, CIE L*, a*, and b* values were measured from the cervical and incisal regions of each specimen against black and white backgrounds using a VITA EasyShade V spectrophotometer, and TP values were calculated. Mechanical evaluation was performed using a piston-on-three- ball biaxial flexural strength test. Data were analyzed using appropriate statistical methods, and the level of significance was set at p<0.05. The results showed that the sintering protocol had no significant effect on mechanical strength; however, speed sintering significantly reduced translucency values in all materials (p<0.05). Significant differences were observed among the brands in terms of both translucency and fracture strength. ZirCAD Prime and VITA groups demonstrated higher fracture strength compared to Katana. In all materials, the incisal region exhibited higher translucency values than the cervical region. In conclusion, although speed sintering offers clinical time efficiency, it leads to a limited reduction in optical properties. The chemical composition and phase distribution in multilayered zirconia systems play a decisive role in determining their optical and mechanical performance.
Benzer Tezler
- Tekrarlanan fırınlamanın farklı tip yüksek translusens monolitik zirkonya materyallerinin translusensi ve iki eksenli bükülme dayanımına olan etkisi
Effect of repeated firing on the translucency and biaxial flexural strength of different types of high translucency monolithic zirconia materials
SEDA YILDIZLAR
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. TUBA YILMAZ SAVAŞ
- Sinterleme parametrelerindeki değişikliklerin monolitik translusent zirkonya özellikleri üzerine etkilerinin değerlerndirilmesi
Evaluation of the effects of sintering parameters on properties of monolithic translucent zirconia
CANER ÖZTÜRK
Doktora
Türkçe
2017
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. GÜLŞEN CAN
- Farklı sinterleme durumlarının monolitik zirkonya materyalinin optik özelliklerine etkisi
Effect of different sintering situations on optical characteristics of monolithic zirconia
AYŞEGÜL ATİLLA
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiBolu Abant İzzet Baysal ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. HAMİYET KILINÇ
- Farklı bar altyapılı monolitik zirkonya all-on-four protezlerin kırılma dayanımlarının karşılaştırılması
Comparison of fracture resistance of monolithic zirconia all-on-four prostheses with different bar substructures
İREM SARKAYA
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş Hekimliğiİnönü ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ NAGEHAN BAKİ
DR. ÖĞR. ÜYESİ MESUT TUZLALI
- Niyobyum içerikli tam sinterize ve yüksek hızlı sinterleme protokolü uygulanan yarı sinterize monolitik zirkonya materyallerinde hidrotermal yaşlandırmanın eğilme dayanımı ve translusensi üzerine etkisi
The effect of hydrothermal aging on flexural strength and translucency in niobium containing fully sintered and high speed sintered protocol applied partially sintered monolithic zirconia materials
SERVET GÜLSÜM CEYLAN
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiAydın Adnan Menderes ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. MUSA ŞAMİL AKYIL