Tekrarlanan fırınlamanın farklı tip yüksek translusens monolitik zirkonya materyallerinin translusensi ve iki eksenli bükülme dayanımına olan etkisi
Effect of repeated firing on the translucency and biaxial flexural strength of different types of high translucency monolithic zirconia materials
- Tez No: 828623
- Danışmanlar: DOÇ. DR. TUBA YILMAZ SAVAŞ
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: tekrarlanan fırınlama, monolitik zirkonya, bükülme dayanımı, translusensi, CAD/CAM, Dental materyaller, Dental stres analizi, Fırınlama, Mikroskopi-elektron taramalı, Zirkonyum, repeated firing, monolithic zirconia, flexural strength, translucency, CAD/CAM, Dental materials, Dental stress analysis, Firing, Microscopy-electron scanning, Zirconium
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Selçuk Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu in vitro çalışmanın amacı; tekrarlanan fırınlamanın üç farklı yüksek translusens 4Y-TZP monolitik zirkonya materyalinin translusens parametresi (TP00) ve iki eksenli bükülme dayanımına olan etkisinin incelenmesidir. Toplam 180 adet disk şeklindeki (14,00- 0,01 mm çap ve 1,20 -0,01 mm kalınlık) örnek üç farklı (Vita YZ/ST, Katana STML ve DD Cube ONE/ML) monolitik zirkonya materyalinden bilgisayar destekli tasarım – bilgisayar destekli üretim (CAD-CAM) ile üretildi. Hazırlanan numunelere üretici firma talimatları doğrultusunda sinterleme işlemi yapıldı. Her bir zirkonya materyaline üretici firmanın talimatları doğrultusunda glaze uygulandı. Ardından örnekler ek fırınlama işlemine göre rastgele 4 alt gruba ayrıldı (n=15): Kontrol grubu (T1), 2. fırınlama grubu (T2), 3. fırınlama grubu (T3) ve 5. fırınlama grubu (T5). Ardından tüm örnekler distile suda 10 dk boyunca ultrasonik temizleyici ile temizlendi. Örneklerin Commission Internationale de I' Eclairage (CIE) L*, a* ve b* renk koordinatları dental bir spektrofotometre ile siyah ve beyaz arka planlar kullanılarak ölçüldü ve TP00 değerleri hesaplandı. Örneklerin iki eksenli bükülme dayanımı üç top üzerinde piston testi ile yapıldı. Örneklere ISO 6872 standartlarına göre üniversal bir test cihazında kırılma olana kadar 1mm/dak yük uygulandı. Grupların içinden rastgele seçilen birer örnek taramalı elektron mikroskobu (SEM) ile analiz edildi. Tüm gruplardaki tetragonal-monoklinik faz dönüşümü değerlendirilmesi X ışını kırınımı (XRD) ile yapıldı. Verilerin istatistiksel analizi iki yönlü ANOVA, iki yönlü Robust ANOVA, Spearman's rho korelasyon katsayısı ve Bonferroni düzeltmesi ile yapıldı. İki eksenli bükülme dayanımı değerleri ek olarak Weibull analizi ile de değerlendirildi (α=0,05). Materyalin ana etkisi TP00 ortanca değerleri üzerinde istatistiksel olarak anlamlı bulunmuşken (P=0,029); fırınlamanın TP00 ortanca değerleri üzerindeki etkisi istatistiksel olarak anlamlı bulunmamıştır (P=0,715). Ayrıca materyal ve fırınlama etkileşimi TP00 ortanca değerleri üzerinde istatistiksel olarak anlamlı bulunmamıştır (P=0,679). Vita materyalinin ortanca TP00 değeri diğer materyallerden istatistiksel olarak yüksektir (P<0,05). Ancak Katana ve DD Cube materyallerinin ortanca TP00 değerleri arasında istatistiksel olarak fark yoktur (P=0,712). Materyal ve fırınlamanın ana etkisi bükülme dayanımı ortalama değerleri üzerinde istatistiksel olarak anlamlı bulunmuştur (P<0,001). Materyallerin ortalama bükülme dayanımı değerlerine göre sıralaması Vita YZ/ST (575,53 ± 93,4 MPa)>DD Cube ONE/ML (530,28 ± 81,02 MPa)>Katana STML (463,04 ± 87,66 MPa) şeklindedir. Ancak materyal ile fırınlama etkileşimi iki yönlü bükülme dayanımı değerleri üzerinde istatistiksel olarak anlamlı bir fark yaratmamıştır (P=0,918). Materyalin etkisinden bağımsız olarak T1 grubu, fırınlama gruplarından istatistiksel olarak daha düşük iki yönlü bükülme dayanımı değeri göstermiştir (P<0,001). T2, T3 ve T5 gruplarının ortalama bükülme dayanımı değerleri arasında ise istatistiksel olarak anlamlı bir fark bulunmamıştır (P=0,918). Tekrarlanan fırınlamanın TP00 parametresi ile bükülme dayanımı arasındaki ilişki istatistiksel olarak anlamlı bulunmamıştır (P=0,320). Tekrarlanan fırınlama 4Y-TZP içerikli monolitik zirkonya materyallerinin TP00 değerlerini etkilememiştir. Ancak TP00 değerleri farklı monolitik zirkonya materyallerinden etkilenmiştir. İki eksenli bükülme dayanımı değerleri ise tekrarlanan fırınlama ve farklı monolitik zirkonya materyallerinden etkilenmiştir. Bu nedenle klinik koşullarda bu parametrelerin 4Y-TZP içerikli monolititk zirkonya materyallerinin optik ve mekanik özelliklerini etkileyebileceği göz önünde bulundurulmalıdır.
Özet (Çeviri)
The aim of this in vitro study was to investigate the effect of repeated firing on the translucency parameter (TP00) and biaxial flexural strength of three different high translucency 4Y TZP monolithic zirconia materials. A total of 180 disc-shaped specimens (14,00 - 0,01 mm diameter and 1,20 - 0,01 mm thickness) were produced from three different monolithic zirconia material (Vita YZ/ST, Katana STML and DD Cube ONE/ML) with computer-aided design-computer-aided manufacturing (CAD-CAM). The prepared samples were sintered in accordance with the manufacturer's instructions. Each zirconia material was glazed as per the manufacturer's instructions. The specimens were then randomly divided into 4 subgroups according to the additional firing process (n=15): Control group (T1), 2nd firing group (T2), 3rd firing group (T3) and 5th firing group (T5). All specimens were then cleaned with an ultrasonic cleaner in distilled water for 10 min. The Commission Internationale de I' Eclairage (CIE) L*, a*, and b* color coordinates of the specimens were measured with a dental spectrophotometer using black and white backgrounds and TP00 values were calculated. The biaxial flexural strength of the specimens was determined by piston test on three balls. A load of 1mm/min was applied to the specimens until fracture in a universal testing machine according to ISO 6872 standards. One randomly selected specimen from each group was analyzed by scanning electron microscopy (SEM). The tetragonal-monoclinic phase transformation in all groups was evaluated by X-ray diffraction (XRD). Statistical analysis of the data was performed by two-way ANOVA, two-way Robust ANOVA, Spearman's rho correlation coefficient and Bonferroni correction. Biaxial flexural strength values were additionally evaluated by Weibull analysis (α=0,05). The main effect of material was statistically significant on the TP00 median values (P=0,029), whereas the effect of firing on the TP00 median values was not statistically significant (P=0,715). In addition, the interaction of material and firing was not statistically significant on the median TP00 values (P=0,679). The median TP00 value of Vita material was statistically higher than the other materials (P<0,05). However, there is no statistically significant difference between the median TP00 values of Katana and DD Cube materials (P=0,712). The main effect of material and firing was statistically significant on the mean flexural strength values (P<0,001). The order of the materials according to the mean flexural strength values was Vita YZ/ST (575,53 ± 93,4 MPa)>DD Cube ONE/ML (530,28 ± 81,02 MPa)>Katana STML (463,04 ± 87,66 MPa). However, the interaction of material and firing did not create a statistically significant difference on the biaxial flexural strength values (P=0,918). Regardless of the effect of the material, the T1 group showed a statistically lower two-way flexural strength value than the firing groups (P<0,001). There was no statistically significant difference between mean biaxial flexural strength values of T2, T3 and T5 groups (P=0,918). The relationship between TP00 parameter and flexural strength of repeated firing was not statistically significant (P=0,320). Repeated firing did not affect the TP00 values of monolithic zirconia materials containing 4Y-TZP. However, TP00 values were affected by different monolithic zirconia materials. Biaxial flexural strength values were affected by repeated firing and different monolithic zirconia materials. Therefore, it should be considered that these parameters may affect the optical and mechanical properties of 4Y-TZP-containing monolithic zirconia materials in clinical conditions.
Benzer Tezler
- Tekrarlanan fırınlamanın farklı tip lityum disilikat seramiklerin renk ve mekanik özellikleri üzerindeki etkisi
Effect of repeated firing on color and mechanical properties of different types of lithium disilicate ceramics
GÜLER SAFRAN ÇİÇEK
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiKütahya Sağlık Bilimleri ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. MERYEM GÜLCE SUBAŞI
- Tekrarlanan fırınlama işleminin zirkonya kronların marjinal uyum ve optik özelliklerine etkisinin araştırılması
Investigation of the effect of repeated firing on the marginal fit and optical properties of zirconia crowns
AYŞEGÜL ÜÇDAL ASLAN
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiUşak ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. BENGİSU YILDIRIM
- Zirkonyum dioksit alt yapı üzerine uygulanan farklı yüzey işlemlerinin ve tekrarlanan fırınlamanın üst yapı porseleninin bağlanma dayanımına etkisinin in-vitro olarak incelenmesi
In-vitro evaluation of the effect of different surface treatments and repeated firing on their bond strength to two veneer ceramics to zirconia
SİNEM SAVRAN ÇAKIR
Doktora
Türkçe
2011
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. BÜLENT ŞERMET
- Farklı yöntemler ve kalınlıklarda hazırlanan implant üstü metal altyapıların kenar ve iç uyumlarına tekrarlanan fırınlamanın etkisi
Effect of repeated firings on the marginal and internal adaptation of implant supported metal ceramic restorations fabricated with different thicknesses and fabrication method
ABDURRAHMAN ÖĞÜNÇ
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş Hekimliğiİnönü ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ GÜLER YILDIRIM AVCU
- Monolitik lityum disilikat cam seramik bloklardan, farklı kalınlıkta üretilen indirekt restorasyonların glaze işlemi için farklı sayıda fırınlama sonucunda renk değişikliğinin ve mekanik özelliklerinin değerlendirilmesi
Evaluating of color changes and mechanical characteristics of different thicknesses of indirect restorations which produced by monolithic lithium disilicate glass ceramic blocks due to different firing times for glaze.
AGAJAN RAHMANOV
Doktora
Türkçe
2018
Diş HekimliğiDicle ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. REMZİ NİĞİZ