8090 alüminyum-lityum alaşımında retrogresyon ardından yeniden yaşlandırma ısıl işlemiyle özelliklerin optimizasyonu

Optimization of the properties of 8090 aluminum-lithium alloys by retrogression and reaging heat treatment

  1. Tez No: 101415
  2. Yazar: CANAN GAMZE GÜLERYÜZ
  3. Danışmanlar: PROF.DR. AHMET ARAN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 2001
  8. Dil: Türkçe
  9. Üniversite: İstanbul Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Belirtilmemiş.
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 91

Özet

8090 ALÜMİNYUM-LİTYUM ALAŞIMINDA RETROGRESYON ARDINDAN YENİDEN YAŞLANDIRMA ISDL İŞLEMİYLE ÖZELLİKLERİN OPTİMİZASYONU ÖZET 1970'lerdeki petrol krizinden sonra uçak-uzay uygulamalarında hafiflik önem kazanmıştır. Bu aşamada Al-Li alaşımları, uçak üreticilerinin ilgisini, geleneksel alüminyum alaşımlarına göre düşük olan yoğunlukları nedeniyle, eskiden olduğundan daha çok çekmeye başlamıştır. Bununla birlikte Al-Li alaşımları üzerinde, son 15 yılda yapılan çok sayıda araştırmaya rağmen uygulamaları beklendiği kadar olmamıştır. Bunun nedenleri arasında, bu alaşımların sünekliklerinin ve kırılma tokluklarının düşük olması, mekanik özelliklerinde görülen anizotropi, gerilmek' korozyona olan hassasiyetlerinin geleneksel yüksek dayanımlı alaşımlardan daha fazla olması vardır. Bununla birlikte olumlu özellikleri nedeniyle kullanılan birçok Al-Li alaşımı vardır. 8090 hem ticari, hem de askeri uçaklarda kullanılan bir alaşımdır. 1974 yılında, Cina tarafindan 7000 serisi alüminyum alaşımlarında aşın yaşlandırma durumundaki yüksek gerümeli korozyon dayanıklıhğryla birlikte yapay yaşlandırmadaki en yüksek dayanımı birlikte sunan bir ısıl işlem, 'Retrogresyon ardından Yeniden Yaşlandırma (Retrogression and Reaging-RRA^-RYY' geliştirildi. Bu ısıl işlem malzemeye yapay yaşlandırma durumunda uygulanmakta olup, esasen malzemenin kısa süreli olarak kısmen çözündürülmesi ve ardından orijinal yaşlandırma koşullarında yeniden yaşlandırümasında oluşur. Son yıllarda yapılan çalışmalar bu ısıl işlemin Al-Li alaşımlarında gerümeli korozyon problemini gidermede kullanılabileceğini göstermiştir. Pek çok araştırmacı, belirli alaşımlar için, en uygun ısıl işlemi senaryosunu tanımlamak üzerinde yoğunlaşmıştır. Bu çalışmada, 8090 Al-Li-Cu-Mg-Zr alaşımı üzerinde deneyler yapılmıştır. İlk etapta alaşımın yapay yaşlandırmaya olan cevabı araştırılmış, alaşıma, RYY ısıl işlemleri uygulanarak bu ısıl işlemin hassasiyetine olan etkisi üzerinde durulmuştur. XI

Özet (Çeviri)

OPTIMIZATION OF THE PROPERTIES OF 8090 ALUMINUM-LITHIUM ALLOYS BY RETROGRESSION AND REAGING HEAT TREATMENT SUMMARY After petrol crisis in the late 1970s, weight saving problem had great importance for aerospace vehicles. Alummum-lithium alloys are of considerable potential interest to the aerospace industry because of their significantly lower density compared with conventional aluminum alloys. Although Al-Li alloys have been studied intensively in the past 15 years, their applications remained limited. The reasons are their lower ductility and fracture toughness, mechanical anisotropy, lower stress corrosion cracking resistance. In 1974, B. Cina, patented a novel heat treatment method that reduced the susceptibility of the 7000 series aluminum alloys to stress corrosion cracking, while still substantially retaining the original strength of the alloy. This process is known as 'Retrogression and Reaging Heat Treatment' and applied to the material in the artificial aging condition and consists of a short time retrogression, or partial solution treatment at a temperature that changes according to the alloy, followed by reaging using the same conditions used for the original artificial aging. Although most of the studies had been performed on 7000 type alloys, recent investigations have shown that, it is possible to apply this heat treatment to solve the stress corrosion problem of ahuninum-lithium alloys. The studies are concerned on the development of the most effective heat treatment conditions. 8090 is a Al-Li-Cu-Mg-Zr alloy and it has an application area on both commercial and military aircraft. It is aimed to determine the most effective heat treatment for better stress corrosion durability for 8090 alloy. At first stage, the aging behavior of the material was investigated by applying aging through different time periods and the aging time which gives highest strength is obtained (in order to specify T6 condition).Possible RRA treatments and stress corrosion test are applied for 8090 alloy. Appropriate RRA treatments which give acceptable strength and stress corrosion resistance are tried to determine. Xll

Benzer Tezler

  1. Burdur ili mermer sektörünün kurumsal ve ekonomik yapısı

    İnstitutional and economic structure of marble sector in burdur

    AHMET SARITAŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2006

    EkonomiAkdeniz Üniversitesi

    İşletme Ana Bilim Dalı

    PROF.DR. AYŞE KURUÜZÜM

  2. 8090 Al-Li alaşımında retrogresyon ardından yeniden yaşlandırma işleminin yorulma özelliklerine etkisi

    Effects of retrogression and reaging on fatigue properties of 8090 Al-Li alloy

    ALİ ÖZGÜR ILGAZ

    Yüksek Lisans

    Türkçe

    Türkçe

    2004

    Makine Mühendisliğiİstanbul Teknik Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF.DR. MEHMET DEMİRKOL

  3. Alüminyum - çinko metal işleme tesisi atıksuyunun elektrokoagülasyon yöntemi ile arıtılabilirliğinin incelenmesi

    Research on refinability of aluminum – zinc metal working plant waste water with electrocoagulation method

    BANU TÜRK

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Çevre MühendisliğiOndokuz Mayıs Üniversitesi

    Çevre Mühendisliği Ana Bilim Dalı

    DOÇ. DR. NEVZAT BEYAZIT

  4. Yüksek hızda şekillendirilen alüminyum alaşımlarında oluşan deformasyon incelenmesi

    An Investigation at deformation at aluminium clylindrical curs formed under high

    MUSTAFA YAŞAR

    Doktora

    Türkçe

    Türkçe

    2001

    Makine MühendisliğiMarmara Üniversitesi

    Makine Eğitimi Ana Bilim Dalı

    PROF.DR. OSMAN YAZICIOĞLU

    PROF.DR. İBRAHİM KADI

  5. Zeolit Y kristalizasyonuna polielektrolitlerin etkisi

    Influence of polyelectrolytes on crystallization of zeolite Y

    H. JÜLİDE KÖROĞLU

    Doktora

    Türkçe

    Türkçe

    2002

    Kimya Mühendisliğiİstanbul Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. A. NUSRET BULUTCU