Antimikrobiyal monomer ilave edilmiş dental 3D yazıcı materyallerin mikrobiyal tutulumlarının incelenmesi

Investigation of microbial adhesion of dental 3D printing materials incorporated with an antimicrobial monomer

PDF İndir

  1. Tez No: 1015354
  2. Yazar: VİLDAN TURGUT
  3. Danışmanlar: PROF. DR. NESLİHAN TEKÇE
  4. Tez Türü: Diş Hekimliği Uzmanlık
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: 3B baskı, biyofilm, canlı biyokütle, MPC, yüzey pürüzlülüğü, 3D printing, biofilm, viable biomass, 2-methacryloyloxyethyl phosphorylcholine, surface roughness
  7. Yıl: 2026
  8. Dil: Türkçe
  9. Üniversite: Kocaeli Üniversitesi
  10. Enstitü: Diş Hekimliği Fakültesi
  11. Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Restoratif Diş Tedavisi Bilim Dalı
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

ÖZET Amaç: Bu çalışmanın amacı, iki farklı üç boyutlu (3B) baskı dental reçineye ağırlıkça %0, %1 ve %2 oranlarında 2-metakriloiloksietil fosforilkolin (MPC) ilave edilerek hazırlanan örneklerde yüzey pürüzlülüğü ve canlı biyokütle düzeylerinin değerlendirilmesidir. Gereç ve Yöntem: Çalışmada VarseoSmile TriniQ ve PowerResins C&B Ceramic Resin olmak üzere iki farklı 3B baskı dental reçine kullanıldı. Her reçine için ağırlıkça %0, %1 ve %2 MPC içeren gruplar oluşturuldu. Diş ve rezin kompozit örnekleri kontrol grupları olarak dahil edildi. Örneklere standardize bitirme ve polisaj işlemleri uygulandı. Yüzey pürüzlülüğü, temassız optik profilometre ile Sa parametresi kullanılarak değerlendirildi. Canlı biyokütle analizi için Streptococcus mutans, Streptococcus sanguinis ve Candida albicans içeren çok türlü biyofilm modeli oluşturuldu ve canlı biyokütle düzeyleri MTT yöntemi ile belirlendi. Yüzey pürüzlülüğü verilerinin analizinde tek yönlü varyans analizi (One-way ANOVA) ve Tukey HSD post-hoc testi, canlı biyokütle verilerinin analizinde ise Welch ANOVA ve Games-Howell post-hoc testi kullanıldı (α=0,05). Bulgular: Her iki 3B baskı dental reçinede de ağırlıkça %1 ve %2 MPC ilavesi, MPC içermeyen gruplara kıyasla canlı biyokütle değerlerini anlamlı düzeyde azalttı (p<0,001). Ancak %1 ve %2 MPC grupları arasında anlamlı fark bulunmadı (p>0,05). Yüzey pürüzlülüğü açısından değerlendirildiğinde, MPC ilavesi her iki reçine sisteminde de anlamlı bir değişikliğe neden olmadı (p>0,05). Sonuç: Bu in vitro çalışmanın sınırları dahilinde, her iki 3B baskı dental reçinede MPC ilavesi sonrasında yüzey pürüzlülüğü değerleri açısından anlamlı fark bulunmamıştır. Ağırlıkça %1 ve %2 MPC ilavesi, MPC içermeyen gruplara kıyasla canlı biyokütle değerlerini anlamlı düzeyde azaltmış; ancak %1 ve %2 MPC grupları arasında anlamlı fark bulunmamıştır.

Özet (Çeviri)

ABSTRACT Objective: The aim of this study was to evaluate the surface roughness and viable biomass levels of specimens prepared from two different three-dimensional (3D)-printed dental resins modified with 0 wt%, 1 wt%, and 2 wt% 2-methacryloyloxyethyl phosphorylcholine (MPC). Materials and Methods: Two 3D-printed dental resins, VarseoSmile TriniQ and PowerResins C&B Ceramic Resin, were used in this study. For each resin, groups containing 0 wt%, 1 wt%, and 2 wt% MPC were prepared. Natural tooth and resin composite specimens were included as control groups. Standardized finishing and polishing procedures were performed during specimen preparation. Surface roughness was evaluated using a non-contact optical profilometer based on the Sa parameter. For viable biomass analysis, a multispecies biofilm model consisting of Streptococcus mutans, Streptococcus sanguinis, and Candida albicans was established, and viable biomass levels were determined using the MTT assay. Surface roughness data were analyzed using one-way analysis of variance (ANOVA) followed by Tukey HSD post hoc tests, whereas viable biomass data were analyzed using Welch ANOVA followed by Games–Howell post hoc tests (α=0.05). Results: In both 3D-printed dental resins, the incorporation of 1 wt% and 2 wt% MPC significantly reduced viable biomass levels compared with the unmodified groups (p<0.001). However, no significant difference was observed between the 1 wt% and 2 wt% MPC groups (p>0.05). Regarding surface roughness, MPC incorporation did not result in a significant change in either resin system (p>0.05). Conclusion: Within the limitations of this in vitro study, no significant difference in surface roughness values was found after MPC incorporation in either 3D-printed dental resin. The incorporation of 1 wt% and 2 wt% MPC significantly reduced viable biomass values compared with the MPC-free groups; however, no significant difference was found between the 1 wt% and 2 wt% MPC groups.

Benzer Tezler

  1. Tez No

    507231

    Poliakrilamid biyokompozit sentezi

    Synthesis of polyamylamide biocomposite

    GÜLŞAH CEVAHİR

    Yüksek Lisans

    Türkçe

    Türkçe

    2018

    Bilim ve Teknolojiİstanbul Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. OYA ATICI

  2. Tez No

    911970

    Hidroksiapatit bağlayıcı antimikrobiyal peptit içerikli bir self adeziv rezin simanın fiziksel ve mekanik özelliklerinin değerlendirilmesi

    Evaluation of physical and mechanical properties of a self adhesive resin cement containing hydroxyapatite binding antimicrobial peptide

    AYŞENUR TURAN

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2025

    Diş HekimliğiErciyes Üniversitesi

    Restoratif Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. HACER BALKAYA

  3. Tez No

    618137

    Geçici protez materyali olarak kullanılan akrilik ve kompozit rezinlere antibakteriyel ajan eklenmesinin bakteriyel tutuluma, materyalin fiziksel ve kimyasal özelliklerine etkisinin incelenmesi

    Evaluation of adding antibacterial agent effects on bacterial accumulation, physical and chemical properties of acrylic and composite resin-based provisional crown materials

    SERDAR KILIÇ

    Doktora

    Türkçe

    Türkçe

    2015

    Diş HekimliğiKaradeniz Teknik Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. SUBUTAY HAN ALTINTAŞ

  4. Tez No

    1010329

    Biointerfacial mechanical modulation of model lipid membranes by gramicidin D: A quartz crystal microbalance with dissipation analysis

    Gramisidin D'nin model lipid membranlarda biyoarayüzeysel mekanik modülasyonunun disipasyonlu kuvars kristal mikroterazi analizi

    ŞEBNEM SEHERLER

    Doktora

    İngilizce

    İngilizce

    2026

    Biyoteknolojiİstanbul Teknik Üniversitesi

    Moleküler Biyoloji-Genetik ve Biyoteknoloji Ana Bilim Dalı (disiplinlerarası)

    DR. ÖĞR. ÜYESİ ABDULHALİM KILIÇ

  5. Tez No

    970817

    Antibakteriyel özelliğe sahip kuaterner amonyum tuzu katkılı poli (laktik asit) kompozit filmlerinin hazırlanması

    Preparation of quaternary ammonium salt added poly(lacti acid) composite films having antibacterial properties

    BETÜL KÜBRA AYDIN

    Yüksek Lisans

    Türkçe

    Türkçe

    2025

    Polimer Bilim ve TeknolojisiKocaeli Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    DOÇ. DR. MERVE DANDAN DOĞANCI

Geri Dön