Farklı yüzey işlemleri ve rezin simanlar uygulanmış PEEK alt yapının termal siklus sonrası CAD/CAM seramikler ile bağlanma dayanımının ve translusensi özelliklerinin değerlendirilmesi
Evaluation of shear bond strength and translucency properties of PEEK frameworks and CAD/CAM ceramics with different surface treatments and resin cements after thermocycling
- Tez No: 1024884
- Danışmanlar: DOÇ. DR. SİBEL DİKİCİER
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Bağlanma dayanımı, CAD/CAM, PEEK, Renk değişimi (ΔE00), Termal yaşlandırma, Translusensi, PEEK, CAD/CAM, Thermal aging, Color change (ΔE₀₀), Translucency, Bond strength
- Yıl: 2026
- Dil: Türkçe
- Üniversite: Sağlık Bilimleri Üniversitesi
- Enstitü: Hamidiye Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı, farklı yüzey işlem yöntemleri ve rezin siman türlerinin PEEK ile farklı CAD/CAM bloklar arasındaki optik özellikler ve bağlanma dayanımı üzerindeki etkilerini değerlendirmektir. Bu kapsamda kumlama ve piranha asidi uygulaması sonrası, dual-cure ve self-adeziv rezin simanlar ile lityum disilikat ve hibrit bloklar kullanılarak oluşturulan örnekler incelenmiştir. Gereç ve Yöntem: PEEK yüzeylerine kumlama ve piranha asidi uygulanmış yüzey işlemi öncesi ve sonrası yüzey pürüzlülük değerleri ölçülmüştür. Örnekler lityum disilikat ve hibrit bloklar ile dual-cure ve self adeziv rezin simanlar kullanılarak simante edilmiştir. Optik özellikler termal yaşlandırma öncesi ve sonrası değerlendirilmiş ardından makaslama bağlanma dayanımı testi uygulanmıştır. Veriler uygun istatistiksel yöntemlerle analiz edilmiştir. Bulgular: Yüzey pürüzlülüğü kumlama > piranha > kontrol şeklinde sıralanmış ve fark anlamlı bulunmuştur (p<0,001). Termal yaşlandırma sonrası tüm gruplarda L*, a* ve b* değerleri anlamlı şekilde azalmıştır (p<0,05). Hibrit bloklarda renk değişimi lityum disilikat bloklara göre daha yüksek bulunmuştur. Blok türü ΔTP ve ΔE00 üzerinde anlamlı etki göstermiştir (p<0,001; partial η²≈0,33). Tüm grupların ortalama ΔE00 değerleri algılanabilirlik eşiğinin üzerinde bulunmuş, hibrit bloklar lityum disilikat bloklara göre daha yüksek renk değişimi göstermiştir (p<0,001). En yüksek bağlanma dayanımı değeri kumlama + hibrit blok + dual-cure grubunda en düşük değer piranha + LDS + self-adeziv grubunda elde edilmiştir. Bağlanma dayanımında en belirleyici faktör siman türü olup (partial η²=0,36), dual-cure simanlar daha yüksek değerler sağlamıştır. Sonuç: Kumlama, PEEK yüzeyinde en etkili yüzey işlemi olarak daha yüksek bağlanma dayanımı sağlamıştır. Optik stabilitede blok türü, bağlanma dayanımında ise yüzey işlemi ve siman türü belirleyici olmuştur.
Özet (Çeviri)
Aim: The aim of this study was to evaluate the effects of different surface treatment methods and resin cement types on the optical properties and bond strength between polyetheretherketone (PEEK) and different CAD/CAM blocks. In this context, specimens prepared using lithium disilicate and hybrid CAD/CAM blocks cemented with dual-cure and self-adhesive resin cements after airborne-particle abrasion and piranha acid surface treatments were investigated. Materials and Methods: PEEK surfaces were subjected to airborne-particle abrasion and piranha acid treatment, and surface roughness values were measured before and after surface modification. The treated surfaces were cemented to lithium disilicate and hybrid CAD/CAM blocks using dual-cure and self-adhesive resin cements. Optical properties were evaluated before and after thermal aging, followed by shear bond strength testing. The data were analyzed using appropriate statistical methods. Results: Surface roughness values were ranked as airborne-particle abrasion > piranha acid > control, and the differences were statistically significant (p<0.001). After thermal aging, L*, a*, and b* values significantly decreased in all groups (p<0.05). Hybrid blocks exhibited greater color changes than lithium disilicate blocks, whereas the cement type had no significant effect on optical parameters (p>0.05). Block type had a significant effect on ΔTP and ΔE00 (p<0.001). A negative correlation was observed between ΔTP and ΔE00 (r = −0.34; p = 0.006). All groups showed ΔE00 values above the perceptibility threshold, and lithium disilicate blocks demonstrated lower color change values than hybrid blocks (p<0.001). The highest bond strength was obtained in the airborne-particle abrasion + hybrid block + dual-cure resin cement group. Dual-cure resin cements provided higher bond strength values. Conclusion: Airborne-particle abrasion was the most effective surface treatment for improving the bond strength of PEEK. While block type was the primary factor affecting optical stability, surface treatment and cement type were more influential on bond strength.
Benzer Tezler
- Farklı yüzey işlemleri uygulanan zirkonya seramiğe üç farklı rezin simanın bağlanmasının incelenmesi
Investigation of bond strength of three different resin cements to zirconia ceramics which different surface treatments are applied
MERYEM GÜLCE SUBAŞI
Doktora
Türkçe
2011
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ÖZGÜR İNAN
- Farklı yüzey hazırlama işlemlerinin zirkonya-rezin bağlantı değerlerine etkisinin araştırılması
Effect of different surface treatment methods on bond strength of zirconia and resin cement
SEDA ŞANLI
Doktora
Türkçe
2013
Diş HekimliğiEge ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. MİNE DÜNDAR ÇÖMLEKOĞLU
- Rezin simanların tam seramik alt yapı rengi üzerine etkileri
Effects of resin cements on the color of all ceramic core substructure
UFUK BAŞOĞLU
Doktora
Türkçe
2009
Diş HekimliğiYeditepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. İDİL DİKBAŞ
- Farklı yüzey işlemleri uygulanmış Y-TZP alt yapı malzemesinin rezin simanlarla bağ dayanımının incelenmesi
Evaluation of bond strength of luting resins to a Y-TZP framework material processed with different surface treatments
ALİ ERDEM
Doktora
Türkçe
2011
Diş HekimliğiEge ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ADALET ERDEM
- Üç değişik protetik alt yapı materyalinin iki farklı siman ile bağlanma dirençlerinin incelenmesi
Three different infrastructure prosthetic material, with cement bağlanmadi̇rençleri̇ni̇n study of two different
VEYSEL ERATİLLA
Doktora
Türkçe
2013
Diş HekimliğiDicle ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
YRD. DOÇ. DR. AYÇA DENİZ İZGİ