Synthesis and mechanical properties of unsaturated polyester based nanocomposites
Doymamış poliester bazlı nanokompozitlerin sentezlenmesi ve mekanik özelliklerinin araştırılması
- Tez No: 114962
- Danışmanlar: PROF. DR. ÜLKÜ YILMAZER
- Tez Türü: Yüksek Lisans
- Konular: Kimya Mühendisliği, Chemical Engineering
- Anahtar Kelimeler: Nanokompozit, Doymamış Poliester Nanokompozitleri, Mekanik Özellikler, Organik Modifiye Killer, Montmorillonit. vı, Montmorillonit, Nanokompozitler, Sentez, Nanocomposite, Unsaturated Polyester Nanocomposites, Mechanical Properties, Organically Modified Clays, Montmorillonite. IV, Montmorillonite, Nanocomposites, Synthesis
- Yıl: 2001
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
oz DOYMAMIŞ POLIESTER BAZLI NANOKOMPOZİTLERİN SENTEZLENMESİ VE MEKANİK ÖZELLİKLERİNİN ARAŞTIRILMASI İnceoğlu, Ali Baran Yüksek Lisans, Kimya Mühendisliği Bölümü Tez Yöneticisi: Prof. Dr. Ülkü Yılmazer Eylül 2001, 80 sayfa Nanokompozitler, mineral dolgulu ve çok az miktarlarda (<10%) nano boyutlu mineral içeren yeni bir sınıf kompozitlerdir. Kullanılan nano boyutlu parçacıkların boy-en oranının (yaklaşık 200-1000) ve yüzey alanının (750 m2/g) çok yüksek olmasından dolayı, polimerlerin, mekanik, yanmazlık, ısıl ve bariyer özellikleri çok iyi yönde gelişmeler göstermektedirler ve bu parçacıklar malzemelerin yoğunluğuna ve ışık geçirgenliklerine çok fazla etkide bulunmamaktadırlar. Bu çalışma, doymamış poliesterler ile kuaternar amonyum tuzlan ile organik olarak modifiye edilmiş killerin çeşitli oranlarda karıştırılarak mekanik özelliklerinin incelenmesini içermektedir. Karışma esnasında, polimerzincirleri kil tabakalarının arasında bulunan van der Waals boşluklarına girerler ve bu sayede bu boşlukların genişlemesine yol açarlar. Bu çalışmanın amacı doymamış poliester ile modifiye kili kullanarak yeni bir nanokompozit elde etmektir. Sentezleme işleminden sonra oluşan malzemelerin XRD analizleri incelenmiş ve kil tabakaları arasındaki mesafenin 1.25 nm'den 4.5 nm'ye çıktığı gözlenmiştir. Ayrıca oluşan nanokompozitlerin mekanik özellikleri incelenmiş ve bükülme modülünün, ağırlıkça % 3 modifiye kil eklendiğinde % 35 arttığı görülmüştür. Bunun yanında ağırlıkça % 5 modifiye kil eklendiğinde de çekme modülüsünün de % 17 arttığı gözlenmiştir. DSC diagramlarından da kil eklenmesiyle, malzemenin camsı sıcaklığının arttığı gözlenmiştir. Bütün bu sonuçlardan elde edilen bilgilere göre bir kısmı tam açılmış bir kısmı yan açılmış nanokompozitler elde edilmiştir.
Özet (Çeviri)
ABSTRACT SYNTHESIS AND MECHANICAL PROPERTIES OF UNSATURATED POLYESTER BASED NANOCOMPOSITES Inceoğlu, Ali Baran M.S., Department of Chemical Engineering Supervisor: Prof. Dr. Ülkü Yilmazer September 2001, 80 pages Nanocomposites are a new class of mineral-field plastics that contain relatively small amounts (<10%) of nanometer-sized clay particles. Through modification of any plastics matrix using tiny clay platelets, a new class of materials, termed nanocomposites, can be created. The particles, due to their extremely high aspect ratios (about 200 to 1000), and high surface area (in excess of 750 m2/g) promise to improve structural, mechanical, flame retardant, thermal and barrier properties without substantially increasing the density or reducing light transmission properties of the base polymer. The process involves mixing the unsaturated polyester (UP) and layered silicate powders that have been modified with hydroxyl terminated quaternary IIIammonium salt. During mixing, the polymer chains diffuse from the bulk polymer into the van der Waals galleries between the silicate layers. The objective of this study is to make a new nanocomposite composed of unsaturated polyester as the matrix and organically modified clay as the filler. After the synthesis, XRD patterns showed that the interlayer spacing was expanded from 1.25 nm to 4.5 nm. The mechanical properties of the nanocomposites were analyzed and it was found that adding only 3 w/w % organically modified clay improved the flexural modulus of unsaturated polyester by 35%. The tensile modulus of unsaturated polyester was improved 17% at 5% of organically modified clay loading. From DSC diagrams it was found that Tg values of the nanocomposites also increased with the clay content. From these results, it is concluded that a partially exfoliated / intercalated nanocomposite is formed at relatively low clay contents.
Benzer Tezler
- Epoxy based nanocomposites materials
Epoksi bazlı nanokompozit malzemeler
ÇİĞDEM BAŞARA
Yüksek Lisans
İngilizce
2002
Kimya MühendisliğiOrta Doğu Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. ÜLKÜ YILMAZER
YRD. DOÇ. DR. GÖKNUR BAYRAM
- POSS modifiye alev geciktirici doymamış polyester reçine sentezi ve karakterizasyonu
Synthesis and characterization of POSS modified flame retardant unsaturated polyester resin
SERPİL İPEK
Yüksek Lisans
Türkçe
2023
Polimer Bilim ve TeknolojisiMarmara ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. NİLHAN KAYAMAN APOHAN
- UV-ışınları ile sertleştirilen polimerik filmlerin hazırlanması, karakterizasyonu ve uygulama alanları
The Preparation, the characterization, and various applications of UV-cured polymeric films
ATTİLA GÜNGÖR
- Biomedical application of an enzymatically synthesized biopolyester
Enzimatik olarak sentezlenmiş bir biyopoliesterin biyomedikal uygulaması
ŞENOL BEYAZ
Yüksek Lisans
İngilizce
2024
Biyoteknolojiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. FATOŞ YÜKSEL GÜVENİLİR