Improvement of flame retardance propertles of unsaturated polyesters

Başlık çevirisi mevcut değil.

  1. Tez No: 15509
  2. Yazar: ŞÜKRÜ ÖZTÜRK
  3. Danışmanlar: PROF.DR. GÜNGÖR GÜNDÜZ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya Mühendisliği, Chemical Engineering
  6. Anahtar Kelimeler: Yanıcı lık, Yanmazlık, Doymamış Poliesterler, Kendi Kendisini Söndüren, Poliester liodifikasyonu, Çarpma Dayanımı, Şeriflik, Flammabili ty, Flame Retardance, Unsaturated Polyesters, Self-extinguishing, Polyester Modification, Impact Strength, Hardness
  7. Yıl: 1991
  8. Dil: İngilizce
  9. Üniversite: Orta Doğu Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Belirtilmemiş.
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 91

Özet

DOYMAMIŞ POL 1 ESTERLER İN YANMAZLIK ÖZELLİKLERİNİN ARTTIRILMASI ÖZTÜRK, Şükrü Yüksek Lisans Tezi, Kimya Mühendisliği Bölümü Orta Doğu Teknik Üniversitesi Tez Yöneticisi: Prof. Dr. Güngör GÜNDÜZ Eylül 1991, 91 sayfa ÖZET Bu çalışmada, endüstride yaygın alarak kullanılan prapilen glikol esaslı bir doymamış poliester reçinesi tetra-bromofitalik anhidrit (TBPA) ile modifiye edilmiştir. Sözkonusu modifikasyonun poliesterin yanmazlık ve mekanik özellikleri (çarpma dayanımı, sertlik) üzerindeki etkileri deneysel olarak incelenmiştir. Modifiye edilmiş poliester iki basamaklı bir pişirme işlemiyle sentezlenmiştir. İlk basamak prapilen glikol esaslı poliesterin sentezlenmesini, ikinci basamak ise bu poliesterin TBPA ile modifikasyonunu içermektedir. Tavlama (çaprazlama) reaksiyonu bir stiren-akrilonitril monomer sistemi ile yapılmıştır. Bu amaçla elde edilen reçinenin sırasıyla, %40 ve %20'si kadar stiren ve akrilonitril kullanılmış tır.Yanmazlık ile poliesterin içerdiği brom miktarı arasında lineer bir ilişki olduğu anlaşılmıştır. Ayrıca yanmazlık testleri, kendi kendisini söndüren bir poliester reçinesi elde edilebilmek için, sözkonusu reçinenin en az %12 brom içermesi gerektiğini göstermiştir. Maksimum çarpma dayanımı 10,5 (J/m. genişilik) olarak, %9. I brom içeren reçinede elde edilmiştir. Çarpma dayanımı maksimum noktada, modifiye edilmemiş poliesterin hemen hemen iki katı bir değere ulaşmıştır. Ayrıca maksimum çarpma dayanımına sahip reçinenin minimum sertlikte olduğu görülmüştür. Maksimum sertlik 27.6 BHN olarak %0. O Br içeren Cmodifiye edilmemiş D poliesterde elde edilmiştir.

Özet (Çeviri)

IMPROVEMENT OF FLAME RETARD ANCE PROPERTIES OF UNSATURATED POLYESTERS ÖZTÜRK, Şükrü M. S in Chemical Engineering Middle East Technical University- Supervisors Pro-f. Dr. Güngör GOMDÜZ September 1991,91 pages ABSTRACT In this research, a conventional propylene glycol based unsaturated polyester was modified by tetra-bromo phthalic anhydride (TBPA) at -five different concentrations. The effect of this modification on the flame retardance and the mechanical properties (i.e. impact strength, hardness) of the polyester was studied experimentally. The synthesis of modified polyester was performed by a two step cooking process which includes the synthesis of conventional polyester and the modification of this polyester by TBPA. A styrene-acrylonitrile monomer system (40% and 20% of the final polyester respectively) was used for curing (crossl inking) reaction. mA linear relation was observed between the -flame retardance and the bromine content of the polyester. The results o-f -Flame retardance tests indicated that a self-extinguishing polyester can be obtained by using at least 12% Br in modified resin. The maximum impact strength which is 10.5 J/m. width was obtained at 9. IX Br in modi-Fied polyester. The impact strength was almost doubled at the maximum point with respect to unmodified polyester. The maximum in the impact strength corresponded to the minimum in hardness. The maximum hardness which is 27.6 BHN was obtained at OX Br (i.e. unmodified polyester).

Benzer Tezler

  1. Tez No

    200047

    Cam elyaf takviyeli poliester kompozitlere yanmazlık özelliği kazandırılması

    The improvement of flame retardancy of glass fiber reinforced polyester composite materials

    MİYASER DEMİREL

    Yüksek Lisans

    Türkçe

    Türkçe

    2007

    Kimya MühendisliğiGazi Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    DOÇ.DR. NURSEL DİLSİZ

    PROF.DR. VECİHİ PAMUK

  2. Tez No

    780830

    POSS modifiye alev geciktirici doymamış polyester reçine sentezi ve karakterizasyonu

    Synthesis and characterization of POSS modified flame retardant unsaturated polyester resin

    SERPİL İPEK

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Polimer Bilim ve TeknolojisiMarmara Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF. DR. NİLHAN KAYAMAN APOHAN

  3. Tez No

    243666

    Plazma teknolojisi kullanılarak çeşitli doğal ve sentetik liflerin buruşmazlık ve güç tutuşurluk özelliklerinin geliştirilmesi

    The improvement of crease resistance and flame retardance properties of some natural and synthetic fibers using plasma technology

    BENGİ KUTLU

    Doktora

    Türkçe

    Türkçe

    2008

    Tekstil ve Tekstil MühendisliğiDokuz Eylül Üniversitesi

    Tekstil Mühendisliği Bölümü

    YRD. DOÇ. DR. AYSUN CİRELİ AKŞİT

  4. Tez No

    284432

    Hammaddeleri farklı tekstil malzemelerine güç tutuşurluk özelliğinin kazandırılmasında yeni uygulamalar

    New applications for different raw materials textile stuffs to improvement of flame retardancy propoerties

    FATMA MÜGE KABASAKAL

    Yüksek Lisans

    Türkçe

    Türkçe

    2011

    Tekstil ve Tekstil MühendisliğiKahramanmaraş Sütçü İmam Üniversitesi

    Tekstil Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. REMZİ GEMCİ

  5. Tez No

    436190

    Plastikleştirilmiş poli(laktik asit)'in alev dayanımının fosfor bazlı katkı maddeleri ile geliştirilmesi

    Improvement of the flame retardancy of plastized poly(lactic acid) by means of phosphorus based flame retardant fillers

    FATMA YEMİŞÇİ

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    KimyaKocaeli Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    DOÇ. DR. AYŞE AYTAÇ

Geri Dön