Geri Dön

Surface modification and biocompatibility studies of polyurethane membranes

Poliürethan membranların yüzey modifikasyonu ve biyouyumluluk çalışması

  1. Tez No: 116388
  2. Yazar: YEŞİM ÖZDEMİR
  3. Danışmanlar: PROF. DR. NESRİN HASIRCI
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya, Chemistry
  6. Anahtar Kelimeler: Polyurethane, biocompatibility, plasma surface modification, cell attachment, biomaterial, glow-discharge. IV
  7. Yıl: 2001
  8. Dil: İngilizce
  9. Üniversite: Orta Doğu Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 92

Özet

ÖZ POLİÜRETAN MEMBRANLARIN YÜZEY MODİFİKASYONU VE BİYOUYUMLULUK ÇALIŞMASI Özdemir, Yeşim Yüksek Lisans, Kimya Bölümü Supervisor: Prof. Dr. Nesrin Hasırcı Aralık, 2001, 78 Sayfa Poliüretanlar kan ve doku ile gösterdiği uyumdan dolayı medical alanda kullanılan sentetik polimer ürünler arasında özellikle protez ve organ destek malzemesi olarak ön sıralarda yer almaktadır. Saf olarak elde edilmesinin kolaylığı, geliştirilebilir fiziksel ve mekanik özelliklere sahip olması, sterilizasyon işleminin hiç bir şekilde polimerin yapışma zarar vermemesi ve özelliklerinin kolayca biyolojik ortama adaptasyonunun sağlanması, poliüretanların biyomedikal amaçlı kullanımım desteklemiştir. Ancak, poliüretan yüzeyler hücre yapışması, tutunması ve yayılması konusunda yeterli gelişmeyi göstermediklerinden doku mühendisliği alanında tercih edilmemektedirler. Poliüretan biyomateryallerin yüzey özelliklerini, hücre tutunmasını, çoğalmasını geliştirmek için birçok metod kullanılmaktadır.Bu çalışmada, toluenediisocyanate (TDI) ve polipropilenglikol kullanılarak katkısız poliüretan membranlar hazırlanmıştır. Hazırlanan membranlar oksijen plazma elektriksel deşarj tekniği ile modifîye edilmiş, yüzey hidrofîlikliği ve yüzeye hücre tutunması test edilmiştir. Bu çalışmada medikal saflıkta hazırlanan membranların çekme tesleri yapılmış, Modulus, UTS ve PSBR değerleri hesaplanmıştır. Kimyasal kompozisyona bağlı olarak hesaplanan elastik modulus değerleri 1.26-5.57 MPa arasında, UTS değerleri 0.78-3.77 MPa arasında, %SBR değerleri ise %56.9- %114.2 arasında değişmektedir. Genel olarak, konsantrasyonlardaki TDI/polyol değeri arttıkça, modulus ve UTS değerleri yükselmiş, % SBR değerleri düşmüştür. Yüzey açışı değerleri uygulanan oksijen plazma gücüne bağlı olarak, 66°- 45° değerleri arasında değişiklik göstermektedir. Uygulanan plazmanın gücü arttıkça yüzey temes açısı düşmekte ve poliüretan yüzeylerin hidrofüik karakteri artmaktadır. Polimerik yüzeylerde oksijen plazma uygulamaları, hücre yapışması deneylerini pozitif yönde etkilemektedir. Uygulanan plazma gücü arttıkça membranlara tutunan hücre sayısı 42.4'den-23 hücre/cm2 değerine düşmüştür. Vero hücreleri poliüretan membranlar üzerinde hidrofobik yapışma göstermiştir. Anahtar Sözcükler. Poliüretan, biyouyumluluk, plazma yüzey modifikasyonu, hücre yapışması, biyomateryal, glow discharge. vı

Özet (Çeviri)

ABSTRACT SURFACE MODIFICATION AND BIOCOMPATIBILITY STUDIES OF POLYURETHANE MEMBRANES Özdemir, Yeşim MS., Department of Chemistry, Supervisor. Prof. Dr. Nesrin Hasırcı December, 2001, 78 Pages Polyurethanes are widely used in medical applications as prosthesis and supporting materials of organs because of their excellent blood and tissue compatibility. Easy synthesis, improvable physical and mechanical properties, stability during sterilisation, easy adaptation to the biological environment make them preferable of biomaterials. However cellular adhesion on polyurethane surfaces is relatively poor. Because of the unsatisfactory cell adherence and proliferation, their use in tissue engineering products is limited. Various methods have been developed to promote fast endothelialization on polyurethane materials. In this study, polyurethane membranes in medical purity were prepared from toluene diisocyanates (TDI) and polypropyleneglycol by using various amounts of substances without adding any ingredient. Surfaces of the membranes were modified by using oxygen plasma (glow-discharge) technique and effects of inapplied plasma power on mechanical and surface properties as well as on the attachment of Vero cells were examined. Elastic modulus, ultimate tensile strength (UTS) and percent strain before rupture (PSBR) values were found to be in the range of 1.26-5.57 MPa, 0.78-3.77 Mpa, and 56.97-114.2%, respectively. In general, modulus and UTS values demonstrated an increase and PSBR demonstrated a decrease, as TDI/Polyol ratio in the polymer increased in polymer compositions. Water contact angle values of the plasma modified surfaces varied between 66° and 45° demonstrating a decrease as the applied plasma power was increased. Application of oxygen plasma altered the surface chemistry and effected cell adhesion.lt was observed that as the applied power increased, number of attached cells decreased from 42.4 to 23 cell/cm2 indicating the hydrophobic adhesion of Vero cells on polyurethanes.

Benzer Tezler

  1. Poliüretan filmlerin yüzey modifikasyonu ve biyouyumluluk çalışmaları

    Surface modification of polyurethane films and biocompatibility studies

    TUĞBA AKKAŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2011

    Kimya Mühendisliğiİstanbul Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. F. SENİHA GÜNER

  2. Poliüretan hidrojellerin plazmayla yüzey modifikasyonu ve protein adsorpsiyonu

    Plasma surface modification and protein adsorption of polyurethane hydrogels

    CANSU ÇITAK

    Yüksek Lisans

    Türkçe

    Türkçe

    2011

    Biyokimyaİstanbul Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. F.SENİHA GÜNER

  3. Synthesis and surface modification studies of biomedical polyurethanes to improve long term biocompatibility

    Uzun süreli biyouyumluluğun geliştirilmesi amacıyla biyomedikal poliüretanların sentezi ve yüzey modifikasyonu çalışmaları

    EDA AYŞE AKSOY

    Doktora

    İngilizce

    İngilizce

    2008

    Polimer Bilim ve TeknolojisiOrta Doğu Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF. DR. NESRİN HASIRCI

  4. Improvement of inadequencies of small diameter artificial blood vessels

    Küçük çaplı yapay damarların mevcut yetersizliklerinin iyileştirilmesi

    İPEK YALÇIN ENİŞ

    Doktora

    İngilizce

    İngilizce

    2016

    Tekstil ve Tekstil Mühendisliğiİstanbul Teknik Üniversitesi

    Tekstil Mühendisliği Ana Bilim Dalı

    PROF. DR. ÜMMÜHAN TELEM GÖK SADIKOĞLU

  5. Surface free energy evaluation, plasma surface modification and biocompatibility studies of PMMA

    PMMA filmlerde yüzey enerjisi hesaplaması, plazma ile yüzey modifikasyonu ve biyouyumluluk çalışmaları

    CANTÜRK ÖZCAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2006

    KimyaOrta Doğu Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. NESRİN HASİRCİ