Synthesis and characterization of poly(dimethylsiloxane) and polythiophene composites
Polidimetilsiloksan ve politiofen kompozitlerinin sentezi ve karakterizasyonu
- Tez No: 116472
- Danışmanlar: PROF. DR. SAVAŞ KÜÇÜKYAVUZ, PROF. DR. ZUHAL KÜÇÜKYAVUZ
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Elektrokimyasal Polimerleşme, İletken Polimerler, PDMS/Pth Kompozitleri, PDMS/PTh/CF Kompozitleri, PDMS/PTh/CF Kompozitlerinin Mekanik Özellikleri. v, Electrochemical Polymerization, Conductive Polymers, PDMS/PTh Composites, PDMS/PTh/CF Composites, Mechanical Properties of PDMS/PTh/CF Composites
- Yıl: 2001
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 86
Özet
Bu çalışmada, polidimetilsiloksan (PDMS)/politiofen (PTh) ve PDMS/PTh/karbon elyaf (GF) kompozitleri elektrokimyasal olarak sentezlenmiştir. Elektrokimyasal sentez TBATFB destek elektroliti ve asetonitril çözücüsü kullanılarak 2.2V'da gerçekleştirilmiştir. PDMS/PTh kompo2dtlerinin karakterizasyonu CV, FT-IR, SEM, DSC, TGA ve iletkenlik çalışmalarıyla yapılmıştır. vıPDMS/PTh kompozitlerinin iletkenliklerinin 2.2 S/cm-5.2 S/cm aralığında olduğu gözlenmiştir, %30'a kadar PDMS katıldığında PTh iletkenliğinde kayda değer bir değişim görülmemiştir. FTTR, SEM ve DSC çalışmaları PDMS ile PTh arasında fiziksel bir yapışma değil fakat güçlü bir etkileşimin varlığını göstermiştir. Oldukça esnek ve katlanabilir PDMS/PTh kompozitleri elde edilmiştir. Fakat bu kompozitlerin çekme özellikleri zayıftır. İstenilen çekme özelliklerine ulaşmak için kompozite karbon elyaf katılmıştır. PDMS/PTh kompozitlerine benzer elektrokûnyasal koşullar bu kompozitlerin sentezi için de kullanılmıştır. PDMS/PTh/CF kompozitleri, SEM, TGA, iletkenlik ölçümleri ve mekanik testler ile karakterize edilmiştir. PDMS/PTh/CF kompozitlerinin iletkenliklerinin PDMS/PTh kompozitlerinin iletkenliklerine benzer olduğu görülmüştür. Karbon elyafin PDMS/PTh matrisi tararından kaplandığı ve bu matris içinde düzgün olarak yönlendiği SEM çalışmalarında görülmüştür. Mekanik testlerde, karbon elyafin kompozit içindeki miktarı arttıkça kompozitlerin çekme kuvvetlerinin arttığa görülmüştür. vuAyrıca, PDMS varlığının kompozitlere daha yüksek uzama oranları sağladığı saptanmıştır. Son olarak, çekme modulus verileri yüksek karbon elyaf içerikli ve düşük PDMS içerikli kompozMerin daha dayanıldı kompozitler olduğunu göstermiştir.
Özet (Çeviri)
In this study, polydimethylsiIoxane(PDMS)/polythiophene(PTh) and PDMS/PTh/ carbon fiber(CF) composites were synthesized electrochemically. Electrochemical synthesis was performed at 2.2V using TBATFB as the supporting electrolyte and acetonitrile as the solvent. Characterization of PDMS/PTh composites was done by CV, FT-IR, SEM, DSC, TGA and conductivity measurements. IllConductivities of PDMS composites were observed in the range of 2.2 S/cm-5.2 S/cm. Addition of PDMS content up to 30 percent did not change conductivity of PTh appreciably. FT-IR, SEM and DSC studies showed existence of a strong interaction, rather than physical adhesion, between PDMS and PTh. Highly flexible and foldable PDMS/PTh composites were obtained. However, these composites were poor in tensile properties. In order to reach desired tensile properties, CF was added to the composite. Same electrochemical conditions as in the case of PDMS/PTh were used for the synthesis of PDMS/PTh/CF composites. Characterization of PDMS/PTh/CF was done by using SEM, TGA, conductivity measurements and mechanical tests. Conductivities of PDMS/PTh/CF composites were similar to PDMS/PTh composites. SEM studies show that CF were coated by PDMS/Pth matrix and well oriented in the matrix. In mechanical tests, it has been observed that tensile strength of composites increases with increasing CF content. IVIn addition, higher percent elongation was obtained by the addition of PDMS. Finally, tensile modulus data showed that higher CF content and lower PDMS content describe stiffer composites.
Benzer Tezler
- Synthesis and characterization of poly (4-vinylpyridine) - poly (dimethysiloxane) block copolymers and electrical conductivity of their charge transfer complexes
Poli (4-vinilpiridin) - poli (dimetilsiloksan) blok kopolimerlerinin sentezi, karakterizasyonu ve yük transfer komplekslerinin elektriksel iletkenliği
NİHAN NUGAY
- Synthesis and characterization of interpenetrating polymer networks
Başlık çevirisi yok
EMİNE ELİF HAMURCU GÜREL
- Silikon esaslı makroinimer varlığında yeni organojellerin sentezi, karakterizasyonu ve absorbent olarak kullanımı
Synthesis and characterization of novel organogels in the presence of silicone based macroinimer and usage as abrsobent
NIGAR MAMMADLI
- Grafen köpük / SiO2 katkılı şok emici nanokompozit malzemelerin üretimi ve karakterizasyonu
Synthesis and characterization of graphene foam / Sio2 based shock absorbing nanocomposite
ÇAĞLAR ERDEM
Yüksek Lisans
Türkçe
2020
Mühendislik Bilimleriİzmir Katip Çelebi ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
DOÇ. DR. FETHULLAH GÜNEŞ
- Atık polietilentereftalattan özel blok kopolimerler ve çevre dostu alkid reçine üretimi
Production of special block copolymers and environmental friendly alkyd resins from PET wastes
OĞUZ MECİT