Study of salt-water cracking behavior of 7050 T73651 aluminum alloy through slow strain rate testing under potentiostatic control

7050 T73651 alüminyum alaşımının çatlama tavrının tuzlu su çözeltisinde ve potensiyostatik kontrol altında yavaş çekme deneyi ile incelenmesi

  1. Tez No: 119338
  2. Yazar: ESRA KUŞ
  3. Danışmanlar: PROF. DR. MUSTAFA DORUK, DOÇ. DR. RIZA GÜRBÜZ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Gerilimli Korozyon Çatlaması, Yavaş Çekme Testi, 7050 T73651, Al-Zn-Mg-Cu Alası mı, Potansiyel Kontrolü. VI, Stress Corrosion Cracking, Slow Strain Rate Testing, 7050 T73651, Al-Zn-Mg-Cu alloy, Potential Control. IV
  7. Yıl: 2002
  8. Dil: İngilizce
  9. Üniversite: Orta Doğu Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 88

Özet

öz 7050 T73651 ALÜMİNYUM ALAŞIMININ ÇATLAMA TAVRININ TUZLU SU ÇÖZELTİSİNDE VE POTANSİYOSTATİK KONTROL ALTINDA YAVAŞ ÇEKME DENEYİ İLE İNCELENMESİ Kuş, Esra Yüksek Lisans, Metalürji ve Malzeme Mühendisliği Bölümü Tez Yöneticisi: Prof. Dr. Mustafa Doruk Ortak Tez Yöneticisi: Assoc. Prof. Dr. Rıza Gürbüz Haziran 2002, 73 sayfa Bu çalışmada Al-Zn-Mg-Cu 7050 T73651 alaşımının deniz suyundaki gerilimli korozyon çatlaması incelendi. Dar en yönünde kesilen numuneler elektrokimyasal potansiyel kontrolü altında yavaş çekme yöntemiyle 3.5% NaCI çözeltisinde test edildi. Çekme hızı bütün deneylerde 1.71 xlO^s-1 olarak uygulandı. Yavaş çekme deneyleri, 10 ayrı potansiyel kademesine ek olarak açık devre konumunda da uygulandı. Deney sonuçları uzama yüzdesi, kopma zamanı, ve maksimum dayanç olarak değerlendirildi ve kırılma yüzeyleri üzerindeki irdelemelerden yararlanılarak yorumlanmaya çalışıldı.Normalize edilen değerlerin uygulanan potansiyellere karşı eğrileri çizilerek elektrokimyasal potansiyelin malzemenin uzama ve dayancı üzerindeki etkisi incelendi. 7050 T73651 alaşımının 3.5% NaCI çözeltisinde çatlamaya en duyarlı olduğu bölgenin korozyon potansiyeli olduğu gözlendi. Korozyon potansiyelinden daha soy olan potansiyel kademelerinde alaşımın anodik çözelim yoluyla gerilimli korozyon çatlamasına uğradığı saptandı. Katodik bölgede ise alaşımın belli bir potansiyel aralığında korunduğu ve havada elde edilenlere çok yaklaşan uzama ve dayanç değerlerine ulaştığı gözlendi.

Özet (Çeviri)

ABSTRACT STUDY OF SALT-WATER CRACKING BEHAVIOR OF 7050 T73651 ALUMINUM ALLOY THROUGH SLOW STRAIN RATE TESTING UNDER POTENTIOSTATIC CONTROL Kuş, Esra M.Sc, Department of Metallurgical and Materials Engineering Supervisor: Prof. Dr. Mustafa Doruk Co-Supervisor: Assoc. Prof. Dr. Rıza Gürbüz June 2002, 73 pages Stress corrosion cracking (SCC) of Al-Zn-Mg-Cu alloy 7050 T73651 in marine environment has been investigated in the present work. The alloy was tested in the short transverse direction by means of potentiostatically controlled slow strain rate (SSR) tests. 3.5% NaCI solution was used as a substitute of seawater. A strain rate of 1.71 x10"6s_l was applied. SSR tests were performed at 10 different potentials and under open circuit condition. Evaluation criteria was based on %elongation, time to failure, UTS and the fracture mode. Normalized values of %elongation, time to failure and UTS were plotted as a function of the applied potential. iii7050 T73651 exhibited the most brittle behavior when the alloy was strained under its corrosion potential. SCC through anodic dissolution was observed at potentials more noble than the corrosion potential. There is a range of cathodic potentials where the material was observed to be protected that the ductility and strength measures were improved almost to the values obtained when straining the specimen in the laboratory air.

Benzer Tezler

  1. Tez No

    898683

    Development of selective iron-based fischer-tropsch catalysts to light olefins

    Hafif olefinler için seçici demir bazli fischer-tropsch katalizörlerinin geliştirilmesi

    YASEMİN FATİH AGHDAEI

    Doktora

    İngilizce

    İngilizce

    2023

    Kimya Mühendisliğiİstanbul Teknik Üniversitesi

    Kimya Mühendisliği Ana Bilim Dalı

    PROF. DR. HÜSNÜ ATAKÜL

    DOÇ. DR. ALPER SARIOĞLAN

  2. Tez No

    653876

    Boyalara ve kaplamalara nano metal oksit katkısının fiziksel, antikorozif ve antibakteriyel etkilerinin incelenmesi

    Determination of physical, antiorrosive and antibacterial effects of nano metal oxide additives to paints and coatings

    EZGİ KIZILKONCA DURAN

    Doktora

    Türkçe

    Türkçe

    2020

    Kimyaİstanbul Teknik Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. FATMA BEDİA BERKER

  3. Tez No

    83936

    Su kirliliğinin beton borulara etkisinin araştırılması ve değerlendirilmesi

    A Investigation of the effect pollution to concrete pipe and its evalvation

    ALİ ULUCAN

    Yüksek Lisans

    Türkçe

    Türkçe

    1999

    Çevre MühendisliğiFırat Üniversitesi

    Çevre Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. AYHAN ÜNLÜ

  4. Tez No

    467593

    Ahşap yatlarda kullanılan çeşitli verniklerin farklı ağaç malzemeler üzerindeki performanslarının karşılaştırılması

    Comparison of the performance of various varnishes used in wooden yachts on different wood species

    MURAT ALTIPARMAK

    Yüksek Lisans

    Türkçe

    Türkçe

    2017

    Ağaç İşleriMuğla Sıtkı Koçman Üniversitesi

    Ağaç İşleri Endüstri Mühendisliği Ana Bilim Dalı

    DOÇ. DR. MEHMET ÇOLAK

  5. Tez No

    66591

    Etrinjit ile sülfat çöktürmesinin incelenmesi

    Sulfate removal by ettringite precipitation

    ELİF PEHLİVANOĞLU

    Yüksek Lisans

    Türkçe

    Türkçe

    1997

    Çevre Mühendisliğiİstanbul Teknik Üniversitesi

    Çevre Mühendisliği Ana Bilim Dalı

    PROF. DR. OLCAY TÜNAY

Geri Dön