Portland kompoze çimento ile aynı dayanım sınıfındaki çimentolarla üretilen harç ve betonlarda geçirgenlik ve diğer özelliklerinin araştırılması

Research on porosity and other properties of concrete and cement mortars prepared by using portland cement and portland composite cement which is at the same compressive strength class

  1. Tez No: 120759
  2. Yazar: TEOMAN SELÇUK KÖKSAL
  3. Danışmanlar: YRD. DOÇ. DR. HÜSEYİN TEMİZ
  4. Tez Türü: Yüksek Lisans
  5. Konular: İnşaat Mühendisliği, Civil Engineering
  6. Anahtar Kelimeler: Portland cement, Composite Cement, Mortar, Dough Concrete, Durability, Permeability. II
  7. Yıl: 2002
  8. Dil: Türkçe
  9. Üniversite: Kahramanmaraş Sütçü İmam Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 61

Özet

ÖZET Teoman Selçuk KOKSAL KAHRAMANMARAŞ SÜTÇÜ İMAM ÜNİVERSİTESİ FEN BİLİMLERİ ENSTİTÜSÜ İNŞAAT MÜHENDİSLİĞİ ANABİLİM DALI YÜKSEK LİSANS TEZİ ÖZET PORTLANT KOMPOZE ÇİMENTO İLE AYNI DAYANIM SIMFINDAKI ÇİMENTOLARLA ÜRETİLEN HARÇ VE BETONLARDA GEÇİRGENLİK VE DİĞER ÖZELLİKLERİNİN ARAŞTIRILMASI Teoman Selçuk KOKSAL DANIŞMAN : Yrd. Doç. Dr. Hüseyin TEMİZ Yıl : 2002, Sayfa : 51 Jüri : Yrd. Doç. Dr. Hüseyin TEMİZ Yrd. Doç. Dr. Özkan GÜVERCİN Yrd. Doç. Dr. Adil AKYÜZ Türkiye'de ve dünyada yaygın olarak kullanılan çimentonun yapı maliyeti ve dayanımı üzerinde önemli bir yeri vardır. Maliyeti düşürmek, hammadde kullanımını azaltmak, bazı atık maddeleri değerlendirmek ve çimento niteliğini iyileştirmek amacıyla değişik özelliklere sahip çimentolar üretilmiştir. Bu araştırmada, son birkaç yıldır yaygın olarak kullanılan Portland Kompoze (PKÇ/A 32.5R, PKÇ/B 32.5R ve kompoze KZÇ/A 32.5R) çimentoları ile üretilen hamur, harç ve betonların bazı özelliklerinin, Portland Çimentosu (PÇ 32.5) ile karşılaştırılması yapılmıştır. Araştırmada kullanılan çimentoların kimyasal yapılarında, katkılı çimentolarda Si02, A1203, Fe2O3; ve MgO yüzdelerinin PÇ 32.5'e göre arttığı CaO miktarının azaldığı görülmüştür. Katkılı çimentoların özgül ağırlıklarında katkısız çimentoya güre azalmalar olmuştur. Normal kıvam su miktarı, katkı oranı fazla olan çimentolarda yüksek çıkmıştır. Katkı oranının artmasına bağlı olarak priz başlama ve sona erme süreleri uzamıştır. Hacimsel genleşme değerinde ise en az genleşme KZÇ/A 32.5R türü çimento da olmuştur. Harç numunelerin Na2S04 'lü ve kükürt ortamlardaki dayanımları PÇ 32.5 hariç standartların verdiği değerlerin üzerinde çıkmıştır. Kompoze numunelerin kükürtlü ortamlardaki davranışının Portland çimentosuna güre daha iyi olduğu saptanmıştır. Beton ve harç numunelerin 7 günlük basınç dayanımlarının PÇ 32.5'li numunelere göre düşük çıktığı, 28 ve 90 günlük dayanımlarda ise PÇ 32.5'li numuneleri yakaladıkları bazılarında ise geçtikleri gözlenmiştir. Beş atmosfer su basıncı altında farklı çimento türleriyle üretilen bütün beton numunelerin suyu geçirmediği görülmüştür. Anahtar Kelimeler : Portland Çimento, Kompoze Çimento, harç, hamur, beton, dayanım, dayanıklılık, geçirgenlik.

Özet (Çeviri)

ABSTRACT Teoman Selçuk KOKSAL UNIVERSITY OF KAHRAMANMARAŞ SUTCU IMAM DEPARTMENT OF CIVIL ENGINEERING INSTITUTE OF NATURAL AND APPLIED SCIENCES MSc THESIS ABSTRACT RESEARCH ON POROSITY AND OTHER PROPERTIES OF CONCRETE AND CEMENT MORTARS PREPARED BY USING PORTLAND CEMENT AND PORTLAND COMPOSITE CEMENT WHICH IS AT THE SAME COMPRESSIVE STRENGTH CLASS Teoman Selçuk KOKSAL Supervisor : Yrd. Doç. Dr. Hüseyin TEMİZ Year : 2002, Pages: 51 Jury : Yrd. Doç. Dr. Hüseyin TEMİZ Yrd. Doç. Dr. Özkan GÜVERCİN Yrd. Doç. Dr. Adil AKYÜZ Cement, the most widely used construction material both in the world and in Turkey, has a very important role on the construction cost and on it's strength. In order to reduce the cost, to reduce the raw material usage, and to utilize waste materials, and to improve the quality, different types of cements are produced. In this research, the properties of cement paste, cement mortar and concrete, produced by using Portland Composite Cements are compared with those prepared by using Portland Cement (PC 32.5). When the proportions of chemical compositions of cements used were compared, it was seen that“Si02, AI2O3, Fe203 and MgO”in cement with high addictives were increasing, while the CaO proportion was decreasing. The amount of normal right consistency water is high in cements with high addition proportion. Concerning with the addition proportion, the initial and final setting times became longer. In the merit of volume expansion, the least expansion occurred in KZC/A 32.5 R cement. The compressive strength of mortar samples except the ones prepared by PC 32.5 reached higher values given in the standards in Na2S04 and sulfur environments. It was fixed that composite samples were better than ordinary Portland Cements in sulfur environment It was also seen that, cements with additives have less compressive strength for 7 days when compared with the ordinary Portland Cements, but for 28 and 90 days compressive strength's they could reach and sometimes exceed the Portland Cement Samples'. Under 5 atm water pressure, the concrete produced with different types of cements did not let water penetrate.

Benzer Tezler

  1. Tez No

    570722

    Sülfatlı su içerikli kum zeminlerde portland kompoze (Traslı) çimento ve portland uçucu kül çimento kullanılarak oluşturulan jet-grout kolonlarının taşıma gücüne sülfatın etkisi

    The effect of sulphate on the bearing capacity of jet-grout columns constructed by using portland composite (Pozzuolana) cement and portland fly ash cement on sand soi̇ls with sulphate water content

    SİNAN AKBAY

    Yüksek Lisans

    Türkçe

    Türkçe

    2019

    İnşaat MühendisliğiKonya Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. MUSTAFA YILDIZ

  2. Tez No

    799108

    Portland klinkeri ile üretilen kalkerli çimentonun, aynı dayanım sınıfına ait sülfat dayanımı yüksek puzolanlı, katkısız ve sr5 çimentolarının yerine kullanılabilirliğinin araştırılması

    Investigation of the usage of portland limestone cement instead of high sulfate resistance cements in same strength class which are pozzolanic, additive-free and sr5

    AHMET YİĞİT

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    İnşaat MühendisliğiKonya Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. ÜLKÜ SULTAN KESKİN

  3. Tez No

    172406

    Hızlı kür uygulanmış betonlarda bir günlük basınç dayanımı ile 28 günlük basınç dayanımı arasındaki ilişkiye katkı ve çimento türünün etkisi

    Influence of the chemical admixture and cement type on the releation of the compresive strength of concrete's one day strength gained by rapid curing and 28th day strength +

    AHMET UTKU YAZGAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2006

    İnşaat MühendisliğiAkdeniz Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF.DR. FİKRET TÜRKER

  4. Tez No

    133012

    Akıcı ve çok akıcı betonlarda kuruma büzülmesine çimento ve katkı maddesi türünün etkisi

    Influence of different cement and chemical admixture types on drying shrinkage of fluid and high fluid concretes

    NİYAZİ UĞUR KOÇKAL

    Yüksek Lisans

    Türkçe

    Türkçe

    2002

    İnşaat MühendisliğiAkdeniz Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. FİKRET TÜRKER

  5. Tez No

    120208

    Değişik tip çimentoların ve bunlardan üretilen betonların sülfat direnci

    Sulfate resistance of different types of cements and concrete produced from these cements

    GÖZDE İNAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2002

    İnşaat MühendisliğiEge Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. KAMBİZ RAMYAR

Geri Dön