Geri Dön

Yanar kovan malzemelerinin hazırlanması

Preparation of combustible cartridge materials

PDF İndir

  1. Tez No: 123383
  2. Yazar: ENİS TOLGA EROĞLU
  3. Danışmanlar: PROF.DR. AHMET R. ÖZDURAL
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya Mühendisliği, Chemical Engineering
  6. Anahtar Kelimeler: Yanar kovan, nitroselüloz, kompozit malzeme, Combustible cartridge, nitrocellulose, composite material. Advisor : Prof. Dr. Ahmet Rıfat ÖZDURAL, Hacettepe University, Department of Chemical Engineering, Chemical Engineering Division
  7. Yıl: 2002
  8. Dil: Türkçe
  9. Üniversite: Hacettepe Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 67

Özet

YANAR KOVAN MALZEMELERİNİN HAZIRLANMASI Enis Tolga EROĞLU Hacettepe Üniversitesi, Kimya Mühendisliği Bölümü, Kimya Mühendisliği Anabilim Dalı. ÖZET Bu tez çalışmasında yanar kovanların yapımına yönelik yanar keçe tabakalarının hazırlanması amaçlanmıştır. Farklı içeriklerde dört numune yapılmıştır. İlk yapılan numunenin içeriği, nitroselüloz, kraft, akrilik ve polyester lifleri (sentetik lifler), düzenleyici (difenilamin), reçine bağlayıcı (AAC 420E) ve destekleyicidir (Resin 5131). Temel alınan bu yapıdan başka nişasta ve (veya) sentetik lifler ilave edilerek veya çıkartılarak farklı özelliklerde yanar kovan malzemeleri hazırlanmıştır. Bunlar sırasıyla temel yapı, temel yapı + nişasta, temel yapı - sentetik lifler, temel yapı - sentetik lifler + nişastadır. Elde edilen farklı içerikteki numunelerin, mukavemetini ve sertliğini arttırmak için yanar kovan malzemesi üretildikten sonra iki aşamada polimerik filmle kaplanmıştır. İlk önce PVA (4 g) ve su (96 g) çözeltisi püskürtülerek kaplanmıştır. Sonra etil selüloz (5 g) ve etil asetat (100 mi) çözeltisine daldırılarak kaplanmıştır. Son numunelerin (etil selüloz kaplı) su geçirmediği, sudan etkilenmediği ve pürüzlü bir yapı oluşturduğu gözlenmiştir. Kaplamalardan önce ve de sonra numunelerde homojenlik sağlanamadığı görülmüştür. Elde edilen bütün ürünlerin mukavemeti, sertliği, kalınlığı ve kül miktarı ölçülmüştür. Bu verilerin sonucunda numune hazırlanışında aynı içerikte malzemeler kullanılmasına rağmen oldukça farklı veriler elde edilmiştir. Bu farklılık liflerin uzunluğu, sudaki minerallerin etkisi ve bulamacın bekletilme süresi ile ilgilidir. Kaplamalar öncesinde ve sonrasında deney no 5 de (içerik olarak temel alınan) en iyi değerler gözlenmiştir. Ancak diğer yapılan deneylerden de elde edilen son ürünler (kaplanmış halde) yanar kovan kapları yapımında kullanılabilecek kadar iyi sonuçlar vermiştir.

Özet (Çeviri)

PREPARATION OF COMBUSTIBLE CARTRIDGE MATERIALS Enis Tolga ERO?LU Hacettepe University, Department of Chemical Engineering, Chemical Engineering Division. ABSTRACT The aim of this thesis was to prepare felted combustible nitrocellulose boards for a probable use in the preparation of combustible cartridges. Four different samples of felted combustible nitrocellulose boards were prepared using different amounts of ingredients. The main ingredients were nitrocellulose, kraft paper, acrylic and polyester fibers, diphenylamine (stabilizer), resin binder and retention aid materials. Furthermore, is also added to the preparation medium and the acrylic and polyester fibers are removed from the recipe, so as to obtain combustible nitrocellulose boards having different properties. After the preparation of felted combustible nitrocellulose boards, they are coated with two different polymeric films in a consecutive scheme. For this purpose the samples first spray- coated with aqueous PVA solution (%4 by weight). Following spray coating, samples were dipped into a bath of ethyl acetate so as to complete the second coating stage. It was found that the second coating stage, the samples became water resistant and they possessed rough surfaces. However the samples were not homogenous both prior to the coating and after the coating. Several tests, including strength, hardness, ash content were carried out in order to characterize the samples. It was observed that the results of tests showed a wide variety among the samples. These results could be attributed to the use of different fiber lengths, slurry preparation and the purity of water used. It was found that the best combustible nitrocellulose boards, in regard of final use in combustible cartridges, were that obtained in experiment 5. However it was concluded that all boards meet the requirements of preparing combustible propellant containers for mortar applications.

Benzer Tezler

  1. Tez No

    142597

    Yeni Cami'nin akustik açıdan performans değerlendirmesi

    Evaluation of the acoustical performance of the New Mosque

    EVREN YILDIRIM

    Yüksek Lisans

    Türkçe

    Türkçe

    2003

    Mimarlıkİstanbul Teknik Üniversitesi

    Mimarlık Ana Bilim Dalı

    PROF. DR. SEVTAP YILMAZ DEMİRKALE

  2. Tez No

    752152

    Graphene based materials obtained from graphite and polyacrylonitrile based carbon fiber for energy storage and conversion systems

    Enerji depolama ve dönüşüm sistemleri için grafit ve poliakrilonitril esaslı karbon fiberden grafen tabanlı malzemelerin üretilmesi

    MEHMET GİRAY ERSÖZOĞLU

    Doktora

    İngilizce

    İngilizce

    2022

    Enerjiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF. DR. ABDÜLKADİR SEZAİ SARAÇ

    PROF. DR. YÜCEL ŞAHİN

  3. Tez No

    905898

    Construction of history through audiovisual archives in contemporary documentary: The postmodern history of migration in Love Deutschmarks and Death

    Çağdaş belgeselde sesli-görüntülü arşivler aracılığıyla tarihin yeniden inşası: Aşk, Mark ve Ölüm'de göçün postmodern tarihi

    AYŞE GÜLSEZER

    Yüksek Lisans

    İngilizce

    İngilizce

    2024

    Radyo-TelevizyonKadir Has Üniversitesi

    İletişim Bilimleri Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ ESİN PAÇA CENGİZ

  4. Tez No

    75051

    Ballistic performance and impact behavior of alumina armor ceramic

    Alümina zırh seramiklerinin balistik performansı ve çarpışma davranışı

    MURAT VURAL

    Doktora

    İngilizce

    İngilizce

    1998

    Uçak Mühendisliğiİstanbul Teknik Üniversitesi

    Havacılık ve Uzay Mühendisliği Ana Bilim Dalı

    PROF. DR. M. ZEKİ ERİM

  5. Tez No

    888485

    Un-claiming the experience of the ends of the projected image: The loss and the survivals of architectural drawing in the shadow of projection

    İzidüşürülmüş imgenin son deneyimleri üzerindeki haklardan feragat etmek: İzdüşümün gölgesinde mimari çizimin yitimleri ve hayatta kalışları

    EMİNE BAHAR AVANOĞLU

    Doktora

    İngilizce

    İngilizce

    2024

    Mimarlıkİstanbul Teknik Üniversitesi

    Mimarlık Ana Bilim Dalı

    PROF. DR. AYŞE ŞENTÜRER

Geri Dön