Yapı malzemelerinin sol-jel yöntemi ile su itici kaplanması
Water repellent coating of masonry materials with sol-gel method
- Tez No: 132992
- Danışmanlar: PROF. DR. ERTUĞRUL ARPAÇ
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2002
- Dil: Türkçe
- Üniversite: Akdeniz Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 119
Özet
ÖZET YAPI MALZEMELERİNİN SOLJEL YÖNTEMİ İLE SU İTİCİ KAPLANMASI Muharrem GÜN Yüksek lisans Tezi, Kimya Anabilim Dalı Danışman : Prof. Dr. Ertuğrul ARPAÇ Mayıs 2002, 107 Sayfa Bu çalışmada, yapı malzemelerinin bünyesine su girişi önlenmeye çalışılmıştır. Bunun için Sol-jel yöntemi kullanılarak tuğla, beton, gazbeton numuneleri, faklı oranlarda organik olarak modifiye edilmiş silanlar (Metiltrietoksisilan (MTEOS), Propiltrimetoksisilan (PTMOS), Feniltrietoksisilan (pHTEOS), Viniltrimetoksisilan (VTMOS)) içeren çözeltilerle kaplanmıştır. Kaplama çözeltisi olarak toplam silan yüzdesi %10 ve %30 olan, organik olarak modifiye silan: Tetraetoksisilan (TEOS) mol oranı 4:1 olan ve TEOS 'a göre mol oranı %5 ve %10'tak 3,3,4,4,5,5,6,6,7,7,8,8- Tridekaflorooktiltrietoksisilan (F-Silan) içeren çözeltiler kullanılmıştır. Kaplamada kullanılan silanların hidrolizi için 0,1 N HC1, çözgen olarak da mutlak etanol kullanılmıştır. Elde edilen kaplamaların performansla rının kıyaslanması için tuğla, beton, gazbeton numuneler farklı oranlarda ticari kaplama çözeltileri ile de kaplanmıştır. Bütün kaplamalar numunelere vakumlu ve vakumsuz olmak üzere iki ayrı ortamda uygulanmıştır. Kaplanan numunelerin su absorbsiyonları, oda sıcaklığında bünyelerinde bulundurabildikleri nem oranları belirlenmiş ve kondenzasyon testleri gerçekleştirilmiştir. Ayrıca, farklı çözeltilerle kaplanan yüzeylerdeki su tutunma açılan goniometre ile ölçülmüş ve birbirleri ile kıyaslanmıştır. Çalışma sonucunda, yapı malzeme yüzeylerine uygulanan su itici kaplamaların su absorbsiyonunu engellediği gözlenmiştir. ANAHTAR KELİMELER : Sol-gel, Su itici kaplama, Alkilsilan, Flor Silan, Tuğla, Beton, Gazbeton JÜRİ : Prof. Dr. Ertuğrul ARPAÇ Prof. Dr. Suphi KORMALI ^/>J?Ûj}£- Yrd. Dç. Dr. Birsen BÜYÜKT
Özet (Çeviri)
ABSTRACT WATERREPELLENT COATING OF MASONRY MATERIALS WITH SOL-GEL METHOD Muharrem GÜN M.S. Thesis, Department of Chemistry Advisor : Prof. Dr. Ertuğrul ARPAÇ May 2002, 107 pages In this study, it is aimed to prevent water absorbtion of the masonry materials. Brick, concrete, and gas concrete metarials were coated with solutions, which contains organically modified silanes (ORMOSIL) ((Methyltriethoxysilane (MTEOS), Propyltrimethoxysilane (PTMOS), Phenyltriethoxysilane (pHTEOS), Vmyltrimethoxysilane (VTMOS)) in different ratios, using sol-gel method. Coating solutions were prepared in concentration of 10-30 %in grams of total silane, (ORMOSIL and Tetraethoxysilane (TEOS)) and have a ratio 4:1 for ORMOSIL:TEOS. Also solutions of 3,3,4,4,5,5,6,6,7,7,8,8-Tridecafluorooctyltriethoxysilane (F-Silanes) in concentration 5 % and 10 % in moles of TEOS, were used for coating. 0,1 N HC1 was used to hydrolyze silanes and absolute ethyl alcohol was used as a solvent. To compair the performance of the prepared coatings brick, concrete, and gas concrete materials were also coated with commercial coating solutions in different ratio. All coating were applied to the samples in two conditions as vacuumed and non- vacuumed medium. Water absobrtion, moisture content at room temperature, condensation tests of coated surface were determined. Additionally, contact angles of water on surfaces coated with different solutions were measured with goniometer and the results were compared. It is concluded that the all hydrophobic coatings applied to the masonry materials prevented water penetration. KEY WORDS : Sol-gel, Water reppellent coating, Alkylsilane, Flour Silane, Brick, Concrete, Gas concrete COMMITTEE : Prof. Dr. Ertuğrul ARPAÇ Ş/ Prof. Dr. Suphi KORMALI ^//^>^y?A^~- Yrd. Dç. Dr. Birsen BÜYÜKTAŞ Jsh
Benzer Tezler
- Silika içerikli aerojelin sol-jel yöntemi ile sentezlenmesi ve mimari yapı malzemesinin performansının geliştirilmesi
Synthesising silica aerogel by sol-gel method and devoloping the performance of architectural building material
TUBA ARKAN DEMİRÖRS
- Mimari yapılar için çevre dostu kompozit malzemelerin geliştirilmesi
Development of eco-friendly composite materials for architectural structures
REYHAN KOÇ
Yüksek Lisans
Türkçe
2024
Bilim ve TeknolojiNevşehir Hacı Bektaş Veli ÜniversitesiNanobilim ve Nanoteknoloji Ana Bilim Dalı
PROF. DR. CEMAL ÇARBOĞA
DR. ÖĞR. ÜYESİ FATMA ZEHRA KOÇAK
- Yakın kızılötesi yansıtıcı, hidrofobik ve anti-bakteriyel yüzey özelliklerine sahip multifonksiyonel kaplamalı ısı yalıtım malzemelerinin üretimi
Production of multifunctional coated thermal insulation materials with near-infrared reflective, hydrophobic and anti-bacterial surface properties
EMRE YAVUZ
Doktora
Türkçe
2022
KimyaAkdeniz Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. NİYAZİ UĞUR KOÇKAL
- UV ışınlarıyla sertleşebilen flor içeren hibrit kaplama uygulamaları ve karakterizasyonu
Applications and characterization of fluor containing UV curable hybrid coatings
OKAN ÖZDEMİR
Yüksek Lisans
Türkçe
2013
Polimer Bilim ve TeknolojisiMarmara ÜniversitesiMetal Eğitimi Ana Bilim Dalı
YRD. DOÇ. DR. MUSTAFA ÇAKIR
- Y2O3 ve Yb+3:Y2O3 partiküllerinin üretimi ve karakterizasyonu
Y2O3 and Yb+3:Y2O3 particles production and characterization
ELİF EMİL
Yüksek Lisans
Türkçe
2017
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. SEBAHATTİN GÜRMEN