Patlama kaynağı yöntemi ile bakır-paslanmaz çelik malzemelerinin birleştirilmesi ve ara yüzeyin mekanik-mikroyapı özelliklerinin incelenmesi
Bonding of copper and stainless steel by using explosion welding and investigation of mechanical-microstructural properties of interface
- Tez No: 133431
- Danışmanlar: YRD. DOÇ. DR. BEHÇET GÜLENÇ
- Tez Türü: Doktora
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2003
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 130
Özet
Bu çalışmada, bakır ve paslanmaz çelik levhaların, farklı oranlarda patlayıcı miktarı ve ara boşluk mesafeleri kullanılarak patlamalı kaynak yöntemi ile birleştirilebilirlikleri araştırılmıştır. Patlama kaynağı ile bakır ve paslanmaz çelik malzemelerin iyi birleşme özellikleri sergileyerek birleştirilebildiği deneysel çalışmalar sonunda tespit edilmiştir. Birleşme ara yüzeyinde intermetalik bileşenler oluşmamıştır. Patlayıcı oranının ve ara boşluk mesafesinin arttığında, doğrusal biçimdeki birleşme ara yüzeyinin dalgalı bir birleşme ara yüzeyi haline dönüştüğü görülmüştür. Patlayıcı oranının ve ara boşluk mesafesinin artışıyla beraber, oluşan dalgaların boylarında ve genliklerinde bir artış olmuştur. Çarpışmadan kaynaklanan deformasyondan dolayı levhaların birleşme ara yüzeyleri ve dış yüzeylerindeki sertlik değerlerinde bir artışın meydana geldiği tespit edilmiştir. Patlayıcı oranı ve ara boşluk mesafesinin artması ile beraber oluşan dalgalanmadan dolayı birleşme yüzey alanının arttığı ve çekme - makaslama testlerinde ayrılmaların oluşmadığı belirlenmiştir. Birleştirilmiş numunelere uygulanan farklı çaplardaki eğme testleri sonucunda, birleşme ara yüzeyinde herhangi bir hataya rastlanılmamıştır. Birleştirilen levhalara uygulanan SEM-EDS analizlerinden, birleşme ara yüzeyinde difüzyonun oluşmadığı fakat farklı sürelerde yapılan ısıl işlemler ile difüzyonun oluşabileceği tespit edilmiştir.Anahtar Kelimeler : Patlama kaynağı, Bakır-paslanmaz çelik, Patlayıcı oranı, Araboşluk mesafesi.
Özet (Çeviri)
In this study, bonding ability of copper and steel with explosion welding was investigated using different ratios of explosive and different stand-off distance. Experimental studies showed out that, copper and stainless steel can be bonded with a good quality of bonding properties with explosion welding. In the bonding interface, intermetallics were not formed. It was observed that, when explosive ratio and stand-off distance were increased smooth bonding interface was transformed to a wavy bonding interface. As the ratio of explosive and stand-off distance increase, the amplitude and wavelength of wave were increased. It was found that, hardness of bonding interface and outer face of plates were increased because of deformation that was originating from impact the effect. Total interface area increased as a result of wavy interface which was caused by increased explosive ratio and stand-off distance. In additio, wavy interfaces did not seperate after tensile-shearing test Bending tests applied on bonded samples had different diameters indicated that interfaces of the bonded samples have not any defect. Scanning Electron Microscopy EDS analyses showed that diffusion did not take place between bonding plates, however, diffusion was observed after annealing of the bonded samples for different times.KeyWords : Explosion welding, Copper-stainless steel, Explosive ratio, Stand-off distance
Benzer Tezler
- Synthesis of silicon-graphene composite anode via magnesiothermic reduction of silica fume for high-performance lithium-ion batteries
Yüksek performanslı lityum-iyon bataryalar için silisyum-grafen kompozit anot malzemesinin silika dumanının magneziotermik yolla indirgenmesi ile sentezlenmesi
NİHAT FATİH KAYACIOĞLU
Yüksek Lisans
İngilizce
2023
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. REHA YAVUZ
- Yangın riski taşıyan açık alanlar için CBS tabanlı, bulut altyapılı, yüksek hassasiyetli, nanofotonik erken yangın tespit sistemi tasarımı ve uygulaması
Design and implementation of a GIS based, cloud substructured, high sensitive, nanophotonic early fire detection system for fire risk areas
YÜCEL GÜLLÜCE
Doktora
Türkçe
2019
Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve Kontrolİstanbul Teknik ÜniversitesiBilişim Uygulamaları Ana Bilim Dalı
PROF. DR. RAHMİ NURHAN ÇELİK
- Multimodal vision-based driver monitoring system in autonomous vehicles
Çok modlu görüntü tabanlı sürücü izleme sistemi otonom araçlarda
LEILA GHASEMZADEH
Yüksek Lisans
İngilizce
2023
Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve Kontrolİstanbul Teknik ÜniversitesiBilgisayar Bilimleri Ana Bilim Dalı
YRD. DOÇ. DR. SEFER BADAY
- Design of fuzzy logic controller for fighter aircraft fuel tank pressurization
Muharip uçakların yakıt tankı basınçlandırması için bulanık mantık kontrolörü tasarımı
TUNA TİLKİOĞLU
Yüksek Lisans
İngilizce
2020
Endüstri ve Endüstri MühendisliğiHacettepe ÜniversitesiEndüstri Mühendisliği Ana Bilim Dalı
PROF. DR. ÖZLEM MÜGE TESTİK
- Titanyum levhaların patlamalı kaynak yöntemi ile farklı metallere birleştirilmesi ve arayüzey özelliklerinin incelenmesi
Investigation of titanium plates of different metals by explosive welding method and investigation of their interface properties
NİZAMETTİN KAHRAMAN
Doktora
Türkçe
2003
Metalurji MühendisliğiGazi ÜniversitesiMetal Eğitimi Ana Bilim Dalı
Y.DOÇ.DR. BEHÇET GÜLENÇ