Fonksiyonel derecelendirilmiş malzemelerden yapılmış termal bariyer kaplamalarındaki kenar çatlaklarının süreksiz rejimde sonlu elemanlar metodu ile incelenmesi

Finite element analysis of edge cracks in the thermal barrier coating's made of functionally gradient materials in transient regime

  1. Tez No: 153040
  2. Yazar: EMİNE GÜLİN DİMİTOKA
  3. Danışmanlar: Y.DOÇ.DR. BORA YILDIRIM, Y.DOÇ.DR. SERKAN DAĞ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Termal bariyer kaplamaları, Fonksiyonel derecelendirilmiş malzemeler, gerilim şiddet çarpanı, sonlu elemanlar metodu, zenginleştirilmiş sonlu elemanlar, süreksiz rejimde ısıl analiz ıı, Thermal barrier coatings, Functionally gradient materials, Finite elements, crack, stress intensity factor, enriched finite elements, transient thermal analysis. IV
  7. Yıl: 2004
  8. Dil: Türkçe
  9. Üniversite: Eskişehir Osmangazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: 50

Özet

ÖZET Termal bariyer kaplamaları malzemenin çalışma sıcaklığını yükselterek sistemin verimini arttırmak amacı ile kullanılır. Genelde metal alt tabakanın üzerine homojen seramik kaplama şeklinde uygulanmaktadır. Bu tür kaplamalarda çalışma esnasında görülen en önemli problem, metal alt tabaka ile seramik kaplamanın termal genleşme sabitlerinin farklı olması nedeniyle ortaya çıkan çatlaklar ve metal/seramik ara yüzündeki ayrılmalardır. Sözkonusu çatlakları ve ayrılmaları önlemek için fonksiyonel derecelendirilmiş malzemelerden yapılmış kaplamalar geliştirilmiştir. Bu tür kaplamalarda malzeme özellikleri kaplama kalınlığı boyunca fonksiyonel olarak değiştirilmekte ve bu sayede kaplama ile alt tabaka arasındaki uyumsuzluk ve termal gerilmeler dolayısıyla arayüzde çatlak oluşma ihtimali en düşük dereceye indirilebilmektedir. Bu tür fonksiyonel derecelendirilmiş ve konvensiyonel kaplamalarda çok sık görülen diğer bir problem de üretim veya çalışma sırasında kaplamanın üst yüzeyinde oluşan kenar çatlaklarıdır. Bu tür çatlaklar özellikle soğuma sırasında ilerlemekte, kaplamanın işlevini yapmasını engellemekte ve hatta dökülmesine neden olmaktadır. Bu çalışmada yüksek çalışma sıcaklığındaki uçak türbinlerinin ana malzemesi olan titanyum alaşımı Tİ-6A1-4V alt tabakası üzerine kaplanmış Zr02/Ti-6A1-4V den oluşan ve üst yüzeyinde bir kenar çatlağı içeren fonksiyonel derecelendirilmiş malzemeden yapılmış; farklı kaplama tipleri için, soğuma sırasında süreksiz rejimde özel olarak geliştirilmiş sonlu elemanlar metodu kullanılarak gerilim şiddet çarpanları hesaplanmıştır. Bulunan çarpanlar karşılaştırılarak yorumlanmıştır.

Özet (Çeviri)

ABSTRACT Thermal Barrier Coatings are used for rising system efficiency by increasing working temperature. Generally they are applied as homogeneous ceramic coatings over metal substrate. The most important problem in that kind of coatings is separations at interface of the metal/ceramic and cracks during operation because of the thermal expansion constant difference between metal substrate and ceramic coating. To prevent these cracks and separations“Functionally Gradient Materials”coatings are improved. In these coatings the material characteristics are changing functionally through the coatings thickness. Consequently, mismatch and thermal stress between coating and substrate and so possibility of occurance crack at interface of substrate/coating can be minimized. Another problem that appears frequently in this kind of functionally gradient and conventional coatings is edge crackings at upper surface of coatings during production or operation. That kind of cracks are growing up especially while getting cooller and this situation causes to ruin the function of thermal barrier coatings and even may cause of the spallation the coating. In this study, stress intensity factors for an edge crack on Zr02/Ti-6A1-4V. FGM coatings of Tİ-6A1-4V substrates are calculated in transient regime during cool down from operating temperature. Special finite elements developed for traded materials are used.

Benzer Tezler

  1. Fonksiyonel derecelendirilmiş malzeme ve sandviç plakların patlama yükü altındaki titreşim analizi

    Vibration analysis of functionally graded materials and sandwich plates under blast load

    ÖMER BURAK TUNCA

    Yüksek Lisans

    Türkçe

    Türkçe

    2009

    Metalurji Mühendisliğiİstanbul Teknik Üniversitesi

    Uçak ve Uzay Mühendisliği Ana Bilim Dalı

    DOÇ. DR. VEDAT ZİYA DOĞAN

  2. Fonksiyonel derecelendirilmiş bir plağın analizi

    Analysis of functionally graded plates

    OZAN ÖZARSLAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2007

    Uçak Mühendisliğiİstanbul Teknik Üniversitesi

    Disiplinlerarası Ana Bilim Dalı

    Y.DOÇ.DR. VEDAT ZİYA DOĞAN

  3. Santrifüj döküm ile üretilmiş fonksiyonel derecelendirilmiş malzemenin fretting yorulması davranışının deneysel ve nümerik analizi

    Experimental and numerical analysis of fretting fatigue behavior of functionally graded material manufactured by centrifugal casting

    ARZUM ULUKÖY

    Doktora

    Türkçe

    Türkçe

    2011

    Makine MühendisliğiPamukkale Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. MUZAFFER TOPÇU

    PROF. DR. SÜLEYMAN TAŞGETİREN

  4. Fonksiyonel derecelendirilmiş malzemeden üretilen plakların mekanik ve ısıl yükler altındaki burkulma analizi

    Buckling analysis of functionally graded plates under thermal and mechanical loads

    İBRAHİM UTKU AKTAŞ

    Yüksek Lisans

    Türkçe

    Türkçe

    2021

    Havacılık Mühendisliğiİstanbul Teknik Üniversitesi

    Uçak ve Uzay Mühendisliği Ana Bilim Dalı

    PROF. DR. VEDAT ZİYA DOĞAN

  5. Düzgün olmayan kalınlıktaki fonksiyonel derecelendirilmiş diskin termal yük altındaki gerilme analizi

    Stress analysis of functionally graded discunder thermal load

    AYŞEGÜL ÖZGÜR

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Makine MühendisliğiAmasya Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    PROF. DR. İBRAHİM KELEŞ