Effects of chain extension and branching on the properties of recycled poly (ethylene terephthalate)-organoclay nanocomposites
Zincir uzamasının ve dallanmasının geri kazanılmış poli(etilen tereftalat)-organokil nanokompozitlerinin özelliklerine etkileri
- Tez No: 153542
- Danışmanlar: PROF. DR. ÜLKÜ YILMAZER
- Tez Türü: Yüksek Lisans
- Konular: Kimya Mühendisliği, Chemical Engineering
- Anahtar Kelimeler: Nanokompozit, Termoplastik Nanokompozitler, Atık PET, Montmorillonit, Zincir Uzaması/Dallanması vıı, Nanocomposite, Thermoplastic Nanocomposites, Recycled PET, Montmorillonite, Chain Extension/Branching
- Yıl: 2004
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
oz ZİNCİR UZAMASININ VE DALLANMASININ GERİ KAZANILMIŞ POLİ(ETİLEN TEREFTALAT)-ORGANOKİL NANOKOMPOZİTLERİNİN ÖZELLİKLERİNE ETKİLERİ Keyfoğlu, Ali Emrah Yüksek Lisans, Kimya Mühendisliği Bölümü Tez Yöneticisi : Prof. Dr. Ülkü Yılmazer Haziran 2004, 136 sayfa Bu çalışmada zincir uzaması ve dallanmanın, geri kazanılmış PET ve organik olarak modifiye edilmiş kil ile hazırlanan nanokompozitlerin özellikleri üzerindeki etkisi incelenmiştir. Zincir uzatma ve dallandırma kimyasalı olarak maleik anhidrit (MA) ve piromellitik dianhidrit (PMDA) kullanılmıştır. Nanokompozit numuneleri çift vidalı ekstrüzyonu takiben, enjeksiyonla kalıplama yöntemiyle hazırlanmıştır. Geri kazanılmış PET, organik kil oram ağırlıkça %2, %3 ve %4 olacak şekilde organik olarak modifiye edilmiş montmorilloniüe karıştırılmıştır. İkinci ekstrüzyon basamağında ağırlıkça % 0.5, 0.75 ve 1 oranlarında MA veya PMDA ilk ekstrüzyondan elde edilen ürünlere eklenmiştir, ikinci basamağın reaktif ekstrüzyon olmasından dolayı, anhidritler, vida hızının etkisini gözlemlemek için farklı vida hızlarında (75, 150 ve 350 devir/dakika) eklenmiştir. vıXRD analizleri, kil tabakaları arasındaki mesafenin, polimerle işlendikten sonra yan açılmış bir yapının elde edildiğini belirten bir şekilde 19.21 A dan 28-34 A' a çıktığım göstermiştir. PMDA, MA ve kil miktarıyla beraber vida hızının kil tabakaları arasındaki mesafeyi etkilemediği gözlenmiştir. İlk ekstrüzyon basamağında, ağırlıkça %3 kil içeren nanokompozitler ara yüzeyde iyi yapışmayı gösterecek şekilde Young modülünde önemli bir artış ve kopmadaki uzamada azalma sağlamıştır. Zincir uzatıcı ajanların eklenmesinden sonra, MA ve PMDA'nın molekül ağırlığında artış ve dallanmaya bağlı olarak mekanik özellikleri iyileştirdiği gözlenmiştir. Düşük oranlarda PMDA'nın daha etkili olduğu gözlenmiştir; buna bağlı olarak PMDA'mn daha etkili bir zincir uzatıcı olduğu söylenebilir. DSC analizi ile MA'nın camsı geçiş sıcaklığım ve erime sıcaklığını PMDA' ya göre daha çok arttırdığı gözlenmiştir.
Özet (Çeviri)
ABSTRACT EFFECTS OF CHAIN EXTENSION AND BRANCHING ON THE PROPERTIES OF RECYCLED POLY(ETHYLENE TEREPHTHALATE)-ORGANOCLAY NANOCOMPOSITES Keyfoğlu, Ali Emrah M.S., Department of Chemical Engineering Supervisor : Prof. Dr. Ülkü Yılmazer June 2004, 136 pages In this study, the effects of chain extension and branching on the properties of nanocomposites produced from recycled poly(ethylene terephthalate) and organically modified clay were investigated. As the chain extension/branching agent, maleic anhydride (MA) and pyromellitic dianhydride (PMDA) were used. The nanocomposites were prepared by twin-screw extrusion, followed by injection molding. Recycled poly(ethylene terephthalate), was mixed with 2, 3 and 4 weight % of organically modified montmorillonite. During the second extrusion step, 0.5, 0.75 or 1 weight % of MA or PMDA was added to the products of the first extrusion. As the second extrusion step is reactive extrusion, the anhydrides were added at three different screw speeds of 75, 150, 350 rpm, in order to observe the change of properties with the screw speed. IVXRD analysis showed that, the interlayer spacing of Cloisite 25A expanded from 19.21 A to about 28-34 A after processing with polymer indicating an intercalated structure. PMDA, MA and organoclay content as well as the screw speed did not have a recognizable effect on interlayer distance. In the first extrusion step, nanocomposites containing 3% organoclay content gave significant increase in Young's modulus and decrease in elongation to break values indicating good interfacial adhesion. After the addition of chain extenders, it was observed that both MA and PMDA gave rise to improved mechanical properties of the nanocomposite owing to the branching and chain extending effects that increase the molecular weight. However, PMDA gave better mechanical properties at lower content which makes it a more effective chain extender. DSC analysis showed that MA was more effective in increasing the glass transition temperature and melting temperature in comparison to PMDA.
Benzer Tezler
- Elektrik enerji iletim şebekelerinin optimal genişletme planlaması
Optimal expansion planning of power transmission networks
NAZİF HÜLAGÜ SOHTAOĞLU
Doktora
Türkçe
1994
Elektrik ve Elektronik Mühendisliğiİstanbul Teknik ÜniversitesiPROF.DR. NESRİN TARKAN
- Dallanmış ve dendrimer makromoleküler yapıların istatistiki termodinamiği
Statistical thermodynamics of branched and dendrimer macromolecular structures
MUSTAFA ASLAN
Doktora
Türkçe
2009
Polimer Bilim ve TeknolojisiMarmara ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. UĞUR YAHŞİ
- Total diz artroplastisi sonrası kapalı kinetik zincir egzersizlerinin fonksiyonel kapasite, diz ekleminin fonksiyonelliği, diz ekstansör kaslarının kuvveti, diz eklemi hareket açıklığı, ağrı ve ödem üzerine etkisinin incelenmesi: Randomize kontrollü çalışma
Investigation of the effects of closed kinetic chain exercises on functional capacity, knee joint functionality, knee extensor muscle strengthi range of motion, pain and edema after total knee arthroplasty: A randomized controlled trial
SUDE ÖZTURHALLI
Yüksek Lisans
Türkçe
2026
Fiziksel Tıp ve Rehabilitasyonİstanbul Aydın ÜniversitesiFizyoterapi ve Rehabilitasyon Ana Bilim Dalı
DR. ÖĞR. ÜYESİ GÖZDE BAŞBUĞ
- Elektronik veri değişimi (EDI) uygulamalarının tedarik zinciri yönetimindeki rolü, ticari ilişkilere etkisinin Türkiye'deki durumu ve kavramsal model önerisi
The Role of EDI (electronic data interchange) application in supply chain and it's effects on trading partner relationships in Turkey and proposed conceptual model
AYÇA BABA
Yüksek Lisans
Türkçe
2003
Endüstri ve Endüstri MühendisliğiÇukurova ÜniversitesiEndüstri Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. OYA YÜREĞİR
- Hemofilik bireylerde denge ve yürümenin geliştirilmesinde kapalı kinetik zincir egzersizlerine karşın proprioseptif egzersizlerin etkinliğinin karşılaştırılması
Comparison of efficiency of closed kinetic chain exercises versus proprioceptive exercises in improving balance and gait in people with hemophilia
TUĞÇE POYRAZ İŞLEYEN
Doktora
Türkçe
2025
Fizyoterapi ve Rehabilitasyonİstanbul Üniversitesi-CerrahpaşaFizyoterapi ve Rehabilitasyon Ana Bilim Dalı
PROF. DR. ELA TARAKCI