İyonik poli (N.N dimetilakrilamid-ko-akrilamid) hidrojellerinin sentezi ve şişme davranışları
Synthesis and characterization of macroporous and thermo-sensitive poly (N-isopropylacrylamide-co-acrylamide) hydrogels
- Tez No: 166033
- Danışmanlar: DOÇ.DR. TUNCER ÇAYKARA, PROF.DR. BAKİ ERDOĞAN
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Ionic Hydrogel, swelling, pH-sensitive Page Number : 69 Advisers : Prof. Dr. Baki Erdoğan, Assoc. Prof. Dr. Tuncer Çaykara
- Yıl: 2005
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Ill İYONİK POLİ [N,N DİMETİLAKRİLAMİD- KO- AKRİLAMİD] HİDROJELLERİNİN SENTEZİ VE ŞİŞME DAVRANIŞLARI (Yüksek Lisans Tezi) İlkay AKÇAKAYA GAZİ ÜNİVERSİTESİ FEN BİLİMLERİ ENSTİTÜSÜ Haziran 2005 ÖZET Bu çalışmada iyonik P(DMAAm-ko-AAm) hidrojelleri, %0- ile %14,8 arasında değişen mol oranlarında itakonik asit (IA); N,N- Dimetilak- rilamid (DMAAm) ve akriamid (AAm) monomerleri, N,N'-metilen bisakrilamid m(BAAm) çapraz bağlayıcısı ve amonyum persülfat (APS)- N,N,N',N'-tetrametiletilendiamin (TEMED) başlatıcı sistemi kullanılarak sulu çözeltide radikalik polimerizasyon reaksiyonu ile 22°C de sentezlenmiştir. Sentezlenen bu iyonik poli[N,N-Dimetilakrilamid-ko- akriamid] hidrojellerinin şişme davranışlarına pH, iyonik şiddet ve çözücü bileşiminin etkisi incelenmiştir. pH 2.0- 9.0'daki denge şişme değerleri Mc ve % parametrelerinin belirlenmesinde kullanılmıştır. Teorik olarak hesaplanan ve deneysel olarak bulunan denge şişme değerleri karşılaştırılmıştır. Farklı pH'daki diprotik asit içeren hidrojellerin denge şişme değerlerinin önceden bildirilmesinde kullanılan teorini uygun olduğu görülmüştür. Bilim Kodu Anahtar Kelime Sayfa Adedi Tez Yöneticileri 405.02.01 İyonik hidrojel, şişme, pH duyarlı 69 Prof. Dr. Baki Erdoğan, Doç. Dr. Tuncer Çaykara
Özet (Çeviri)
IV SYNTHESIS AND SWELLING BEHAVIOUR OF IONIC POLY [N,N DIMETHYLACRYLAMIDE- CO- ACRYLAMIDE] HYDROGELS (M. Sc. Thesis) İlkay AKÇAKAYA GAZİ UNIVERSITY INSTITUTE OF SCIENCE AND TECHNOLOGY June 2005 ABSTRACT In this study, the ionic hydrogels were prepared by free-radical crosslinking polymerization of aqueous solutions containing itaconic acid (IA) of varying concentration between 0 and 14,8 mole %, N,N dimethylacrylamide (DMAAm) and acrylamide (AAm) monomers, N,N'- methylenebis(acrylamide) (MBAAm) as the crosslinker, ammonium persulfate (APS) as the initiator and N,N,N\N'-tetramethylethylene- diamine (TEMED) as the activator at room temperature. Effect of pH, ionic strength, temperature and solvent compositions on the swelling behaviour of ionic poly[N,N Dimethylacrylamide-co- acrylamide] hydrogels were studied. The equilibrium swelling values at pH 2- pH 9 were used determination of Mc and % parameters. The results of swelling measurements were compared with the theory of swelling equilibrium. It was shown that the theory satisfactory predicts the equilibrium swelling of hydrogels with diprotic acid content in the buffer solutions of pH. Science Code : 405.02.01
Benzer Tezler
- Design of biopolymer-based advanced functional materials
Biyopolimer esaslı gelişmiş fonksiyonel malzemelerin tasarımı
SENA ÇİFTBUDAK
Yüksek Lisans
İngilizce
2022
Kimyaİstanbul Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. NERMİN ORAKDÖĞEN
- İlaç içeren NIPAAM hidrojellerinin salınım kinetiğinin incelenmesi
Investigation of the in vitro drug release kinetics of PNIPAAM hydrogels
CEYDA ŞİMŞEK
- Gözenekli, iyonik süper absorban polimer jellerin hazırlanması ve karakterizasyonu
The preparation and characterization of porous and ionic super absorbent polymer gels
AYŞEGÜL GÖKALP
Yüksek Lisans
Türkçe
2009
Kimya Mühendisliğiİstanbul ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. GÜLTEN GÜRDAĞ
- Swelling, elasticity and inhomogeneity of poly(N,N-dimethylacrylamide) hydrogels
Poli(N,N-dimetilakrilamid) hidrojellerinin şişme, elastisite ve inhomojenite özellikleri
NERMİN ORAKDÖĞEN
Doktora
İngilizce
2006
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF.DR. OĞUZ OKAY
- Mechanically strong hyaluronic acid-based hydrogels
Yüksek mekanı̇k dayanımlı hyalüronı̇k ası̇t hı̇drojellerı̇
BURAK TAVŞANLI