Carbon supported and surfactant stabilized metal nanoparticle catalysts for direct methanol fuel cells
Doğrudan metanol yakıt pilleri için karbon destekli ve sürfaktantla stabilize edilmiş metal nanokatalizörlerin hazırlanması ve analizi
- Tez No: 167025
- Danışmanlar: DOÇ. DR. GÜLSÜN GÖKAĞAÇ
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Doğrudan Methanol Yakıt Pilleri, Direct Methanol Fuel Cells, Platinum and Platinum-Ruthenium Nanoparticles, Carbon-Supported Thiol Stabilized Catalysts, Cyclic Voltammetry, Transmission Electron Microscopy, X-ray Photoelectron Spectroscopy
- Yıl: 2005
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: 92
Özet
ÖZ DOĞRUDAN METANOL YAKIT PİLLERİ İÇİN KARBON DESTEKLİ VE SÜRFAKTANTLA STABİLİZE EDİLMİŞ METAL NANOKATALİZÖRLERİN HAZIRLANMASI VE ANALİZİ Çelik, Çağlar Yüksek Lisans, Kimya Bölümü Tez Yöneticisi: Doç. Dr. Gülsün Gökağaç Ağustos 2005, 72 sayfa Son yıllarda, karbon destekli sürfaktantlar, örneğin 1-dekantiol, oktadekantiol, ile stabilize edilmiş platin ve platin/rutenyum maddeleri üzerinde çalışmalar yapılmıştır. Bu tez çalışmasında ilk kez 1-hegzantiol organik stabilizatörü kullanılarak, karbon destekli ve bu sürfaktantla stabilize edilmiş platin ve platin/rutenyum nanoparçacık katalizörleri hazırlanmıştır. Bu yeni katalizörler, doğrudan metanol yakıt pili sisteminde kullanılan metanolün yükseltgenme tepkimesinde kullanılmışlardır. Hazırlanan katalizörlerin doğasının aydınlatılmasında dönüşümlü voltametre, X-ışınlan fotoelektron spektroskopisi ve transmisyon (geçirmeli) elektron mikroskopu tekniklerinden faydalanılmıştır. Sıcaklığın ve zamanın katalitik aktiviteye olan etkisi incelenmiş ve en aktif katalizörün, karbon destekli, 1-hegzantiol ile stabilize edilmiş ve 200°C'de 5 saat ısıtılmış olan platin nanoparçacık içeren katalizör olduğu bulunmuştur. Platin nanoparçacıklann çapı ~ 10 nm olarak ölçülmüştür. vıMetal nanoparçacıkların boyutlarının ve karbon destek üzerindeki dağılımlarının, Pt/Ru yüzey kompozisyonunun, Pt(0), Pt(H) ve Pt(TV) türlerinin bağıl değerlerinin, sürfaktatların metal nanoparçacık yüzeyinden uzaklaşıp uzaklaşmamalarının hazırlanan maddelerin katalitik aktiviteleri üzerinde oynadığı rol saptanmıştır. Hazırlanan karbon destekli 1-hegzantiol ile stabilize edilmiş Pt7sRu25 ve Pt97Ru3 nanoparçacık içeren katalizörlerin aktivitelerinin, karbon destekli 1- hegzantiol ile stabilize edilmiş Pt nanoparçacık içeren katalizörün aktivitesinden oldukça düşük olduğu gözlenmiştir. Bunun nedeni, stabilizator tabakasının metal etrafından yeterince uzaklaştırılmamasıyla ve Pt(ü) ve Pt(TV) miktarlarının metanol yükseltgenmesinde etkin tür olan Pt(0) miktarına göre artmasıyla açıklanabilir.
Özet (Çeviri)
ABSTRACT CARBON SUPPORTED AND SURFACTANT STABILIZED METAL NANOP ARTICLE CATALYSTS FOR DIRECT METHANOL FUEL CELLS Çelik, Çağlar M.S., Department of Chemistry Supervisor: Assoc. Prof. Dr. Gülsün Gökağaç August 2005, 72 pages Carbon supported surfactant, such as 1-decanethiol and octadecanethiol, stabilized platinum and platinum/ruthenium species have been prepared recently. In this thesis, for the first time, 1-hexanethiol has been used as an organic stabilizer for the preparation of carbon supported platinum and platinum/ruthenium nanoparticle catalysts. These new catalysts were employed for methanol oxidation reaction, which were used for direct methanol fuel cells. Cyclic voltammetry, X-ray photoelectron spectroscopy and transmission electron microscopy have been used in order to determine the nature of the catalysts. The effect of temperature and time on catalytic activity of catalysts were examined and the maximum catalytic activity was observed for carbon supported 1- hexanethiol stabilized platinum nanoparticle catalyst (with 1:1 thiol/platinum molar ratio) which was heated up at 200°C for 5 hours. The particle size of platinum nanoparticles was determined to be ~ 10 nm in diameter. The size and distribution of metal nanoparticles on carbon support, the Pt/Ru surface composition, the relative amount of Pt(0), Pt(II) and Pt(IV) and the removal IVof organic surfactant molecules around the metal nanoparticles were found to be important in determining the catalytic activity of electrodes towards methanol oxidation reaction. A significant decrease in catalytic activity was observed for carbon supported 1-hexanethiol stabilized Pt7sRu25 and Pt97Ru3 (with 1:1 thiol/PtRu molar ratio) with respect to carbon supported 1-hexanethiol stabilized Pt (with 1:1 thiol/platinum molar ratio). This result might be due to unremoved stabilizer shell around platinum/ruthenium nanoparticles and increase in amount of Pt(II) and Pt(IV) compared to Pt(0) where the methanol oxidation occured.
Benzer Tezler
- Activity of carbon supported platinum nanoparticles toward methanol oxidation reactions: Role of metal precursor and new surfactants
Karbon destekli platin nanoparçacıklı katalizörlerin metanol yükseltgenme tepkimesine karşı aktiviteleri: Başlangıç metal bileşiklerinin ve yeni sürfaktantın rolleri
SELDA ŞEN
- The preparation and analysis of new carbon supported Pt and Pt+second metal nanoparticles catalysts for direct methanol fuel cells
Doğrudan metanol yakıt pilleri için yeni karbon destekli Pt ve Pt+ikinci metal nanoparçacıklı katalizörlerin hazırlanması ve analizleri
FATİH ŞEN
Doktora
İngilizce
2012
KimyaOrta Doğu Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. GÜLSÜN GÖKAGAÇ ARSLAN
- Development of highly efficient platinum nanocatalysts for the dehydrogenation of ammonia borane via rational design of graphitic carbon nitride-based heterojunction photocatalysts
Grafitik karbon nitrür temelli heteroeklem fotokatalizör tasarımları ile amonyak boranın dehidrojenlenmesinde etkinliği yüksek platin nanokatalizörlerinin geliştirilmesi
MERVE AKSOY
Doktora
İngilizce
2021
EnerjiKoç ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
DOÇ. DR. ÖNDER METİN
- Autothermal reforming of petroleum fractions
Petrol fraksiyonlarının ototermal reformlanması
ARZU ARSLAN BOZDAĞ
Doktora
İngilizce
2019
Kimya MühendisliğiOrta Doğu Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. NAİME ASLI SEZGİ
PROF. DR. TİMUR DOĞU
- Kriyojenik koşullar altında termal stres ile modifiye edilmiş çok duvarlı karbon nanotüplerin makrodispersiyonuna yüzey aktif maddelerin etkisi
Effect of surface-active substances on the macrodispersion of thermal stress modified multi-wall carbon nanotubes under cryogenic conditions
AYKUT YİRMİBEŞOĞLU
Yüksek Lisans
Türkçe
2023
Kimya MühendisliğiHitit ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. NİHAN KAYA
DOÇ. DR. FİLİZ BORAN