Normal ve hafif beyaz betonun özellikleri üzerine bir araştırma

A research on the features of normal and light white concrete

  1. Tez No: 169912
  2. Yazar: HACI MURAT GENÇ
  3. Danışmanlar: Y.DOÇ.DR. HÜSEYİN TEMİZ
  4. Tez Türü: Yüksek Lisans
  5. Konular: İnşaat Mühendisliği, Civil Engineering
  6. Anahtar Kelimeler: Beyaz portland çimento, harç, hamur, dayanım, beyaz beton, bims tozu, uçucu kül, hafif beton, White Portland cement, Mortar, Paste, Resistance, White Concrete, Pumice powder, Fly Ash, Light Weight Concrete n
  7. Yıl: 2004
  8. Dil: Türkçe
  9. Üniversite: Kahramanmaraş Sütçü İmam Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Belirtilmemiş.
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

KAHRAMANMARAŞ SUTÇU IMAM ÜNİVERSİTESİ FEN BİLİMLERİ ENSTİTÜSÜ İNŞAAT MÜHENDİSLİĞİ ANABİLİM DALI YÜKSEK LİSANS TEZİ ÖZET NORMAL VE HAFD7 BEYAZ BETONUN OZELLDXLERI ÜZERİNE BİR ARAŞTİRMA Hacı Murat GENÇ DANIŞMAN : Yrd. Doç. Dr. Hüseyin TEMİZ Yd : 2004, Sayfa : 45 Jüri: Yrd. Doç. Dr. Hüseyin TEMİZ Yrd. Doç. Dr. Metin KÖSE Doç. Dr. Cafer GENÇOĞLAN Bu araştırmada, genel olarak dekoratif ve estetik uygulamalarda kullanılan, beyaz çimentonun gri çimentolarla benzer kimyasal kompozisyona sahip oldukları için beton agregalarının bağlayıcı malzemesi olarak yararlanılması halinde dayanım bakımından hangi özelliklere sahip olacağı ve standardın öngördüğü şartları taşıyıp taşımadığı araştırılmıştır. Bu çalışmada bütün karışımlarda Beyaz çimento (BPÇ 42.5), agrega olarak mıcır kullanılmıştır. İki ayrı karışım oluşturulmuştur. Beyaz çimento dozajı 300-400 kg/m3 aralığında değiştirilmiş, yaklaşık 50-100 mm arasında çökme sağlamak için uygun su miktarı kullanılmıştır. Agrega karışımlarının granülümetrisi A32-B32 refarans eğrileri arasında kalacak şekilde sabit tutulmuş olup En büyük tane boyutu 16 mm ve en büyük tane boyutu 32 mm olmak üzere iki tip karışım oluşturularak farklı üç tip ( BS 20, BS 30, BS 40 ) beton sınıfı için numuneler yapılmış ve bu numunelerin 3, 7 ve 28 günlük basınç dayanımları bulunmuştur en yüksek dayanım en büyük tane boyutu 16 mm'Iik karışımda BS 40 için hazırlanmış numunede meydana gelmiştir. Bu numunenin 28 günlük basınç dayanımı 44.8 MPa dır. Verilen beton sınıflarına uygun beton üretilebileceği bulunmuştur. Ayrıca hafif ince agrega (bims tozu) üe hafif beton üretilerek bu betonların basınç dayanımları bulunmuştur. Hafif betonlarda silis dumanı ve uçucu külün etkisini incelemek amacıyla çimentonun belli bir oranı yerine katılan silis dumanı ve uçucu külün dayanımı üzerindeki etkisi bulunmuştur. En yüksek dayanım bims tozu+uçucu kül+süper akışkanlaştırıcı karışımından elden edilmiş olup 28 günlük basınç dayanımı 14.4 MPa bulunmuştur.

Özet (Çeviri)

DEPERTMAN OF CIVIL ENGINEERING INSTITUTE OF NATURAL AND APPLIED SCD2NCES UNIVERSITY OF KAHRAMANMARAŞ SÜTÇÜ İMAM MSc THESIS ABSTRACT A RESEARCH ON THE FEATURES OF NORMAL AND LIGHT WHITE CONCRETE Hacı Murat GENÇ ADVISOR: Ass.Prof. Hüseyin TEMİZ Year: 2004, Pages: 45 Jury: Asst. Prof. Hüseyin TEMİZ Asst. Prof. Metin KÖSE Ass. Prof. Cafer GENÇO?LAN In this research binding properties of white cement, which has a similar chemical structure with grey cement and generally used for decoration, is investigated. Mechanical properties of white cement were also examined if it fits the requirement of the specifications. In this study, white cement (BPÇ 42.5) and crush stone were used for all mixture samples. Two different mixture samples were prepared. Dosage of white cement was between 300 and 400 kg/m3. Appropriate amount of water was used to get a value of slump between 50 and 100 mm. Gradation Curves of aggregate were tried to get between A32 and B32 reference curves. There were three types of concrete (BS 20, BS 30, BS 40) which were made by use of two kinds of mixture. Maximum aggregate diameters of the mixtures were 16mm and 32 mm. Compressive strengths of these mixtures were determined for three, seven and twenty-eight days. Maximum compressive strength was obtained from a mixture sample with a maximum aggregate diameter of 16mm. Twenty-eight days compressive strength of this sample was obtained as 44.8 MPa. As a result, white cement can be used to produce the concrete for a given class of concrete strength. Light-weight concrete was also made by use of light fine aggregate. Twenty- eight days compressive strengths of these mixture samples were determined. Silica fume and fly ash were used instead of cement for a determined ratio in order to observe the effects of Fly ash and Silica fume on the strength of concrete. Maximum twenty-eight days compressive strength of 14.4 MPa was obtained from a mixture sample prepared by (Pumice + Flyash + Superplasticizers)

Benzer Tezler

  1. Tez No

    611441

    Determination of in-plane shear characteristics of rc voided slabs by experimental and analytical methods

    Boşluklu döşemelerin düzlem içi kayma özeliklerinin deneysel ve analitik yöntemlerle belirlenmesi

    ALI ATTARIYAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2019

    İnşaat Mühendisliğiİstanbul Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    DOÇ. DR. BEYZA TAŞKIN AKGÜL

  2. Tez No

    68360

    High strength lightweipht natural agregate concrete

    Yüksek dayanımlı doğal hafif agregalı beton

    İSMAİL ÖZTOK

    Doktora

    İngilizce

    İngilizce

    1997

    İnşaat MühendisliğiOrta Doğu Teknik Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. ASIM YEĞİNOBALI

  3. Tez No

    979433

    Tekstil, kağıt ve doğal taş endüstrisi atıklarının taşıyıcı ve taşıyıcı olmayan hafif beton üretiminde kullanımı

    Use of textile, paper and natural stone industry wastes in structural and non-structural lightweight concrete production

    ÖMER BAYRAK

    Doktora

    Türkçe

    Türkçe

    2025

    İnşaat MühendisliğiBayburt Üniversitesi

    İnşaat Mühendisliği Ana Bilim Dalı

    PROF. DR. EMİN ERDEM

  4. Tez No

    501813

    Tam buğday ve beyaz ekmek tüketiminin hafif şişman ve obez bireylerde postprandiyal glukoz, insülin ve inkretin yanıtları üzerine etkisi

    The effect of the consumption of whole wheat bread and white bread among mildly overweight (BMI 25-30 kg/m2) and obese (BMI 30-35 kg/m2) persons on postprandial glucose, insulin and incretin hormones responses

    MERVE KAYALI

    Yüksek Lisans

    Türkçe

    Türkçe

    2016

    Beslenme ve Diyetetikİstanbul Üniversitesi

    İç Hastalıkları Ana Bilim Dalı

    PROF. DR. NEVİN DİNÇÇAĞ

  5. Tez No

    668171

    Glioblastom tanılı hastalarda tedavi sonrasında normal görünen beyaz cevherin multiparametrik MRG ile değerlendirilmesi

    Evaluation with multiparametric mri of normal-appearing whitematter in patients with treated glioblastoma

    SİNAN ŞAHİN

    Tıpta Uzmanlık

    Türkçe

    Türkçe

    2021

    Radyoloji ve Nükleer TıpAdnan Menderes Üniversitesi

    Radyoloji Ana Bilim Dalı

    PROF. DR. YELDA ÖZSUNAR DAYANIR

Geri Dön